Fireproof coating for wood of thermoplastic resin, alumina trihydrate and glass fibers
Assignee: Individual
•
Filing: 1982-09-29
•
Granted: 1984-04-17
•
Expires: 2002-09-29
Abstract
Abstract There is disclosed a method of coating combustible material such as wood, plywood, shingles and the like with a flameproofing composition. The method employs a flame coating composition which is a mixture of a thermoplastic, ambient-temperature, film former such as a polyvinyl acrylic acetate latex, and alumina trihydrate and glass fibers. The ambient temperature film former is a conventional latex used for coating compositions and should have the property of softening at or below the dehydration temperature of alumina trihydrate (about 280 degrees F.) and be capable of forming a stable foam at such temperatures. The alumina, which comprises the major portion of the coating composition, dehydrates when subjected to flame temperatures and the water vapor released from the alumina forms a stable foam. Additionally, the alumina and the glass fibers, which are used as a filler in the composition, form a refractory coating when subjected to flame and this coating traps the gases and serves as a refractory heat insulation that protects and isolates the combustible material from exposure to the flame and ignition.
Inventors
- 👤 Charles H. Braithwaite, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 13:36
CPC Classifications
C; C09; C09K; C09K21/00; C09K21/14; Y; Y10; Y10S; Y10S428/00; Y10S428/92; Y10S428/921; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31551; Y10T428/31634; Y10T428/31855; Y10T428/3188; Y10T428/31895; Y10T428/31906; Y10T428/31971; Y10T428/31989; Y10T428/4935; Y10T428/662
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
108 words
The method of treating a wood product which comprises: (a) coating at least one surface of said wood product with a suspension of: (i) ambient temperature film former ingredients selected from the class of latexes of polyvinyl acetate, polyacrylates, styrene-butadiene polymers and halogenated derivatives thereof, and copolymers thereof, and (ii) high temperature barrier forming ingredients including from 26 to 30 weight percent of alumina trihydrate, and from 2 to 10 weight percent of glass fibers; (b) drying said coating at a temperature from ambient to about 275 degrees F. for a time sufficient to remove water therefrom and form a dry coating without dehydration of said alumina trihydrate.
Claim 2
Independent Claim
108 words
The method of treating a wood product which comprises: (a) coating at least one surface of said wood product with a suspension of: (i) ambient temperature film former ingredients selected from the class of latexes of polyvinyl acetate, polyacrylates, styrene-butadiene polymers and halogenated derivatives thereof, and copolymers thereof, and (ii) high temperature barrier forming ingredients including from 26 to 30 weight percent of alumina trihydrate, and from 2 to 10 weight percent of glass fibers; (b) drying said coating at a temperature from ambient to about 275 degrees F. for a time sufficient to remove water therefrom and form a dry coating without dehydration of said alumina trihydrate.
Claim 3
Dependent Claim
29 words
The method of claim 1 wherein said suspension is applied at a sufficient dosage to provide a coating with a thickness from 0.02 to 0.100 inch on each face.
Claim 4
Dependent Claim
14 words
The method of claim 2 wherein said wood product is dipped into said suspension.
Claim 5
Dependent Claim
17 words
The method of claim 2 wherein said suspension is sprayed onto a surface of said wood product.
Claim 6
Dependent Claim
29 words
The method of claim 1 wherein said coating is dried by placing said wood product in an oven maintained at a temperature from 250 to about 280 degrees F.
Claim 7
Dependent Claim
17 words
The method of claim 1 wherein said coating is dried by the application of microwave radiation thereto.
Claim 8
Dependent Claim
11 words
The method of claim 1 wherein said latex is polyvinyl acetate.
Claim 9
Dependent Claim
19 words
The method of claim 7 wherein said latex also includes from 3.0 to 5.0 weight percent of a plasticizer.
Claim 10
Dependent Claim
11 words
The method of claim 1 wherein said latex is polyvinylidene chloride.
Claim 11
Dependent Claim
20 words
The method of claim 1 wherein said glass fibers are present in an amount from 3 to 5 weight percent.
Claim 12
Dependent Claim
83 words
A wood product comprising: (a) a wood sheet product having, on both of its opposite, major surfaces, a coating with a thickness from 0.020 to 0.100 inch and comprising: (b) a dried film of a thermoplastic polymer selected from the class of non-cross-linked polyvinyl acetate, polyacrylates, styrene-butadiene polymers, and halogenated derivatives thereof, and as a filler therefore, from 40 to 80 weight percent alumina trihydrate and from 2 to about 10 weight percent glass fibers having lengths from 0.1 to about 0.5 inch.
Claim 13
Dependent Claim
83 words
A wood product comprising: (a) a wood sheet product having, on both of its opposite, major surfaces, a coating with a thickness from 0.020 to 0.100 inch and comprising: (b) a dried film of a thermoplastic polymer selected from the class of non-cross-linked polyvinyl acetate, polyacrylates, styrene-butadiene polymers, and halogenated derivatives thereof, and as a filler therefore, from 40 to 80 weight percent alumina trihydrate and from 2 to about 10 weight percent glass fibers having lengths from 0.1 to about 0.5 inch.
Claim 14
Dependent Claim
11 words
The product of claim 11 wherein said latex is polyvinyl acetate.
Claim 15
Dependent Claim
11 words
The product of claim 11 wherein said latex is polyvinylidene chloride.
Claim 16
Dependent Claim
19 words
The product of claim 11 wherein said latex also includes from 5.0 to 10.0 weight percent of a plasticizer.
References Cited (Backward Citations)
US4223066A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-17 | 1987-10-17 | 1988-04-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-17 | 1991-10-17 | 1992-04-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-17 | 1995-10-17 | 1996-04-17 | $7700.00 | Window Closed / Lapsed |