Method for preparing a thin film amorphous silicon having high reliability
Assignee: NEC Corp
•
Filing: 1981-07-29
•
Granted: 1984-04-10
•
Expires: 2001-07-29
Abstract
Abstract A semiconductor film is prepared by a method wherein a substrate is first disposed as one electrode within a reaction chamber. A supply of semiconductor material is fed into the reaction chamber as the other electrode while introducing a fluoride semiconductor material into said reaction chamber. A high frequency electric field is generated within the reaction chamber to ionize the semiconductor material and decompose the fluoride of the semiconductor material, whereby an amorphous semiconductor film is deposited on the substrate.
Inventors
- 👤 Kesao Noguchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 01:04
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/0021; H; H10; H10P; H10P14/00; H10P14/20; H10P14/22; H10P14/24; H10P14/29; H10P14/2901; H10P14/2902; H10P14/2905; H10P14/2922; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/3438; H10P14/3441; H10P14/3442; H10P14/3444; H10P14/36; H10P14/3602
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
128 words
A method for preparing a semiconductor film by utilizing an ion-plating method, comprising the steps of disposing a substrate within a reaction chamber, providing a semiconductor material, applying an ion accelerating voltage between said substrate and said semiconductor material, evaporating said semiconductor material to supply an evaporated semiconductor gas into said reaction chamber, introducing a fluoride gas of semiconductor material into said reaction chamber, generating a high frequency electric field within said reaction chamber, and controlling a gas pressure within said reaction chamber so that said high frequency electric field causes ionization of said evaporated semiconductor gas but precludes a sputtering of said semiconductor material, whereby said evaporated semiconductor gas is ionized within said reaction chamber and an amorphous semiconductor film containing fluorine is deposited on said substrate.
Claim 2
Independent Claim
128 words
A method for preparing a semiconductor film by utilizing an ion-plating method, comprising the steps of disposing a substrate within a reaction chamber, providing a semiconductor material, applying an ion accelerating voltage between said substrate and said semiconductor material, evaporating said semiconductor material to supply an evaporated semiconductor gas into said reaction chamber, introducing a fluoride gas of semiconductor material into said reaction chamber, generating a high frequency electric field within said reaction chamber, and controlling a gas pressure within said reaction chamber so that said high frequency electric field causes ionization of said evaporated semiconductor gas but precludes a sputtering of said semiconductor material, whereby said evaporated semiconductor gas is ionized within said reaction chamber and an amorphous semiconductor film containing fluorine is deposited on said substrate.
Claim 3
Dependent Claim
33 words
A method for preparing a semiconductor film as claimed in claim 1, wherein said gas pressure within said reaction chamber is controlled within a pressure range of 1×10 -4 to 3×10 -2 Torr.
Claim 4
Dependent Claim
28 words
A method for preparing a semiconductor film as claimed in claim 2, wherein said semiconductor material is silicon and said fluoride of the semiconductor material is silicon tetrafluoride.
Claim 5
Dependent Claim
26 words
A method for preparing a semiconductor film as claimed in claim 2, further comprising the step of introducing an impurity doping gas into said reaction chamber.
Claim 6
Independent Claim
183 words
A method of producing an amorphous silicon film on a substrate by making use of an ion-plating apparatus having a film forming chamber and a silicon evaporating chamber separated from each other, comprising the steps of disposing said substrate within said film forming chamber, applying a potential to said substrate, providing silicon in said silicon evaporating chamber, evaporating said silicon in said silicon evaporating chamber to form silicon gas, supplying said silicon gas from said silicon evaporating chamber into said film forming chamber, introducing silicon tetrafloride gas into said film forming chamber, generating a high frequency electric field within said film forming chamber, and adjusting a gas pressure within said film forming chamber such that said silicon gas supplied into said film forming chamber is ionized when said high frequency electric field is generated in said film forming chamber, whereby said silicon gas within said film forming chamber is ionized and at the same time said silicon tetrafluoride gas is decomposed by said high frequency electric field within said film forming chamber to deposit an amorphous silicon film containing fluorine on said substrate.
Claim 7
Independent Claim
183 words
A method of producing an amorphous silicon film on a substrate by making use of an ion-plating apparatus having a film forming chamber and a silicon evaporating chamber separated from each other, comprising the steps of disposing said substrate within said film forming chamber, applying a potential to said substrate, providing silicon in said silicon evaporating chamber, evaporating said silicon in said silicon evaporating chamber to form silicon gas, supplying said silicon gas from said silicon evaporating chamber into said film forming chamber, introducing silicon tetrafloride gas into said film forming chamber, generating a high frequency electric field within said film forming chamber, and adjusting a gas pressure within said film forming chamber such that said silicon gas supplied into said film forming chamber is ionized when said high frequency electric field is generated in said film forming chamber, whereby said silicon gas within said film forming chamber is ionized and at the same time said silicon tetrafluoride gas is decomposed by said high frequency electric field within said film forming chamber to deposit an amorphous silicon film containing fluorine on said substrate.
Claim 8
Dependent Claim
34 words
A method for producing an amorphous silicon film as claimed in claim 5, wherein said gas pressure within said film forming chamber is adjusted in the range of 1×10 -4 to 3×10 -2 Torr.
Claim 9
Dependent Claim
52 words
A method for producing an amorphous silicon film as claimed in claim 6, wherein a pressure ratio of a partial pressure of said silicon tetrafluoride gas introduced into said film forming chamber to said gas pressure within said film forming chamber is in a range of 2.5×10 -3 to 9.7×10 -1 .
Claim 10
Dependent Claim
52 words
A method for producing an amorphous silicon film as claimed in claim 6 wherein a pressure ratio of a partial pressure of said silicon tetrafluoride gas introduced into said film forming chamber to said gas pressure within said film forming chamber is in a range of 8.7×10 -3 to 9.7×10 -1 .
Claim 11
Dependent Claim
52 words
A method for producing an amorphous silicon film as claimed in claim 6, wherein a pressure ratio of a partial pressure of said silicon tetrafluoride gas introduced into said film forming chamber to said gas pressure within said film forming chamber is in a range of 5.8×10 -2 to 9.7×10 -1 .
Claim 12
Dependent Claim
28 words
A method for producing an amorphous silicon film as claimed in claim 6, further comprising the step of introducing an impurity doping gas into said film forming chamber.
Claim 13
Dependent Claim
38 words
A method for producing an amorphous silicon film as claimed in claim 10, wherein said impurity doping gas is boron trifluoride gas and said doping gas is introduced into said film forming chamber with said silicon tetrafluoride gas.
Claim 14
Dependent Claim
25 words
A method for producing an amorphous silicon film as claimed in claim 6, further comprising the step of introducing hydrogen into said film forming chamber.
Claim 15
Dependent Claim
57 words
A method for producing an amorphous silicon film as claimed in claim 12, wherein said hydrogen is used as a film surface control agent for the film deposited on said substrate, and is mixed with said silicon tetrafluoride gas at a flow rate ratio of 0.01 to 0.13 to the flow rate of said silicon tetrafluoride gas.
Claim 16
Dependent Claim
41 words
A method for producing an amorphous silicon film as claimed in claim 12, wherein said hydrogen is mixed with said silicon tetrafluoride gas at a flow rate ratio of 0.01 to 0.07 to the flow rate of said silicon tetrafluoride gas.
Claim 17
Dependent Claim
37 words
A method for producing an amorphous silicon film as claimed in claim 10, wherein said impurity doping gas is phosphorous pentafluoride, and said doping gas is introduced into said film forming chamber with said silicon tetrafluoride gas.
Claim 18
Dependent Claim
25 words
The method for producing an amorphous silicon film as claimed in claim 6, further comprising the step of introducing hydride into said film forming chamber.
Claim 19
Dependent Claim
59 words
The method for producing an amorphous silicon film as claimed in claim 16, wherein said hydride is used as a film surface control agent for the film deposited on said substrate, and said hydride is mixed with said silicon tetrafluoride gas at a flow rate ratio of 0.01 to 0.13 to the flow rate of said silicon tetrafluoride gas.
Claim 20
Dependent Claim
41 words
The method for producing an amorphous silicon film as claimed in claim 16, wherein said hydride is mixed with said silicon tetrafluoride gas at a flow rate ratio of 0.01 to 0.07 to the flow rate of said silicon tetrafluoride gas.
Claim 21
Dependent Claim
156 words
An ion-plating process of forming an amorphous silicon film comprising the steps of: (a) positioning a source of film material and a substrate in a chamber with said source connected into an electrical circuit as an anode and said substrate connected into said circuit as a cathode, (b) interposing a high frequency electrode between said anode and cathode, (c) energizing said high frequency electrode with sufficient energy to generate a high frequency electric field, whereby the negative charge of said cathode attracts said ions to plate said substrate, (d) evaporating said source of film material to produce a film material gas, and (e) ionizing said film material gas under said high frequency electric field and in a gas pressure within said chamber which precludes any sputtering of said source of film material when said high frequency electric field is generated, whereby the negative charge of said cathode attracts the ionized film materials to plate said substrate.
Claim 22
Dependent Claim
156 words
An ion-plating process of forming an amorphous silicon film comprising the steps of: (a) positioning a source of film material and a substrate in a chamber with said source connected into an electrical circuit as an anode and said substrate connected into said circuit as a cathode, (b) interposing a high frequency electrode between said anode and cathode, (c) energizing said high frequency electrode with sufficient energy to generate a high frequency electric field, whereby the negative charge of said cathode attracts said ions to plate said substrate, (d) evaporating said source of film material to produce a film material gas, and (e) ionizing said film material gas under said high frequency electric field and in a gas pressure within said chamber which precludes any sputtering of said source of film material when said high frequency electric field is generated, whereby the negative charge of said cathode attracts the ionized film materials to plate said substrate.
Claim 23
Dependent Claim
27 words
The process of claim 19 wherein said chamber is a vacuum chamber and the added step of reducing the pressure in said chamber to said gas pressure.
Claim 24
Dependent Claim
16 words
The process of claim 19 and the added step of accelerating said ions toward said cathode.
Claim 25
Dependent Claim
27 words
The process of claim 19 and the added step of reducing the pressure in said chamber to a pressure range of 1×10 -4 to 3×10 -2 Torr.
Claim 26
Dependent Claim
25 words
The process of claim 19 and the added step of introducing silicon tetrafluoride gas into said chamber during the energization of said high frequency electrode.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-10 | 1987-10-10 | 1988-04-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-10 | 1991-10-10 | 1992-04-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-10 | 1995-10-10 | 1996-04-10 | $7700.00 | Window Closed / Lapsed |