Method for producing a solar selective coating on aluminum

Claim 2

A process for the production of a solar selective coating on aluminum which comprises: (a) pretreating the aluminum surface; (b) anodizing the pretreated aluminum at a constant voltage of at least 10 volts in a phosphoric acid bath for a time period sufficient to provide a total anodizing current of from 90 to 175 coulombs per square decimeter of aluminum surface; (c) coloring the anodized aluminum using alternating current in a coloring bath containing at least 85 grams per liter of metal sulfates at a constant voltage of from 8 to 12 volt RMS for a time sufficient to permit total current flow of from 100 to 325 coulombs per square decimeter; and (d) sealing the colored anodized coating to provide a solar selective coating on aluminum of less than 1 micron thickness and having an infrared emittance of not more than 18% and a solar spectrum absorptance of at least 91%.

Claim 3

The process of claim 1 wherein the aluminum surface pretreatment comprises a caustic etch.

Claim 4

The process of claim 2 wherein said caustic etch comprising treatment with 5% sodium hydroxide for at least 15 seconds at an elevated temperature.

Claim 5

The process of claim 1 wherein the aluminum surface pretreatment comprises an acidic chemical brightening.

Claim 6

The process of claim 4 wherein said acidic chemical brightening pretreatment comprises treatment in a phosphoric-nitric acid bath from about 1-3 minutes at a temperature of from about 87° to 115° C.

Claim 7

The process of claim 1 wherein said constant anodizing voltage is from 10 to 20 volts DC.

Claim 8

The process of claim 6 wherein the constant anodizing voltage is set sufficiently high to provide the total current flow in less than 10 minutes.

Claim 9

The process of claim 1 wherein the phosphoric acid bath has a concentration of from 2.5 to 15 wt.%.

Claim 10

The process of claim 2 wherein the concentration of said phosphoric acid bath is from 10 to 15 wt.%.

Claim 11

The process of claim 4 wherein the concentration of said phosphoric acid bath is from 2.5 to 5 wt.%.

Claim 12

The process of claim 1 wherein the temperature of said anodizing bath is from 20°-40° C.

Claim 13

The process of claim 1 wherein the voltage in said coloring bath is coloring about 10 volts RMS.

Claim 14

The process of claim 12 wherein the coloring bath is maintained at room temperature.

Claim 15

The process of claim 13 wherein the coloring bath is maintained at a pH of from 4.1 to 4.5.

Claim 16

The process of claim 14 wherein the coloring bath comprises boric acid and sulfate salts of cobalt and magnesium.

Claim 17

The process of claim 15 wherein the coloring bath comprises boric acid and sulfate salts of nickel and magnesium.

Claim 18

A process for the production of a solar selective coating of less than 1 micron on an aluminum surface, said coating being further characterized by a solar spectrum absorptance of at least 91% and an infrared emittance of not more than 18%, said process comprising: (a) pretreating the aluminum surface with an etch selected from the class consisting of caustic etches and acid etches; (b) anodizing the etched aluminum surface at a constant voltage of from 10-20 volts DC in a 2.5 to 15 wt.% phosphoric acid bath at a temperature of from 20°-40° C. for a time sufficient to provide a total current flow of from 90-175 coulombs per square decimeter of aluminum surface; (c) coloring the anodized aluminum using alternating current at a constant voltage of from 8-12 volts RMS in a coloring bath containing boric acid and at least 88 grams per liter of metal sulfates comprising magnesium sulfate and a second metal sulfate selected from the class consisting of cobalt sulfate and nickel sulfate at room temperature and a pH of from 4.1 to 4.5 for a time sufficient to provide a total current flow of from 100-325 coulombs per square decimeter of aluminum surface; and (d) sealing the colored anodized aluminum surface with a sealing solution which will not interfere with the solar selectivity of the resultant coating.

Claim 19

A process for the production of a solar selective coating of less than 1 micron on an aluminum surface, said coating being further characterized by a solar spectrum absorptance of at least 91% and an infrared emittance of not more than 18%, said process comprising: (a) pretreating the aluminum surface with an etch selected from the class consisting of caustic etches and acid etches; (b) anodizing the etched aluminum surface at a constant voltage of from 10-20 volts DC in a 2.5 to 15 wt.% phosphoric acid bath at a temperature of from 20°-40° C. for a time sufficient to provide a total current flow of from 90-175 coulombs per square decimeter of aluminum surface; (c) coloring the anodized aluminum using alternating current at a constant voltage of from 8-12 volts RMS in a coloring bath containing boric acid and at least 88 grams per liter of metal sulfates comprising magnesium sulfate and a second metal sulfate selected from the class consisting of cobalt sulfate and nickel sulfate at room temperature and a pH of from 4.1 to 4.5 for a time sufficient to provide a total current flow of from 100-325 coulombs per square decimeter of aluminum surface; and (d) sealing the colored anodized aluminum surface with a sealing solution which will not interfere with the solar selectivity of the resultant coating.

Claim 20

A process for the production of a solar selective coating on an aluminum surface, said process being characterized by capability of operation on a continuous basis, and wherein the thickness of the coating may be accurately controlled by measurement of the cumulative current flow using constant voltage comprising: (a) pretreating the aluminum surface with an etch selected from the class consisting of caustic etches and acid etches; (b) anodizing the pretreated aluminum at a constant voltage of from 10 to 20 volts in a phosphoric acid bath for a time period sufficient to provide a total anodizing current of from 90 to 175 coulombs per square decimeter of aluminum surface; (c) coloring the anodized aluminum using alternating current in a coloring bath containing at least 85 grams per liter of metal sulfates, said alternating current bath being maintained at a constant voltage of from 8 volts to 12 volts RMS for a time sufficient to permit total current flow of from 100 to 325 coulombs per square decimeter; and (d) sealing the colored anodized coating with a sealant which will not interfere with the solar selectivity of the resultant coating; whereby a solar selective coating will be formed on said aluminum surface characterized by a thickness of less than 1 micron, an infrared emittance of not more than 18%, and a solar spectrum absorptance of at least 91%.

Claim 21

A process for the production of a solar selective coating on an aluminum surface, said process being characterized by capability of operation on a continuous basis, and wherein the thickness of the coating may be accurately controlled by measurement of the cumulative current flow using constant voltage comprising: (a) pretreating the aluminum surface with an etch selected from the class consisting of caustic etches and acid etches; (b) anodizing the pretreated aluminum at a constant voltage of from 10 to 20 volts in a phosphoric acid bath for a time period sufficient to provide a total anodizing current of from 90 to 175 coulombs per square decimeter of aluminum surface; (c) coloring the anodized aluminum using alternating current in a coloring bath containing at least 85 grams per liter of metal sulfates, said alternating current bath being maintained at a constant voltage of from 8 volts to 12 volts RMS for a time sufficient to permit total current flow of from 100 to 325 coulombs per square decimeter; and (d) sealing the colored anodized coating with a sealant which will not interfere with the solar selectivity of the resultant coating; whereby a solar selective coating will be formed on said aluminum surface characterized by a thickness of less than 1 micron, an infrared emittance of not more than 18%, and a solar spectrum absorptance of at least 91%.

Claim 22

The process of claim 18 wherein said phosphoric acid anodizing bath has a concentration of from 2.5 to 15 wt.% phosphoric acid.

Claim 23

The process of claim 19 wherein the temperature of said anodizing bath is from 20° to 40° C.

Claim 24

The process of claim 18 wherein said coloring bath also contains boric acid and the pH is maintained at from 4.1 to 4.5.

Claim 25

The process of claim 21 wherein said metal sulfates comprise magnesium sulfate.