Attrition resistant metal/oxygen compositions
Assignee: Monsanto Co
•
Filing: 1983-04-23
•
Granted: 1984-04-17
•
Expires: 2003-04-23
Abstract
Abstract Attrition resistant metal/oxygen compositions comprising the infusion and reaction product of an alumina existing in a crystal form selected from the group consisting of gamma , delta , eta , and chi crystal forms, and mixtures thereof, or that can be transformed by heat to such crystal forms, and characterized by a mean particle size from about 10 mu m to about 200 mu m, a fractional porosity of at least 0.2, a surface area of at least 150 m2/g, and a pore diameter such that at least 10 percent of the pores are less than 55 ANGSTROM , and at least one metal oxide, or compound convertible by heat to such metal oxide, having a maximum mean particle size of about 100 mu m, with the proviso that the alumina/metal oxide mean particle size ratio is at least 2, which metal oxide is susceptible of undergoing infusion and reaction with the alumina upon being subjected to temperatures of at least 0.4 Tm for a time sufficient to cause infusion and reaction between the metal oxide and the alumina, wherein Tm is the melting point in DEG K. of the alumina, are useful in a wide variety of metal oxide-catalyzed reactions. The compositions are especially useful in reactions which involve reaction conditions of high stress, for example, vapor phase oxidations under fluidized bed conditions.
Inventors
- 👤 Robert A. Keppel
- 👤 Samuel J. Tremont
- 👤 Emerson H. Lee
- 👤 George D. Davis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 09:52
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/08; B01J21/00; B01J21/02; B01J21/04; B01J23/00; B01J23/16; B01J23/18; B01J35/00; B01J35/60; C; C07; C07C; C07C2/00; C07C2/76; B01J35/61; B01J35/615; B01J35/64; B01J35/647
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
348 words
A process for dehydrocoupling toluene which comprises: (a) contacting the toluene in the vapor phase at a temperature from about 450° C. to about 650° C. with an attrition resistant metal/oxygen composition comprising the infusion and reaction product of (i) 35 to 80 mole percent of an alumina existing in a crystal form selected from the group consisting of γ, δ, η, and χ crystal forms, and mixtures thereof, or that can be transformed by heat to such crystal forms, and characterized by (a) a mean particle size from about 10 μm to about 200 μm, (b) a fractional porosity of at least 0.2, (c) a surface area of at least 150 m 2 /g, and (d) a pore diameter such that at least 10 percent of the pores are less than 55 Å, and (ii) 20 to 65 mole percent of at least one metal oxide, or compound convertible by heat to such metal oxide, having a maximum mean particle size of about 100 μm with the proviso that the alumina/metal oxide mean particle size ratio is at least 2, which metal oxide is susceptible of undergoing infusion and reaction with with the alumina upon being subjected to temperatures of at least 0.4 T m for a time sufficient to cause infusion and reaction between the metal oxide and the alumina, wherein T m is the melting point in °K. of the alumina wherein the composition is represented by the empirical formula selected from the group consisting of Pb 10 Sb 3 Bi 2 O x (Al 2 O 3 ) 7-28 , Bi 15-30 K 4-5 Zr 1-2 O x (Al 2 O 3 ) 16-29 , (PbO x ) 3 (Al 2 O 3 )4, Pb 5 BiO x (Al 2 O 3 )18, Pb 10 Sb 3 Bi 2 KO x (Al 2 O 3 )19, Bi 15 Ca 5 ZrO x (Al 2 O 3 )16, Bi 5 Fe 5 Ca 5 BO x (Al 2 O 3 )8, and Bi 2 Fe 2 Ca 2 O x (Al 2 O 3 )3.
Claim 2
Dependent Claim
348 words
A process for dehydrocoupling toluene which comprises: (a) contacting the toluene in the vapor phase at a temperature from about 450° C. to about 650° C. with an attrition resistant metal/oxygen composition comprising the infusion and reaction product of (i) 35 to 80 mole percent of an alumina existing in a crystal form selected from the group consisting of γ, δ, η, and χ crystal forms, and mixtures thereof, or that can be transformed by heat to such crystal forms, and characterized by (a) a mean particle size from about 10 μm to about 200 μm, (b) a fractional porosity of at least 0.2, (c) a surface area of at least 150 m 2 /g, and (d) a pore diameter such that at least 10 percent of the pores are less than 55 Å, and (ii) 20 to 65 mole percent of at least one metal oxide, or compound convertible by heat to such metal oxide, having a maximum mean particle size of about 100 μm with the proviso that the alumina/metal oxide mean particle size ratio is at least 2, which metal oxide is susceptible of undergoing infusion and reaction with with the alumina upon being subjected to temperatures of at least 0.4 T m for a time sufficient to cause infusion and reaction between the metal oxide and the alumina, wherein T m is the melting point in °K. of the alumina wherein the composition is represented by the empirical formula selected from the group consisting of Pb 10 Sb 3 Bi 2 O x (Al 2 O 3 ) 7-28 , Bi 15-30 K 4-5 Zr 1-2 O x (Al 2 O 3 ) 16-29 , (PbO x ) 3 (Al 2 O 3 )4, Pb 5 BiO x (Al 2 O 3 )18, Pb 10 Sb 3 Bi 2 KO x (Al 2 O 3 )19, Bi 15 Ca 5 ZrO x (Al 2 O 3 )16, Bi 5 Fe 5 Ca 5 BO x (Al 2 O 3 )8, and Bi 2 Fe 2 Ca 2 O x (Al 2 O 3 )3.
Claim 3
Dependent Claim
22 words
The process of claim 1 wherein the mean particle size of the alumina is from about 20 μm to about 125 μm.
Claim 4
Dependent Claim
18 words
The process of claim 1 wherein the alumina has a fractional porosity from about 0.2 to about 0.8.
Claim 5
Dependent Claim
11 words
The process of claim 1 wherein the alumina particles are spheroidal.
Claim 6
Dependent Claim
23 words
The process of claim 1 wherein the alumina is a hydrated alumina selected from the group consisting of Boehmite, pseudo-Boehmite, Bayerite, and Gibbsite.
Claim 7
Dependent Claim
17 words
The process of claim 1 wherein the alumina/metal oxide mean particle size ratio is 15 or more.
Claim 8
Dependent Claim
25 words
The process of claim 6 wherein the metal oxide component concentration is in an amount from about 30 mole percent to about 55 mole percent.
Claim 9
Dependent Claim
55 words
The process of claim 1 wherein the composition is represented by the empirical formula Pb 10 Sb 3 Bi 2 O x (Al 2 O 3 ) 7-28 wherein x is a number taken to satisfy the average valences of Pb, Sb, and Bi in the oxidation states in which they exist in the composition.
Claim 10
Dependent Claim
48 words
The process of claim 1 wherein the composition is represented by the empirical formula (PbO x ) 3 (Al 2 O 3 ) 4 wherein x is a number taken to satisfy the average valence of Pb in the oxidation state in which it exists in the composition.
Claim 11
Dependent Claim
50 words
The process of claim 1 wherein the composition is represented by the empirical formula Pb 5 BiO x (Al 2 O 3 ) 18 wherein x is a number taken to satisfy the average valences of Pb and Bi in the oxidation states in which they exist in the composition.
Claim 12
Dependent Claim
56 words
The process of claim 1 wherein the composition is represented by the empirical formula Pb 10 Sb 3 Bi 2 KO x (Al 2 O 3 ) 19 wherein x is a number taken to satisfy the average valences of Pb, Sb, Bi, and K in the oxidation states in which they exist in the composition.
Claim 13
Dependent Claim
55 words
The process of claim 1 wherein the composition is represented by the empirical formula Bi 15-30 K 4-5 Zr 1-2 O x (Al 2 O 3 ) 16-29 wherein x is a number taken to satisfy the average valences of Bi, K, and Zr in the oxidation states in which they exist in the composition.
Claim 14
Dependent Claim
53 words
The process of claim 1 wherein the composition is represented by the empirical formula Bi 15 Ca 5 ZrO x (Al 2 O 3 ) 16 wherein x is a number taken to satisfy the average valences of Bi, Ca, and Zr in the oxidation states in which they exist in the composition.
Claim 15
Dependent Claim
56 words
The process of claim 1 wherein the composition is represented by the empirical formula Bi 5 Fe 5 Ca 5 BO x (Al 2 O 3 ) 8 wherein x is a number taken to satisfy the average valences of Bi, Fe, Ca, and B in the oxidation states in which they exist in the composition.
Claim 16
Dependent Claim
55 words
The process of claim 1 wherein the composition is represented by the empirical formula Bi 2 Fe 2 Ca 2 O x (Al 2 O 3 ) 3 wherein x is a number taken to satisfy the average valences of Bi, Fe, and Ca in the oxidation states in which they exist in the composition.
Claim 17
Dependent Claim
28 words
The process of claim 1 wherein steam is introduced with the toluene in an amount sufficient to provide a steam/toluene mole ratio between about 0.1 to about 10.
Claim 18
Dependent Claim
30 words
The process of claim 1 wherein the contacting between the toluene and the attrition resistant metal/oxygen composition is effected for a period between about 1 second and about 12 second.
Claim 19
Dependent Claim
17 words
The process of claim 17 wherein the temperature is between about 500° C. and about 600° C.
Claim 20
Dependent Claim
24 words
The process of claim 1 wherein the dehydrocoupling reaction is conducted in a stoichiometric mode of operation in the absence of added free oxygen.
Claim 21
Dependent Claim
24 words
The process of claim 1 wherein a reactant selected from the group consisting of oxygen and an oxygen-containing gas is introduced with the toluene.
Claim 22
Dependent Claim
28 words
The process of claim 20 wherein the oxygen and oxygen-containing gas is introduced in an amount sufficient to conduct the dehydrocoupling reaction in a catalytic mode of operation.
Claim 23
Dependent Claim
28 words
The process of claim 21 wherein the oxygen and oxygen-containing gas is introduced in an amount sufficient to provide a toluene/oxygen mole ratio between about 1 and 8.
Claim 24
Dependent Claim
29 words
The process of claim 20 wherein the oxygen and oxygen-containing gas is introduced in an amount sufficient to conduct the dehydrocoupling reaction in a combined catalytic/stoichiometric mode of operation.
Claim 25
Dependent Claim
23 words
The process of claim 1 wherein the dehydrocoupling reaction is conducted at a toluene conversion level of about 20 to about 55 percent.
Claim 26
Dependent Claim
25 words
The process of claim 1 wherein the surface area of the composition is from about 0.05 m 2 /g to about 5 m 2 /g.
Claim 27
Dependent Claim
17 words
The process of claim 1 wherein the composition exhibits an attrition rate less than 0.5 weight percent/hour.
Claim 28
Dependent Claim
38 words
The process of claims 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, or 26 wherein the dehydrocoupled toluene product is stilbene.
References Cited (Backward Citations)
US3668151A
Cited
US3925447A
Cited
US3957691A
Cited
US4254293A
Cited
US4268703A
Cited
US4260845A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-17 | 1987-10-17 | 1988-04-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-17 | 1991-10-17 | 1992-04-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-17 | 1995-10-17 | 1996-04-17 | $7700.00 | Window Closed / Lapsed |