Co Reduced chromyl halide on silica catalyst
Assignee: Phillips Petroleum Co
•
Filing: 1982-08-05
•
Granted: 1984-03-27
•
Expires: 2002-08-05
Abstract
Abstract A silica composition is calcined at a temperature high enough to remove some but not all of the hydroxyl content. Generally temperatures of at least 400° C. are required and temperatures above 1000° C. are undesirable, the most preferred temperature being about 600°-800° C. The thus calcined silica is then treated with chromyl chloride at an elevated temperature and finally given a treatment in a carbon monoxide ambient. While the final composition contains chlorine which is normally considered a catalyst poison, the material is surprisingly active as an olefin polymerization catalyst.
Inventors
- 👤 Max P. McDaniel
- 👤 Phil M. Stricklen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:01
CPC Classifications
C; C08; C08F; C08F10/00; C08F10/02
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
90 words
A method comprising: (1) treating a silica material having surface hydroxy groups in an oxygen containing ambient at a temperature sufficient to remove some but not all of said hydroxy groups; (2) contacting the thus-treated silica with a chromyl halide at an elevated temperature to give a silica composition having both chromium and halogen as a part thereof; and (3) thereafter contacting said chromium and halogen containing silica composition with an ambient comprising carbon monoxide at an elevated temperature to give a final silica composition containing both chromium and halogen.
Claim 2
Independent Claim
90 words
A method comprising: (1) treating a silica material having surface hydroxy groups in an oxygen containing ambient at a temperature sufficient to remove some but not all of said hydroxy groups; (2) contacting the thus-treated silica with a chromyl halide at an elevated temperature to give a silica composition having both chromium and halogen as a part thereof; and (3) thereafter contacting said chromium and halogen containing silica composition with an ambient comprising carbon monoxide at an elevated temperature to give a final silica composition containing both chromium and halogen.
Claim 3
Dependent Claim
11 words
A method according to claim 1 wherein said halogen is chlorine.
Claim 4
Dependent Claim
35 words
A method according to claim 2 wherein said silica is essentially pure silica produced by combining an alkali metal silicate and an acid to form a hydrogel which is thereafter dried to form a xerogel.
Claim 5
Dependent Claim
25 words
A method according to claim 2 wherein said treatment of (1) is carried out in air at a temperature within the range of 400°-1000° C.
Claim 6
Dependent Claim
25 words
A method according to claim 2 wherein said treatment of (1) is carried out in air at a temperature within the range of 600°-800° C.
Claim 7
Dependent Claim
36 words
A method according to claim 2 wherein said contacting with chromyl chloride is carried out by introducing vaporous chromyl chloride at a temperature within the range of about 100°-400° C. into contact with said silica material.
Claim 8
Dependent Claim
25 words
A method according to claim 2 wherein said chromyl chloride is added as a vapor in a gaseous carrier at a temperature of 150°-300° C.
Claim 9
Dependent Claim
26 words
A method according to claim 2 wherein said contacting with said carbon monoxide ambient is carried out at a temperature within the range of 250°-450° C.
Claim 10
Dependent Claim
40 words
A method according to claim 2 wherein said treatment with carbon monoxide is carried out at a temperature within the range of 250°-450° C. and wherein said carbon monoxide ambient is a mixture of carbon monoxide and a gaseous carrier.
Claim 11
Dependent Claim
12 words
A method according to claim 9 wherein said gaseous carrier is nitrogen.
Claim 12
Dependent Claim
84 words
A method according to claim 10 wherein said contacting with chromyl chloride is carried out by introducing vaporous chromyl chloride in a gaseous carrier at a temperature within the range of 150°-300° C. into contact with said silica material and wherein said silica is treated at a temperature within the range of 600°-800° C., wherein said oxygen containing ambient is air, and wherein after said treatment said air is removed by flushing with an inert gas prior to said contacting with said chromyl chloride.
Claim 13
Dependent Claim
9 words
A composition produced by the method of claim 11.
Claim 14
Dependent Claim
9 words
A composition produced by the method of claim 1.
Claim 15
Independent Claim
105 words
A method of producing an olefin polymerization catalyst comprising: treating a silica containing composition with an oxygen containing ambient at a temperature within the range of 400°-1000° C. for a time within the range of 10 minutes to 20 hours; thereafter contacting said thus treated silica with an ambient comprising CrO 2 Cl 2 at a temperature within the range of 100°-400° C. for a time within the range of 1 minute to 10 hours; and thereafter contacting with a carbon monoxide containing ambient at a temperature within the range of 250°-450° C. for a time within the range of 1 minute to 10 hours.
Claim 16
Independent Claim
105 words
A method of producing an olefin polymerization catalyst comprising: treating a silica containing composition with an oxygen containing ambient at a temperature within the range of 400°-1000° C. for a time within the range of 10 minutes to 20 hours; thereafter contacting said thus treated silica with an ambient comprising CrO 2 Cl 2 at a temperature within the range of 100°-400° C. for a time within the range of 1 minute to 10 hours; and thereafter contacting with a carbon monoxide containing ambient at a temperature within the range of 250°-450° C. for a time within the range of 1 minute to 10 hours.
Claim 17
Dependent Claim
31 words
A method according to claim 14 wherein said silica containing composition is a silica xerogel produced by combining a mineral acid and an alkali metal silicate and drying to remove water.
Claim 18
Dependent Claim
40 words
A method according to claim 15 wherein said oxygen containing ambient is air, wherein said chromyl chloride is introduced as vapor along with a gaseous carrier, and wherein said carbon monoxide ambient comprises carbon monoxide and an inert gaseous carrier.
Claim 19
Dependent Claim
13 words
A method according to claim 16 wherein said gaseous inert carrier is nitrogen.
Claim 20
Dependent Claim
31 words
A method according to claim 17 wherein said silica containing composition is produced by combining sodium silicate and a mineral acid to form a hydrogel and drying to form a xerogel.
Claim 21
Dependent Claim
9 words
A catalyst produced by the method of claim 18.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-03-27 | 1987-09-26 | 1988-03-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-03-27 | 1991-09-26 | 1992-03-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-03-27 | 1995-09-26 | 1996-03-27 | $7700.00 | Window Closed / Lapsed |