Copper-zinc-iron ternary alloy coated steel wire reinforcers in tires
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1983-09-08
•
Granted: 1984-05-01
•
Expires: 2003-09-08
Abstract
Abstract This invention reveals a steel wire element useful in the reinforcement of rubber articles in which the steel wire is provided with an adhesive coating comprising a ternary brass alloy containing about 55 percent to about 75 percent by weight copper, about 15 to about 45 percent by weight zinc, and about 0.1 to about 10 percent by weight iron. Preferably this ternary brass alloy will contain about 1 to 5 percent by weight iron. The steel wire elements of this invention are useful in the reinforcement of vehicle tires, power transmission belts, conveyor belts, hoses, and the like.
Inventors
- 👤 Robert M. Shemenski
- 👤 Dong K. Kim
- 👤 Thomas W. Starinshak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:14
CPC Classifications
C; C25; C25D; C25D3/00; C25D3/02; C25D3/56; C25D3/58; D; D07; D07B; D07B1/00; D07B1/06; D07B1/0606; D07B1/0666; B; B32; B32B; B32B15/00; B32B15/01; B32B15/013; B32B15/015; D07B2205/00; D07B2205/30; D07B2205/3021; D07B2205/3085; D07B2205/3089; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12556; Y10T428/12562; Y10T428/12771; Y10T428/12861; Y10T428/12903; Y10T428/12917; Y10T428/12924
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
70 words
In a rubber article containing at least one steel reinforcing element wherein said steel reinforcing element is provided with an adhesive brass alloy coating, the improvement which comprises said brass alloy being a ternary iron-brass alloy consisting essentially of about 55 percent to about 75 percent copper by weight, about 0.1 percent to about 10 percent iron by weight, and about 15 percent to about 45 percent zinc by weight.
Claim 2
Dependent Claim
70 words
In a rubber article containing at least one steel reinforcing element wherein said steel reinforcing element is provided with an adhesive brass alloy coating, the improvement which comprises said brass alloy being a ternary iron-brass alloy consisting essentially of about 55 percent to about 75 percent copper by weight, about 0.1 percent to about 10 percent iron by weight, and about 15 percent to about 45 percent zinc by weight.
Claim 3
Dependent Claim
44 words
A rubber article as specified in claim 1 wherein said ternary iron-brass alloy consisting essentially of about 60 percent to 67 percent copper by eight, about 1 percent to 5 percent iron by weight, and about 28 percent to 39 percent by weight zinc.
Claim 4
Dependent Claim
22 words
A rubber article as specified in claim 2 wherein said ternary iron-brass alloy contains 2 percent to 4 percent by weight iron.
Claim 5
Dependent Claim
20 words
A rubber article as specified in claim 3 wherein said ternary iron-brass alloy contains about 3 percent by weight iron.
Claim 6
Dependent Claim
25 words
A rubber article as specified in claim 1 wherein said adhesive iron-brass coating has a thickness of from about 0.05 microns to about 0.40 microns.
Claim 7
Dependent Claim
23 words
A rubber article as specified in claim 5 wherein said adhesive iron-brass coating has a thickness ranging from 0.12 microns to 0.25 microns.
Claim 8
Dependent Claim
34 words
A rubber article as specified in claim 1 wherein said rubber is selected from the group consisting of natural rubber, synthetic polyisoprene, polybutadiene, nitrile rubber, carboxylated nitrile rubber, butyl rubber, EPDM, EPR, and polyisobutylene.
Claim 9
Dependent Claim
14 words
A rubber article as specified in claim 7 wherein said rubber is natural rubber.
Claim 10
Dependent Claim
25 words
A rubber article as specified in claim 1 wherein said steel reinforcing element is selected from the group consisting of steel wires and steel cord.
Claim 11
Dependent Claim
14 words
A rubber article as specified in claim 1 in the form of a tire.
Claim 12
Dependent Claim
14 words
A rubber composition as specified in claim 1 in the form of a belt.
Claim 13
Dependent Claim
62 words
A steel reinforcing element useful in the reinforcement of rubber articles in which the steel reinforcing element is provided with an adhesive coating comprising a ternary iron-brass alloy consisting essentially of about 55 percent to about 75 percent by weight copper, about 0.1 percent to about 10 percent by weight iron, and about 15 percent to about 45 percent by weight zinc.
Claim 14
Dependent Claim
62 words
A steel reinforcing element useful in the reinforcement of rubber articles in which the steel reinforcing element is provided with an adhesive coating comprising a ternary iron-brass alloy consisting essentially of about 55 percent to about 75 percent by weight copper, about 0.1 percent to about 10 percent by weight iron, and about 15 percent to about 45 percent by weight zinc.
Claim 15
Dependent Claim
48 words
A steel reinforcing element as specified in claim 12 wherein said ternary iron-brass alloy consisting essentially of about 60 percent to about 67 percent by weight copper, about 1 percent to about 5 percent by weight iron, and about 28 percent to about 39 percent by weight zinc.
Claim 16
Dependent Claim
24 words
A steel reinforcing element as specified in claim 13 wherein said ternary iron-brass alloy contains from 2 percent to 4 percent by weight iron.
Claim 17
Dependent Claim
19 words
A steel reinforcing element as specified in claim 14 wherein said ternary iron-brass alloy contains about 3 percent iron.
Claim 18
Dependent Claim
26 words
A steel reinforcing element as specified in claim 12 wherein said adhesive iron-brass coating has a thickness ranging from about 0.05 microns to about 0.40 microns.
Claim 19
Dependent Claim
24 words
A steel reinforcing element as specified in claim 16 wherein said adhesive iron-brass coating has a thickness ranging from 0.12 microns to 0.25 microns.
References Cited (Backward Citations)
US2870526A
Cited
US2939207A
Cited
US3749558A
Cited
US3961740A
Cited
US4018570A
Cited
US3936536A
Cited
US4068041A
Cited
US4192694A
Cited
US4218517A
Cited
US4255496A
Cited
US4347290A
Cited
US4226918A
Cited
GB2039580A
Cited
US4333785A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-01 | 1987-10-31 | 1988-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-01 | 1991-10-31 | 1992-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-01 | 1995-10-31 | 1996-05-01 | $7700.00 | Window Closed / Lapsed |