Assignee: Alcan Research and Development Ltd
•
Filing: 1976-04-20
•
Granted: 1977-05-10
•
Expires: 1996-04-20
Abstract
Abstract In the process of electrocoloring aluminum by passage of alternating current between anodized aluminum and a counter-electrode while immersed in a bath containing a salt of one or more of the group nickel, cobalt, tin, the range of colors obtainable by the process is extended by subjecting aluminum, which has been anodized under conventional D.C. conditions while immersed in a sulfuric acid-based electrolyte, to an electrolytic treatment in a phosphoric acid based electrolyte before the electrocoloring operation.
Inventors
- 👤 Tahei Asada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 03:04
CPC Classifications
C; C25; C25D; C25D11/00; C25D11/02; C25D11/04; C25D11/18; C25D11/20; C25D11/22; C25D11/12
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
91 words
A process for the production of a coloured anodized aluminum article which comprises forming a porous anodic oxide film of at least 1 micron thickness on aluminum by direct current anodizing in a sulfuric acid-based electrolyte, continuing the anodization of the anodized aluminum under direct current conditions in a phosphoric acid-based electrolyte and finally subjecting the anodized aluminum to passage of alternating current between itself and a counterelectrode while immersed in a bath containing a salt of at least one metal selected from the group consisting of nickel, cobalt and tin.
Claim 2
Dependent Claim
91 words
A process for the production of a coloured anodized aluminum article which comprises forming a porous anodic oxide film of at least 1 micron thickness on aluminum by direct current anodizing in a sulfuric acid-based electrolyte, continuing the anodization of the anodized aluminum under direct current conditions in a phosphoric acid-based electrolyte and finally subjecting the anodized aluminum to passage of alternating current between itself and a counterelectrode while immersed in a bath containing a salt of at least one metal selected from the group consisting of nickel, cobalt and tin.
Claim 3
Dependent Claim
18 words
A process as claimed in claim 1 in which the phosphoric acid-based electrolyte contains 50-150 gms/liter. phosphoric acid.
Claim 4
Dependent Claim
42 words
A process as claimed in claim 2 in which the phosphoric acid-based electrolyte contains at least one additional acid selected from the group consisting of oxalic acid, chromic acid, sulfosalicylic acid, sulfamic acid, tartaric acid, citric acid, gluconic acid and sulfuric acid.
Claim 5
Dependent Claim
28 words
A process as claimed in claim 2 comprising subjecting the sulfuric acid-anodized aluminum to direct current treatment in the phosphoric acid-based electrolyte at a voltage of 20-50 volts.
Claim 6
Dependent Claim
23 words
A process as claimed in claim 4 further comprising maintaining the phosphoric acid-based electrolyte at a temperature in the range of 20°-35° C.
Claim 7
Dependent Claim
24 words
A process as claimed in claim 1 comprising subjecting the anodized aluminum to alternating current for a period of 20 secs. to 12 minutes.
References Cited (Backward Citations)
US3382160A
Cited
US3844908A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-09 | 1980-11-08 | 1981-05-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-09 | 1984-11-08 | 1985-05-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-09 | 1988-11-08 | 1989-05-10 | $7700.00 | Window Closed / Lapsed |