Method of manufacturing magnetic, plastic-bonded molded bodies
Assignee: US Philips Corp
•
Filing: 1981-09-03
•
Granted: 1984-04-24
•
Expires: 2001-09-03
Abstract
Abstract In the manufacture of magnetic, plastic bonded molded bodies having different magnetic properties but the same physical dimensions, it has been found that variations in the amount of the magnetic mass constituent result in a change in the shrinkage behavior of the mass during and after shaping. Therefore, the shaping tools must be adapted to compensate for this varied shrinkage behavior. In order to prevent this varied shrinkage behavior, according to the invention, magnetic material in the mass is replaced by nonmagnetic inorganic material having the same or similar shrinkage behavior, the constituent of plastic remaining the same in both cases. Since the ratio of binder to material to be bonded remains constant as regards volume, in the final product, molded bodies having strongly different magnetic properties can be manufactured without having to change the shaping tool.
Inventors
- 👤 Manfred Moslener
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 09:07
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/10; H01F1/11; H01F1/113
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
158 words
A method of manufacturing magnetic, plastic bonded molded bodies having different respective values of saturation magnetization but having the same physical dimensions, said method comprising the steps of: A. providing a first preselected quantity by volume of a plastic binder material prepared for mixing with a material to be bonded; B. providing a second preselected quantity by volume of a material to be bonded; C. mixing the plastic binder and the material to be bonded to obtain a mixture; and D. processing the mixture obtained in step C into completed molded bodies by using a single shaping tool; characterized in that the material to be bonded consists of a powdered magnetic material and an inorganic nonmagnetic filler having substantially the same shrinkage behavior, the volume ratio between the magnetic material and the nonmagnetic filler being varied from one mixture to the next to obtain different values of saturation magnetization in the completed molded bodies produced from different mixtures.
Claim 2
Independent Claim
158 words
A method of manufacturing magnetic, plastic bonded molded bodies having different respective values of saturation magnetization but having the same physical dimensions, said method comprising the steps of: A. providing a first preselected quantity by volume of a plastic binder material prepared for mixing with a material to be bonded; B. providing a second preselected quantity by volume of a material to be bonded; C. mixing the plastic binder and the material to be bonded to obtain a mixture; and D. processing the mixture obtained in step C into completed molded bodies by using a single shaping tool; characterized in that the material to be bonded consists of a powdered magnetic material and an inorganic nonmagnetic filler having substantially the same shrinkage behavior, the volume ratio between the magnetic material and the nonmagnetic filler being varied from one mixture to the next to obtain different values of saturation magnetization in the completed molded bodies produced from different mixtures.
Claim 3
Dependent Claim
26 words
A method as claimed in claim 1, characterized in that the powdered magnetic material and the inorganic nonmagnetic filler having substantially the same grain size distribution.
Claim 4
Dependent Claim
25 words
A method as claimed in claim 2, characterized in that the material to be bonded consists of at least 1.3 weight percent inorganic nonmagnetic filler.
Claim 5
Dependent Claim
25 words
A method as claimed in claim 3, characterized in that the material to be bonded consists of at most 15 weight percent inorganic nonmagnetic filler.
Claim 6
Dependent Claim
19 words
A method as claimed in claim 4, characterized in that the magnetic material is a ceramic permanent magnetic powder.
Claim 7
Dependent Claim
40 words
A method as claimed in claim 5, characterized in that the ceramic permanent magnetic powder is barium hexaferrite or strontium hexaferrite powder with a grain size of 1 to 500 μm with 65% of the grains less than 32 μm.
Claim 8
Dependent Claim
16 words
A method as claimed in claim 6, characterized in that the nonmagnetic filler is iron oxide.
Claim 9
Dependent Claim
16 words
A method as claimed in claim 6, characterized in that the nonmagnetic filler is calcium carbonate.
Claim 10
Dependent Claim
18 words
A method as claimed in claim 7 or 8 characterized in that the plastic binder is a polyolefin.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-24 | 1987-10-24 | 1988-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-24 | 1991-10-24 | 1992-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-24 | 1995-10-24 | 1996-04-24 | $7700.00 | Window Closed / Lapsed |