Vapor-phase method for growing mercury cadmium telluride
Assignee: United States Department of the Army
•
Filing: 1982-09-29
•
Granted: 1984-03-27
•
Expires: 2002-09-29
Abstract
Abstract The growth of mercury cadmium telluride (Hg.sub.(1-x) Cd x Te) alloys carried out by the pyrolytic decomposition of a mixture of Cd and Te alkyls in an atmosphere of Hg vapor; the ternary alloy is deposited as an epitaxial film on a CdTe single crystal substrate. The substrate is carried on a heated susceptor in a reactor vessel. The susceptor also has a cavity in which mercury is heated (at a temperature different from the substrate temperature) to provide Hg vapor. A mixture of dimethyl cadmium and diethyl tellurium gases flows through the reactor, the gases thermally decompose in the vicinity of the substrate, and combine with the Hg vapor to form Hg.sub.(1-x) Cd x Te on the substrate. The relative proportions of dimethyl cadmium and diethyl tellurium determine x in the compound.
Inventors
- 👤 David A. Jackson, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 06:43
CPC Classifications
C; C30; C30B; C30B25/00; C30B25/02; C30B29/00; C30B29/10; C30B29/46; C30B29/48; Y; Y10; Y10S; Y10S117/00; Y10S117/906; Y10S117/907
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
182 words
A method of growing mercury cadmium telluride of the chemical notation Hg.sub.(1-x) Cd x Te, in a cold wall reactor, wherein x is greater than zero and less than 1, on a semiconductor substrate, including the steps of: loading said substrate onto a susceptor; loading mercury in a reservoir in said susceptor; placing said suceptor and its load into a reactor; purging said reactor; differentially radio-frequency heating said susceptor to bring said substrate and said mercury to different predetermined temperatures whereby mercury vapor pervades said reactor and, as said temperatures are reached; admitting alkyl gases to said reactor; controlling the time and the flow rates of said gases, whereby said gases are thermally decomposed in the vicinity of said substrate and at least some of the decomposition products of the gases combine with the mercury vapor to form mercury cadmium telluride on said substrate; stopping the flow of gases, purging the reactor, and controlling the temperature of susceptor to allow annealing of the substrate and cooldown; removing the susceptor and its load from the reactor, and; removing the substrate from the susceptor.
Claim 2
Independent Claim
182 words
A method of growing mercury cadmium telluride of the chemical notation Hg.sub.(1-x) Cd x Te, in a cold wall reactor, wherein x is greater than zero and less than 1, on a semiconductor substrate, including the steps of: loading said substrate onto a susceptor; loading mercury in a reservoir in said susceptor; placing said suceptor and its load into a reactor; purging said reactor; differentially radio-frequency heating said susceptor to bring said substrate and said mercury to different predetermined temperatures whereby mercury vapor pervades said reactor and, as said temperatures are reached; admitting alkyl gases to said reactor; controlling the time and the flow rates of said gases, whereby said gases are thermally decomposed in the vicinity of said substrate and at least some of the decomposition products of the gases combine with the mercury vapor to form mercury cadmium telluride on said substrate; stopping the flow of gases, purging the reactor, and controlling the temperature of susceptor to allow annealing of the substrate and cooldown; removing the susceptor and its load from the reactor, and; removing the substrate from the susceptor.
Claim 3
Dependent Claim
20 words
The method of claim 1 wherein said substrate is chosen from the group comprising: cadmium telluride, indium antimonide, and germanium.
Claim 4
Dependent Claim
15 words
The method of claim 1 wherein said alkyl gases are diethyl telluride and dimethyl cadmium.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-03-27 | 1987-09-26 | 1988-03-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-03-27 | 1991-09-26 | 1992-03-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-03-27 | 1995-09-26 | 1996-03-27 | $7700.00 | Window Closed / Lapsed |