Colored inorganic complex for use as a pigment and compositions containing it
Assignee: Johnson Matthey PLC
•
Filing: 1983-02-24
•
Granted: 1984-05-15
•
Expires: 2003-02-24
Abstract
Abstract A colored inorganic complex of titanium, stannous and zinc oxides for use in making pigments capable of imparting for example red, yellow or green colors to plastics, paints, glasses or ceramics without reliance on toxic moieties. A wider range of colors can be obtained if the complex is used in a pigment system comprising excess oxides of titanium and zinc or stannic tin. The complex is preferably made by adding an acidified aqueous solution of ions of the metals (e.g. as metal sulphates or metal halides) to alkali so as to precipitate the oxides or oxide precursor such as hydrated oxides which are then washed and fired at over 450 DEG C. to form the complex. The colors obtained may be adjusted by the presence of traces of residual alkali metal moiety.
Inventors
- 👤 John W. Jenkins
- 👤 John Wolstenholme
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 19:35
CPC Classifications
C; C09; C09C; C09C1/00; C09C1/36; C09C1/0009; C01; C01P; C01P2002/00; C01P2002/70; C01P2002/72; C01P2004/00; C01P2004/60; C01P2004/61; C01P2004/62; C01P2006/00; C01P2006/60; C01P2006/62; C01P2006/65; C01P2006/66
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
35 words
An inorganic complex of stannous oxide with titanium and zinc oxides the complex having a colour describable in terms of at least one of the four basic colours which are red, yellow, green and blue.
Claim 2
Dependent Claim
35 words
An inorganic complex of stannous oxide with titanium and zinc oxides the complex having a colour describable in terms of at least one of the four basic colours which are red, yellow, green and blue.
Claim 3
Dependent Claim
36 words
An inorganic complex according to claim 1 having an X-ray diffraction pattern in which the four greatest peaks in intensity of diffracted copper Kα X-rays occur at 2θ Bragg angles of 62.1°+/-0.7°, 52.2°+/-0.7°, 36.3°+/-0.7° and 31.3°+/-0.7°.
Claim 4
Dependent Claim
33 words
An inorganic complex according to claim 2 in which the proportions of tin, titanium and zinc moieties in the complex can be expressed in terms of the formula (TiO 2 ) 2 SnO.ZnO.
Claim 5
Dependent Claim
25 words
A complex according to claim 1 which contains from 300 to 6000 atomic parts of alkali metal moiety per million atomic parts of the complex.
Claim 6
Dependent Claim
31 words
A pigment system comprising a complex as claimed in claim 1 and an additional amount of at least one oxide selected from the group consisting of titanium dioxide and zinc oxide.
Claim 7
Dependent Claim
49 words
A pigment system according to claim 5 wherein the proportions of the tin, titanium, zinc and oxygen moieties in the complex can be expressed in terms of the formula (TiO 2 ) a SnO(ZnO) b where a is from 0.3 to 5 and b is from 0.04 to 5.
Claim 8
Dependent Claim
33 words
A pigment system comprising a complex according to claim 1, together with stannic oxide and from 0 to 2 an uncomplexed oxide selected from the group consisting of titanium dioxide and zinc oxide.
Claim 9
Dependent Claim
57 words
A system according to claim 7 in which the proportions of the tin, titanium, zinc and oxygen moieties in the complex can be expressed in terms of the formula (TiO 2 ) c SnO(ZnO) d (SnO) e where c is from 0.4 to 6.2, d is from 0.1 to 6.2 and e is from 0.2 to 7.
Claim 10
Dependent Claim
25 words
A system according to claim 8 which contains from 300 to 6000 atomic parts of alkali metal per million atomic parts of the total system.
Claim 11
Dependent Claim
56 words
A method for making a complex as claimed in claim 1 or for making a pigment system comprising a complex as claimed in claim 1 which comprises heating an intimate mixture of stannous oxide with titanium dioxide, zinc oxide and optionally stannic oxide at a temperature of over 450° C. under a non-oxidising and non-reducing atmosphere.
Claim 12
Dependent Claim
22 words
A method according to claim 10 wherein the mixture of oxides is heated to a temperature of from 750° to 1000° C.
Claim 13
Dependent Claim
34 words
A method according to claim 10 wherein the mixture of oxides or their precursors is produced by mixing aqueous alkaline solution with an aqueous acidified solution of stannous, titanium, zinc and optionally stannic ions.
Claim 14
Dependent Claim
26 words
A composition comprising a colourable substrate and a complex as claimed in claim 1 or a pigment system comprising a complex as claimed in claim 1.
Claim 15
Dependent Claim
27 words
A composition as claimed in claim 13 wherein the colourable substrate is selected from the group consisting of substrates comprising organic polymers and substrates comprising refractory materials.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-15 | 1987-11-14 | 1988-05-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-15 | 1991-11-14 | 1992-05-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-15 | 1995-11-14 | 1996-05-15 | $7700.00 | Window Closed / Lapsed |