Abstract
Abstract Improved impact modifier composition comprising elastomeric impact modifier polymer and dunkelsperser in a weight ratio of about 99.5/0.5 to 96/4 which is subject to substantially reduced gel formation in rigid thermoplastic matrix polymer formulations. Also disclosed are such formulations, as well as processes for preparing the improved impact modifier compositions.
Inventors
- 👤 David L. Dunkelberger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 16:20
CPC Classifications
C; C08; C08L; C08L51/00; C08L51/04; C08L25/00; C08L25/02; C08L25/04; C08L25/08; C08L25/12; C08L27/00; C08L27/02; C08L27/04; C08L27/06; C08L33/00; C08L33/04; C08L33/06; C08L33/10; C08L33/12; C08L67/00; C08L67/02; C08L69/00
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
112 words
An improved impact modifier composition comprising a blend of an elastomeric impact modifier and a dunkelsperser, the weight ratio of said elastomeric impact modifier to said dunkelsperser being from about 99.5 to 0.5 to about 96 to 4, said dunkelsperser being a polymer or a copolymer, said dunkelsperser polymer or copolymer being formed from at least 50 weight percent of at least one of the monomers selected from the group consisting of styrene, substituted styrene, an olefin, and an unsaturated ester of an organic acid different from the methyl ester of methacrylic acid, and where said dunkelsperser substantially reduces gel colonies in a rigid thermoplastic matrix polymer containing said improved modifier composition.
Claim 2
Dependent Claim
112 words
An improved impact modifier composition comprising a blend of an elastomeric impact modifier and a dunkelsperser, the weight ratio of said elastomeric impact modifier to said dunkelsperser being from about 99.5 to 0.5 to about 96 to 4, said dunkelsperser being a polymer or a copolymer, said dunkelsperser polymer or copolymer being formed from at least 50 weight percent of at least one of the monomers selected from the group consisting of styrene, substituted styrene, an olefin, and an unsaturated ester of an organic acid different from the methyl ester of methacrylic acid, and where said dunkelsperser substantially reduces gel colonies in a rigid thermoplastic matrix polymer containing said improved modifier composition.
Claim 3
Dependent Claim
43 words
The composition of claim 1 where said improved impact modifier composition comprising said elastomeric impact modifier and said dunkelsperser reduces gel colonies of said impact modifier composition in said rigid thermoplastic matrix polymer containing said improved impact modifier composition by at least 90%.
Claim 4
Dependent Claim
29 words
Composition of claim 1 wherein said dunkelsperser is a polymer selected from poly(butyl acrylate), poly(butyl methacrylate), poly(butyl methacrylate/styrene), poly(butyl acrylate/styrene), poly(butyl acrylate/methyl methacrylate), poly(butyl acrylate/butyl methacrylate), and poly(ethyl acrylate).
Claim 5
Dependent Claim
24 words
The composition of claim 1 where said improved impact modifier composition comprises a mixture of emulsions of said elastomeric impact modifier and said dunkelsperser.
Claim 6
Dependent Claim
24 words
The composition of claim 4 in the form of a powder formed by isolating said emulsion mixture by spray drying or coagulating said mixture.
Claim 7
Dependent Claim
55 words
A composition comprising the improved impact modifier composition of claim 1 melt blended with a rigid thermoplastic matrix polymer, said composition being substantially free of visible gel colonies, and where the weight ratio of said rigid thermoplastic matrix polymer to said improved impact modifier composition is about 60 to 40 to about 98 to 2.
Claim 8
Dependent Claim
37 words
The composition of claim 6 wherein said rigid thermoplastic matrix polymer is selected from the group consisting of vinyl chloride polymers and copolymers, methyl methacrylate polymers and copolymers, thermoplastic polyesters, styrene-acrylonitrile copolymers, polystyrene, polycarbonate and glutarimide polymers.
Claim 9
Dependent Claim
34 words
The composition of claim 1 wherein said elastomeric impact modifier polymer is a core-shell polymer selected from the group consisting of butadiene-based core-shell polymers, acrylic elastomer-based core-shell polymers, and mixed acrylic-butadiene-based elastomer core-shell polymers.
Claim 10
Dependent Claim
27 words
The composition of claim 1 wherein the weight ratio of said elastomeric impact modifier to said dunkelsperser is about 99 to 1 to about 97 to 3.
Claim 11
Dependent Claim
21 words
The composition of claim 1 wherein the weight ratio of said elastomeric impact modifier to said dunkelsperser is 98 to 2.
Claim 12
Dependent Claim
85 words
A process for preparing improved impact modifier compositions comprising intimately mixing an elastomeric impact modifier polymer and a dunkelsperser polymer or copolymer in a weight ratio of from about 99.5 to 0.5 to about 96 to 4, where said dunkelsperser polymer or copolymer is formed from at least 50 weight percent of at least one of the monomers selected from the group consisting of styrene, substituted styrene, an olefin, and an unsaturated ester of an organic acid different from the methyl ester of methacrylic acid.
Claim 13
Dependent Claim
85 words
A process for preparing improved impact modifier compositions comprising intimately mixing an elastomeric impact modifier polymer and a dunkelsperser polymer or copolymer in a weight ratio of from about 99.5 to 0.5 to about 96 to 4, where said dunkelsperser polymer or copolymer is formed from at least 50 weight percent of at least one of the monomers selected from the group consisting of styrene, substituted styrene, an olefin, and an unsaturated ester of an organic acid different from the methyl ester of methacrylic acid.
Claim 14
Dependent Claim
38 words
The process of claim 11 where emulsions of said elastomeric impact modifier polymer and said dunkelsperser are mixed together to form an emulsion mixture, and isolating said improved impact modifier by spray drying or coagulating said emulsion mixture.
Claim 15
Dependent Claim
28 words
The process of claim 11 where the weight ratio of said elastomeric impact modifier polymer to said dunkelsperser is about 99 to 1 to about 97 to 3.
Claim 16
Dependent Claim
22 words
The process of claim 11 where the weight ratio of said elastomeric impact modifier polymer to said dunkelsperser is 98 to 2.
Claim 17
Dependent Claim
104 words
A process for improving the dispersability of an elastomeric impact modifier in a rigid thermoplastic matrix polymer comprising intimately mixing a dunkelsperser with said elastomeric impact modifier in a weight ratio of elastomeric impact modifier to dunkelsperser of from about 99.5 to 0.5 to about 96 to 4, and where said dunkelsperser is a polymer or copolymer, said dunkelsperser polymer of copolymer being formed from at least 50 weight percent of at least one of the monomers selected from the group consisting of styrene, substituted styrene, an olefin, and an unsaturated ester of an organic acid different from the methy ester of methacrylic acid.
Claim 18
Dependent Claim
104 words
A process for improving the dispersability of an elastomeric impact modifier in a rigid thermoplastic matrix polymer comprising intimately mixing a dunkelsperser with said elastomeric impact modifier in a weight ratio of elastomeric impact modifier to dunkelsperser of from about 99.5 to 0.5 to about 96 to 4, and where said dunkelsperser is a polymer or copolymer, said dunkelsperser polymer of copolymer being formed from at least 50 weight percent of at least one of the monomers selected from the group consisting of styrene, substituted styrene, an olefin, and an unsaturated ester of an organic acid different from the methy ester of methacrylic acid.
Claim 19
Dependent Claim
33 words
The improved impact modifier composition of claim 1 where said unsaturated ester of organic acid is an ester of acrylic acid, an ester of methacrylic acid having four carbon atoms, or copolymers thereof.
Claim 20
Dependent Claim
16 words
The composition of claim 8 where the butadiene-based core-shell polymer is formed from methacrylate-butadiene-styrene or acrylonitrile-butadiene-styrene.
References Cited (Backward Citations)
US3652483A
Cited
US3956424A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-03 | 1987-10-03 | 1988-04-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-03 | 1991-10-03 | 1992-04-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-03 | 1995-10-03 | 1996-04-03 | $7700.00 | Window Closed / Lapsed |