Graded index optical fibres
Assignee: British Telecommunications PLC
•
Filing: 1983-08-12
•
Granted: 1984-06-05
•
Expires: 2003-08-12
Abstract
Abstract A range of alkali metal borosilicate glass compositions modified by the addition of alkaline earth metal oxides has been found to be especially suitable for the production of graded index optical fibre using the double crucible method. A core glass from this range may be paired with a suitable cladding glass, which may be another glass from the same range or an unmodified alkali metal borosilicate, so that in the nozzle of the double crucible thermal diffusion takes place to give a composition gradient of alkaline earth metal oxide and hence a refractive index gradient. The fibres thus obtained have better refractive index profiles if the proportions of the oxides in the core and cladding glasses are chosen so as to exclude a simple ion-exchange mechanism. Fibres having numerical apertures of up to 0.268 and best loss values as low as 5.0 dB/km have been prepared.
Inventors
- 👤 Keith J. Beales
- 👤 William J. Duncan
- 👤 Anthony G. Dunn
- 👤 George R. Newns
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 11:06
CPC Classifications
G; G02; G02B; G02B6/00; G02B6/02; G02B6/036; G02B6/03616; G02B6/03622; G02B6/03627; C; C03; C03C; C03C13/00; C03C13/04; C03C13/045; C03C13/046; C03C21/00; C03C3/00; C03C3/04; C03C3/076; C03C3/089; G02B6/028; G02B6/0281
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
256 words
A graded index glass optical fibre having a total insertion loss of less than 20 dB/km and having a core and a cladding, said core being formed from a first glass consisting of silica, boric oxide, one alkali metal oxide selected from the group consisting of sodium oxide and potassium oxide, one alkaline earth metal oxide selected from the group consisting of calcium oxide, strontium oxide and barium oxide, and optionally, up to about 5 mole percent of one or more compatible oxides, said compatible oxides not including an alkali metal oxide, and said cladding being formed from a second glass having a refractive index at least 1% lower than that of said first glass and consisting of silica, boric oxide, the same alkali metal oxide as in said first glass, and optionally, up to about 5 mole percent of one or more other compatible oxides, said other compatible oxides not including calcium, strontium oxide or barium oxide or an alkali metal oxide, said first and second glass compositions being selected to exclude compositions which undergo phase separation or devitrification during optical fibre production, and said gradation of refractive index being produced by thermal diffusion between said first and second glasses and being at least partly caused by a composition gradient of alkaline earth metal oxide: said graded index optical fibre being characterised in that the mole percentage of the alkali metal oxide in said first glass is substantially equal to or greater than the mole percentage of the alkali metal oxide in said second glass.
Claim 2
Dependent Claim
256 words
A graded index glass optical fibre having a total insertion loss of less than 20 dB/km and having a core and a cladding, said core being formed from a first glass consisting of silica, boric oxide, one alkali metal oxide selected from the group consisting of sodium oxide and potassium oxide, one alkaline earth metal oxide selected from the group consisting of calcium oxide, strontium oxide and barium oxide, and optionally, up to about 5 mole percent of one or more compatible oxides, said compatible oxides not including an alkali metal oxide, and said cladding being formed from a second glass having a refractive index at least 1% lower than that of said first glass and consisting of silica, boric oxide, the same alkali metal oxide as in said first glass, and optionally, up to about 5 mole percent of one or more other compatible oxides, said other compatible oxides not including calcium, strontium oxide or barium oxide or an alkali metal oxide, said first and second glass compositions being selected to exclude compositions which undergo phase separation or devitrification during optical fibre production, and said gradation of refractive index being produced by thermal diffusion between said first and second glasses and being at least partly caused by a composition gradient of alkaline earth metal oxide: said graded index optical fibre being characterised in that the mole percentage of the alkali metal oxide in said first glass is substantially equal to or greater than the mole percentage of the alkali metal oxide in said second glass.
Claim 3
Dependent Claim
40 words
An optical fibre as claimed in claim 1, further characterised in that said first glass contains 55-65 mole percent silica, 10-20 mole percent boric oxide, 14-25 mole percent sodium oxide, and 2-11 mole percent of the alkaline earth metal oxide.
Claim 4
Dependent Claim
36 words
An optical fibre as claimed in claim 1, further characterised in that said first glass contains 57-61 mole percent silica, 14-16.5 mole percent boric oxide, 19-22 mole percent sodium oxide, and 3-8 mole percent barium oxide.
Claim 5
Dependent Claim
31 words
An optical fibre as claimed in claim 1, further characterised in that said second glass contains 55-65 mole percent silica, 10-20 mole percent boric oxide, and 14-25 mole percent sodium oxide.
Claim 6
Dependent Claim
31 words
An optical fibre as claimed in claim 2, further characterised in that said second glass contains 55-65 mole percent silica, 10-20 mole percent boric oxide, and 14-25 mole percent sodium oxide.
Claim 7
Dependent Claim
31 words
An optical fibre as claimed n claim 3, further characterised in that said second glass contains 55-65 mole percent silica, 10-20 mole percent boric oxide, and 14-25 mole percent sodium oxide.
Claim 8
Dependent Claim
32 words
An optical fibre as claimed in claim 1, further characterised in that said second glass contains 59-63 mole percent silica, 17-19 mole percent boric oxide, and 19-22 mole percent of sodium oxide.
Claim 9
Dependent Claim
32 words
An optical fibre as claimed in claim 2, further characterised in that said second glass contains 59-63 mole percent silica, 17-19 mole percent boric oxide, and 19-22 mole percent of sodium oxide.
Claim 10
Dependent Claim
32 words
An optical fibre as claimed in claim 3, further characterised in that said second glass contains 59-63 mole percent silica, 17-19 mole percent boric oxide, and 19-22 mole percent of sodium oxide.
Claim 11
Dependent Claim
59 words
An optical fibre as claimed in claim 1, further characterized in that said core glass is substantially free from alumina, that said second glass contains up to 4 mole percent of alumina, and that when said compatible oxides in said second glass include alumina, the combined total amount thereof in said second glass does not exceed 5 mole percent.
References Cited (Backward Citations)
US4275951A
Cited
US4242117A
Cited
GB2016443A
Cited
US4351659A
Cited
US4264131A
Cited
US4367012A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-05 | 1987-12-05 | 1988-06-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-05 | 1991-12-05 | 1992-06-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-05 | 1995-12-05 | 1996-06-05 | $7700.00 | Window Closed / Lapsed |