Method of producing homogeneous sintered ZnO non-linear resistors

Claim 1

A method of making a homogeneous, sintered, resistor body, having a substantially uniform density, which can exhibit nonlinear V-I characteristics, comprising the steps of: (A) mixing: (1) a solid particle composition admixture of 75 mole % to 98 mole % of small, finely divided ZnO and 2 mole % to 25 mole % of a small, finely divided additive compound effective to produce non-linearity characteristics within the body, with (2) an aqueous binder solution comprising an organic, water soluble binder that will decompose at temperatures of between about 150° to about 600° C leaving no carbon residue, wherein the weight ratio of solid particles:binder is between about 100:1 to about 100:10, to provide a mixed particle-binder slurry, and then (B) simultaneously drying, mixing and agglomerating the slurry to form a mass of larger spherical particles, the agglomerated particles having an average particle size of between about 0.5 micron to about 500 microns diameter, and at least 50 wt.% of the agglomerated particles have an average particle size between 25 microns to about 500 microns, said particles containing binder, ZnO and additive compound distributed therethrough, and then (C) pressing a mass of the agglomerated particles in a uni-axial press, at between about 36 kg./sq. cm. to about 1,500 kg./sq. cm., to provide a body having a substantially uniform density, and then (D) heating the pressed body: (1) first at a temperature of between 25° and about 600° C, at a temperature rate increase of between 10° C/hr. to about 45° C/hr., effective to slowly decompose and remove the binder, and then (2) between about 625° to about 1,400° C, at a temperature rate increase of between about 75° C/hr. to about 150° C/hr., for a time effective to sinter together the particles of the pressed body, thereby forming a homogeneous sintered body having a substantially uniform density, exhibiting non-linear V-I characteristics.

Claim 2

A method of making a homogeneous, sintered, resistor body, having a substantially uniform density, which can exhibit nonlinear V-I characteristics, comprising the steps of: (A) mixing: (1) a solid particle composition admixture of 75 mole % to 98 mole % of small, finely divided ZnO and 2 mole % to 25 mole % of a small, finely divided additive compound effective to produce non-linearity characteristics within the body, with (2) an aqueous binder solution comprising an organic, water soluble binder that will decompose at temperatures of between about 150° to about 600° C leaving no carbon residue, wherein the weight ratio of solid particles:binder is between about 100:1 to about 100:10, to provide a mixed particle-binder slurry, and then (B) simultaneously drying, mixing and agglomerating the slurry to form a mass of larger spherical particles, the agglomerated particles having an average particle size of between about 0.5 micron to about 500 microns diameter, and at least 50 wt.% of the agglomerated particles have an average particle size between 25 microns to about 500 microns, said particles containing binder, ZnO and additive compound distributed therethrough, and then (C) pressing a mass of the agglomerated particles in a uni-axial press, at between about 36 kg./sq. cm. to about 1,500 kg./sq. cm., to provide a body having a substantially uniform density, and then (D) heating the pressed body: (1) first at a temperature of between 25° and about 600° C, at a temperature rate increase of between 10° C/hr. to about 45° C/hr., effective to slowly decompose and remove the binder, and then (2) between about 625° to about 1,400° C, at a temperature rate increase of between about 75° C/hr. to about 150° C/hr., for a time effective to sinter together the particles of the pressed body, thereby forming a homogeneous sintered body having a substantially uniform density, exhibiting non-linear V-I characteristics.

Claim 8

A method of making a homogeneous sintered, resistor body, having a substantially uniform density, which can exhibit non-linear V-I characteristics due to bulk electrical effects within the body, by: (A) wet mill mixing: (1) a solid particle composition admixture of 75 mole % to 98 mole % of ZnO having an average particle size of between about 0.01 micron to about 1.5 microns diameter and 2 mole % to 25 mole % of an oxide additive selected from the group consisting of Bi 2 O 3 , Co 3 O 4 , CoO, MnO, MnO 2 , Cr 2 O 3 , Sb 2 O 3 and mixtures thereof, having an average particle size of between about 0.01 micron to about 1.5 microns diameter, with (2) an aqueous binder solution comprising: an organic water soluble binder that will decompose at temperatures between about 150° to about 600° C leaving no carbon residue, wherein the weight ratio of oxide:binder is between about 100:1 to about 100:10, and an organic lubricating wax that will decompose at temperatures between about 150° to about 600° C, wherein the weight ratio of mixed oxide:lubricant is between about 100:0.1 to about 100:4 to provide a slurry, and then (B) spray drying the slurry to form larger spherical agglomerated particles, having an average particle size of between about 0.5 micron to about 500 microns diameter, with 50 wt.% to 80 wt.% of the agglomerated powder masses having an average particle size of between about 25 microns and about 500 microns, and 20 wt.% to 50 wt.% of the agglomerated powder masses having an average particle size of between about 0.5 micron and about 2.5 microns, essentially each of said agglomerated particles containing the oxides and binder, and then (C) pressing a mass of the agglomerated particles in a uni-axial press, at between about 72 kg./sq. cm. to about 240 kg./sq. cm., to provide a pressed body having a substantially uniform density, and then (D) heating the pressed body at a temperature: (1) between 25° to about 600° C, at a temperature rate increase of between about 10° C/hr. to about 45° C/hr., to slowly decompose and remove the binder, and then (2) between about 625° to about 1,400° C, at a temperature rate increase of between about 75° C/hr. to about 150° C/hr., for a time effective to sinter together the particles of the pressed body, to form a homogeneous body having a substantially uniform density, which can exhibit non-linear V-I characteristics.

Claim 9

A method of making a homogeneous sintered, resistor body, having a substantially uniform density, which can exhibit non-linear V-I characteristics due to bulk electrical effects within the body, by: (A) wet mill mixing: (1) a solid particle composition admixture of 75 mole % to 98 mole % of ZnO having an average particle size of between about 0.01 micron to about 1.5 microns diameter and 2 mole % to 25 mole % of an oxide additive selected from the group consisting of Bi 2 O 3 , Co 3 O 4 , CoO, MnO, MnO 2 , Cr 2 O 3 , Sb 2 O 3 and mixtures thereof, having an average particle size of between about 0.01 micron to about 1.5 microns diameter, with (2) an aqueous binder solution comprising: an organic water soluble binder that will decompose at temperatures between about 150° to about 600° C leaving no carbon residue, wherein the weight ratio of oxide:binder is between about 100:1 to about 100:10, and an organic lubricating wax that will decompose at temperatures between about 150° to about 600° C, wherein the weight ratio of mixed oxide:lubricant is between about 100:0.1 to about 100:4 to provide a slurry, and then (B) spray drying the slurry to form larger spherical agglomerated particles, having an average particle size of between about 0.5 micron to about 500 microns diameter, with 50 wt.% to 80 wt.% of the agglomerated powder masses having an average particle size of between about 25 microns and about 500 microns, and 20 wt.% to 50 wt.% of the agglomerated powder masses having an average particle size of between about 0.5 micron and about 2.5 microns, essentially each of said agglomerated particles containing the oxides and binder, and then (C) pressing a mass of the agglomerated particles in a uni-axial press, at between about 72 kg./sq. cm. to about 240 kg./sq. cm., to provide a pressed body having a substantially uniform density, and then (D) heating the pressed body at a temperature: (1) between 25° to about 600° C, at a temperature rate increase of between about 10° C/hr. to about 45° C/hr., to slowly decompose and remove the binder, and then (2) between about 625° to about 1,400° C, at a temperature rate increase of between about 75° C/hr. to about 150° C/hr., for a time effective to sinter together the particles of the pressed body, to form a homogeneous body having a substantially uniform density, which can exhibit non-linear V-I characteristics.