Copper electroplating procedure
Assignee: AT&T Inc
•
Filing: 1983-08-25
•
Granted: 1984-05-01
•
Expires: 2003-08-25
Abstract
Abstract In traditional copper electroplating processes, soluble copper anodes are used as the source of copper. There are certain potential advantages to using nonconsumable anodes and adding a source of copper such as copper oxide to replenish the electroplating bath. Periodic reverse current plating is used by some manufacturers to obtain smoother deposits without the use of additives. This periodic reversal of current drastically reduces the service life of the nonconsumable anodes because of dissolution of the metal oxide on the insoluble anode. The invention is a copper electroplating process with a dual-element anode assembly. This assembly consists of electrically isolated copper and metal-oxide electrodes. The metal-oxide electrode is active only during the anodic part of the cycle while the copper electrode is active only during the cathodic part of the cycle. Electrical isolation is achieved by the use of diodes or relays.
Inventors
- 👤 Craig G. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 04:15
CPC Classifications
C; C25; C25D; C25D17/00; C25D17/10; C25D3/00; C25D3/02; C25D3/38; C25D5/00; C25D5/18
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
87 words
A process for electroplating copper using periodic reversing of the electroplating current comprising the step of passing current through a cathode, electroplating solution and nonconsumable dual anode system using a source of current which is periodically reversed in direction from a plating mode to a deplating mode characterized in that the nonconsumable dual anode system comprises metal-oxide anode which is electrically connected to the source of current during the plating mode and chemically inert anode which is connected to the source of current during the deplating mode.
Claim 2
Dependent Claim
87 words
A process for electroplating copper using periodic reversing of the electroplating current comprising the step of passing current through a cathode, electroplating solution and nonconsumable dual anode system using a source of current which is periodically reversed in direction from a plating mode to a deplating mode characterized in that the nonconsumable dual anode system comprises metal-oxide anode which is electrically connected to the source of current during the plating mode and chemically inert anode which is connected to the source of current during the deplating mode.
Claim 3
Dependent Claim
16 words
The process of claim 1 in which the electroplating bath comprises copper sulfate in acid solution.
Claim 4
Dependent Claim
26 words
The process of claim 2 in which the electroplating bath is made acidic with sulfuric acid and the copper concentration is between 0.05 Molar and saturation.
Claim 5
Dependent Claim
29 words
The process of claim 3 in which the concentration of copper is between 0.05 and 1.5 Molar and the concentration of sulfuric acid is between 0.1 and 2 Molar.
Claim 6
Dependent Claim
20 words
The process of claim 4 in which the electroplating bath contains chloride ions in a concentration range from 30-100 mg/liter.
Claim 7
Dependent Claim
99 words
The process of claim 1 in which the surface of the metal-oxide electrode comprises oxide of: a. at least 10 mole percent group VIII metal, said group VIII metal selected from the group consisting of cobalt, nickel, rithenium, rhodium, palladium, iridium and platinum; b. at least 10 mole percent valve metal, said valve metal selected from the group consisting of titanium, zirconium, hafnium, niobium and tantalum; and c. from 0-20 mole percent binder metal, said binder metal selected from the group consisting of beryllium, calcium, strontium, carium, scandium, yttrium, lanthanum and the rare earth elements with atomic numbers 58-71.
Claim 8
Dependent Claim
24 words
The process of claim 6 in which the surface of the metal-oxide electrode comprises 20-90 mole percent oxide of iridium, remainder oxide of tantalum.
Claim 9
Dependent Claim
15 words
The process of claim 1 in which the chemically inert electrode comprises electrically conducting material.
Claim 10
Dependent Claim
14 words
The process of claim 8 in which the chemically inert anode comprises metallic material.
Claim 11
Dependent Claim
20 words
The process of claim 9 in which the metallic material is selected from the group consisting of titanium and tantalum.
Claim 12
Dependent Claim
41 words
The process of claim 1 in which the plating mode is from 0.1-500 seconds in duration and the total quantity of electrical charge involved in the plating mode is from 2-200 times the amount of charge involved in the deplating mode.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-01 | 1987-10-31 | 1988-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-01 | 1991-10-31 | 1992-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-01 | 1995-10-31 | 1996-05-01 | $7700.00 | Window Closed / Lapsed |