Method of coating ammunition with a protective surface layer
Assignee: Rheinmetall Industrie AG
•
Filing: 1981-12-02
•
Granted: 1984-06-05
•
Expires: 2001-12-02
Abstract
Abstract A protective surface coating for ammunition having no cartridge casing and ammunition having a combustible cartridge casing. A body of highly porous nitrocellulose is permeated from the outside with a polymer carried by a solvent to form a binder for the body. A layer of metal platelets containing airpockets is bound to the body with a binding polymer. The metal platelets are covered with an outer coating of a rapidly curing resin. The protective coating is used to prevent the penetration of moisture into the porous cartridge casing or into the powder mass itself and to provide improved stability to heat and flames.
Inventors
- 👤 Manfred Lubben
- 👤 Wolfram Witt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 04:55
CPC Classifications
F; F42; F42B; F42B5/00; F42B5/02; F42B5/18; F42B5/192; F42B5/196
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
139 words
A process for producing an improved ammunition having a surface coating with at least one layer of lacquer, comprising: (a) the steps of preparing a highly porous nitrocellulose body; (b) permeating the highly porous nitrocellulose body with a first polymer which is dispersed in a first solvent; (c) substantially removing the first solvent; (d) covering the outer surface of the body with a dispersion of metal particles in a second polymer solution with a second solution solvent permeating into the body for effecting a firm bond between the porous body and the metal particles; (e) covering the metal particle surface layer with a rapidly curing resin dissolved in a third solvent, the third solvent causing the second polymer to permeate partially from the metal particle layer into the porous body and thereby creating hollow spaces near the metal particles.
Claim 2
Dependent Claim
139 words
A process for producing an improved ammunition having a surface coating with at least one layer of lacquer, comprising: (a) the steps of preparing a highly porous nitrocellulose body; (b) permeating the highly porous nitrocellulose body with a first polymer which is dispersed in a first solvent; (c) substantially removing the first solvent; (d) covering the outer surface of the body with a dispersion of metal particles in a second polymer solution with a second solution solvent permeating into the body for effecting a firm bond between the porous body and the metal particles; (e) covering the metal particle surface layer with a rapidly curing resin dissolved in a third solvent, the third solvent causing the second polymer to permeate partially from the metal particle layer into the porous body and thereby creating hollow spaces near the metal particles.
Claim 3
Dependent Claim
15 words
The process as set forth in claim 1, wherein said first polymer is a polyurethane.
Claim 4
Dependent Claim
24 words
The process as set forth in claim 2, wherein the polyurethane is cured at a temperature of from about 80° C. to 150° C.
Claim 5
Dependent Claim
15 words
The process as set forth in claim 1, wherein the second polymer is a cyclorubber.
Claim 6
Dependent Claim
17 words
The process as set forth in claim 1, wherein the rapidly curing resin is a polyurethane resin.
Claim 7
Dependent Claim
19 words
The process as set forth in claim 1, wherein the metal particles are in the form of aluminum platelets.
Claim 8
Dependent Claim
50 words
The process as set forth in claim 6, wherein a fourth solvent is dispersed on the surface of the body after the covering of the surface of the body with a dispersion of metal platelets and before the covering of the metal platelet surface layer with a rapidly curing resin.
Claim 9
Dependent Claim
28 words
The process as set forth in claim 1, wherein the dispersion of metal particles in a second polymer comprises from about 20 to 50 weight percent aluminum platelets.
Claim 10
Dependent Claim
31 words
The process as set forth in claim 1, wherein the dispersion of metal particles in a second polymer solution comprises from about 5 to 10 weight percent of said second polymer.
Claim 11
Dependent Claim
23 words
The process as set forth in claim 1, comprising the step of curing the resulting covered body for at least about 10 days.
References Cited (Backward Citations)
US3079289A
Cited
DE1200184B
Cited
US4004523A
Cited
US3727512A
Cited
US3730094A
Cited
US3954063A
Cited
US4009231A
Cited
DE2550208A1
Cited
US3987731A
Cited
US4091729A
Cited
US4363273A
Cited
US4304185A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-05 | 1987-12-05 | 1988-06-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-05 | 1991-12-05 | 1992-06-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-05 | 1995-12-05 | 1996-06-05 | $7700.00 | Window Closed / Lapsed |