US4444807A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for treating a surface of a polyester film
Assignee: Olympus Corp
•
Filing: 1983-07-28
•
Granted: 1984-04-24
•
Expires: 2003-07-28
Abstract
Abstract A surface of the thermoplastic polyester film which has stickiness after having been heated is treated with a monocarboxylic acid so as to convert hydroxyl groups on the film surface into corresponding ester groups by reaction with the acid. Further, the film surface is treated with a monohydric alcohol so as to convert carboxyl groups on the film surface into corresponding ester groups by reaction with the alcohol. Thus, the stickiness on the film surface is eliminated.
Inventors
- 👤 Yoshihiko Masakawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 17:33
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/12; C08J2367/00; C08J2367/02
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
146 words
A surface treatment method for a thermoplastic polyester film, comprising: bringing a monocarboxylic acid into contact with a surface of a thermoplastic polyester film which is sticky after having been heated and then contains hydroxy groups and carboxyl groups on said surface, at a temperature not more than about 150° C. but sufficient to cause a reaction thereof with said hydroxyl groups on the surface of said polyester film, so as to convert the hydroxyl groups into corresponding ester groups; and bringing a monohydric alcohol into contact with the surface of said polyester film which is sticky, at a temperature not more than about 150° C. but sufficient to cause a reaction thereof with carboxyl groups on the surface of said polyester film, so as to convert the carboxyl groups into corresponding ester groups; thereby substantially eliminating the stickiness on the surface of said polyester film.
Claim 2
Dependent Claim
146 words
A surface treatment method for a thermoplastic polyester film, comprising: bringing a monocarboxylic acid into contact with a surface of a thermoplastic polyester film which is sticky after having been heated and then contains hydroxy groups and carboxyl groups on said surface, at a temperature not more than about 150° C. but sufficient to cause a reaction thereof with said hydroxyl groups on the surface of said polyester film, so as to convert the hydroxyl groups into corresponding ester groups; and bringing a monohydric alcohol into contact with the surface of said polyester film which is sticky, at a temperature not more than about 150° C. but sufficient to cause a reaction thereof with carboxyl groups on the surface of said polyester film, so as to convert the carboxyl groups into corresponding ester groups; thereby substantially eliminating the stickiness on the surface of said polyester film.
Claim 3
Dependent Claim
38 words
A method according to claim 1, wherein the monocarboxylic acid is a saturated lower aliphatic carboxylic acid having a formula: R.sup.1 --COOH where R 1 is hydrogen atom an alkyl group having not more than 5 carbon atoms.
Claim 4
Dependent Claim
26 words
A method according to claim 1, wherein the monocarboxylic acid is a member selected from the group consisting of formic acid, acetic acid and propionic acid.
Claim 5
Dependent Claim
13 words
A method according to claim 1, wherein the monocarboxylic acid is acetic acid.
Claim 6
Dependent Claim
21 words
A method according to claim 1, wherein the monohydric alcohol is a lower alkanol having not more than 5 carbon atoms.
Claim 7
Dependent Claim
22 words
A method according to claim 1, wherein the monohydric alcohol is a member selected from the group consisting of methanol and ethanol.
Claim 8
Dependent Claim
12 words
A method according to claim 1, wherein the monohydric alcohol is ethanol.
Claim 9
Dependent Claim
56 words
A method according to claim 1, wherein said polyester film is guided onto a heated roller maintained at a temperature higher than the boiling temperature of the monohydric alcohol, and the surface of said polyester film on said heated roller which is sticky is sequentially brought into contact with the monocarboxylic acid and the monohydric alcohol.
Claim 10
Dependent Claim
87 words
A method according to claim 1, wherein said polyester film is guided onto a first heated roller maintained at a first predetermined temperature and the surface of said polyester film on said first heated roller which is sticky is brought into contact with the monocarboxylic acid, and said polyester film is then guided onto a second heated roller maintained at a second predetermined temperature and the surface of said polyester film on said second heated roller which is sticky is brought into contact with the monohydric alcohol.
Claim 11
Independent Claim
169 words
A method for manufacturing a magnetic tape, comprising: providing a thermoplastic polyester film having first and second major surfaces; forming a magnetic thin film on said first major surface of said polyester film at an elevated temperature; bringing a saturated lower aliphatic monocarboxylic acid into contact with said second major surface which contains hydroxyl groups including hydroxyl groups caused to be present thereon as a result of said formation of said magnetic film, at a temperature of not higher than 150° C. and under conditions to cause reaction thereof with said hydroxyl groups, so as to convert the hydroxyl groups into corresponding ester groups; and bringing a lower alkanol into contact with said second major surface which contains carboxyl groups including carboxyl groups caused to be present thereon as a result of said formation of said magentic film, at a temperature of not higher than 150° C. and under conditions to cause reaction thereof with said carboxyl groups, so as to convert the carboxyl groups into corresponding ester groups.
Claim 12
Independent Claim
169 words
A method for manufacturing a magnetic tape, comprising: providing a thermoplastic polyester film having first and second major surfaces; forming a magnetic thin film on said first major surface of said polyester film at an elevated temperature; bringing a saturated lower aliphatic monocarboxylic acid into contact with said second major surface which contains hydroxyl groups including hydroxyl groups caused to be present thereon as a result of said formation of said magnetic film, at a temperature of not higher than 150° C. and under conditions to cause reaction thereof with said hydroxyl groups, so as to convert the hydroxyl groups into corresponding ester groups; and bringing a lower alkanol into contact with said second major surface which contains carboxyl groups including carboxyl groups caused to be present thereon as a result of said formation of said magentic film, at a temperature of not higher than 150° C. and under conditions to cause reaction thereof with said carboxyl groups, so as to convert the carboxyl groups into corresponding ester groups.
Claim 13
Dependent Claim
18 words
A method according to claim 10, wherein the monocarboxylic acid is acetic acid, and the alkanol is ethanol.
Claim 14
Dependent Claim
59 words
A method according to claim 10, wherein said polyester film is guided onto a heated roller maintained at a temperature higher than the boiling point of the alkanol such that said first major surface faces said heated roller, and said second major surface of said polyester film is sequentially brought into contact with the monocarboxylic acid and the alkanol.
Claim 15
Dependent Claim
106 words
A method according to claim 10, wherein said polyester film is guided onto a first heated roller maintained at a first predetermined temperature such that said first major surface faces said first heated roller and said second major surface of said polyester film on said first heated roller is brought into contact with the monocarboxylic acid, and said polyester film is then guided onto a second heated roller maintained at a second predetermined temperature such that said first major surface faces said second heated roller and said second major surface of said polyester film on said second heated roller is brought into contact with the alkanol.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-24 | 1987-10-24 | 1988-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-24 | 1991-10-24 | 1992-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-24 | 1995-10-24 | 1996-04-24 | $7700.00 | Window Closed / Lapsed |