US4438185A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Hydrophilic polymer coated microporous membranes capable of use as a battery separator
Assignee: Celgard LLC
•
Filing: 1982-09-03
•
Granted: 1984-03-20
•
Expires: 2002-09-03
Abstract
Abstract The present invention is directed to microporous membranes having a surfactant impregnated therein which is coated on at least one surface thereof with a polymer coating, such as cellulose acetate. The polymer coating possesses functional groups in the presence of an aqueous alkaline environment which permits it to undergo hydrogen bonding with water and to transport battery electrolyte through the coating by diffusion. The presence of the coating on the normally hydrophobic substrate membrane, when used in conjunction with a suitable surfactant, increases the wettability of the substrate membrane and thereby lowers its electrical resistance. The coating also serves to immobilize various soluble electrode derived ions at the coating-electrolyte interface thereby hindering their penetration into the pores of the substrate microporous membrane. Consequently, the plugging of the pores of the substrate membrane by these ions is substantially reduced thereby increasing the life of a battery in which said coated membranes are used as battery separators.
Inventors
- 👤 Henry T. Taskier
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 05:50
CPC Classifications
B; B01; B01D; B01D69/00; B01D69/12; B01D69/1212; B01D69/1213; H; H01; H01M; H01M50/00; H01M50/40; H01M50/409; H01M50/411; H01M50/414; H01M50/417; H01M50/429; H01M50/449; H01M50/457; H01M50/489; H01M50/491; H01M2300/00; H01M2300/0002; H01M2300/0014; H01M50/454; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
88 words
A process for rendering a normally hydrophobic microporous membrane hydrophilic and reducing the electrical resistance thereof which comprises applying a coating to the surface of said membrane in a manner sufficient to achieve a coating thickness when dry of from about 1 to about 25 microns, said coating being selected from the group consisting of cellulose esters, and polyvinyl alcohol, and impregnating said membrane with a surfactant in a manner and in at least an amount sufficient to render the membrane hydrophilic in the absence of said coating.
Claim 2
Dependent Claim
88 words
A process for rendering a normally hydrophobic microporous membrane hydrophilic and reducing the electrical resistance thereof which comprises applying a coating to the surface of said membrane in a manner sufficient to achieve a coating thickness when dry of from about 1 to about 25 microns, said coating being selected from the group consisting of cellulose esters, and polyvinyl alcohol, and impregnating said membrane with a surfactant in a manner and in at least an amount sufficient to render the membrane hydrophilic in the absence of said coating.
Claim 3
Dependent Claim
35 words
The process of claim 1 wherein the polymer coating is applied as a solution or dispersion and the surfactant is impregnated in the substrate membrane by mixing it with said polymer coating solution or dispersion.
Claim 4
Dependent Claim
12 words
The process of claim 2 wherein the polymer coating is cellulose acetate.
Claim 5
Dependent Claim
129 words
A process for reducing the penetration, of a battery separator which is disposed between a zinc anode and a cathode which constitute the electrodes of at least one rechargeable electrolytic cell employing an alkaline electrolyte, by electrode derived ions which comprises employing as the battery separator at least one normally hydrophobic microporous membrane which has been rendered hydrophilic by applying a coating to the surface of said membrane in a manner sufficient to achieve a coating thickness when dry of from about 1 to about 25 microns, said coating being selected from the group consisting of cellulose esters, and polyvinyl alcohol, and impregnating said membrane with a surfactant in a manner and in at least an amount sufficient to render the membrane hydrophilic in the absence of said coating.
Claim 6
Dependent Claim
129 words
A process for reducing the penetration, of a battery separator which is disposed between a zinc anode and a cathode which constitute the electrodes of at least one rechargeable electrolytic cell employing an alkaline electrolyte, by electrode derived ions which comprises employing as the battery separator at least one normally hydrophobic microporous membrane which has been rendered hydrophilic by applying a coating to the surface of said membrane in a manner sufficient to achieve a coating thickness when dry of from about 1 to about 25 microns, said coating being selected from the group consisting of cellulose esters, and polyvinyl alcohol, and impregnating said membrane with a surfactant in a manner and in at least an amount sufficient to render the membrane hydrophilic in the absence of said coating.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-03-20 | 1987-09-19 | 1988-03-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-03-20 | 1991-09-19 | 1992-03-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-03-20 | 1995-09-19 | 1996-03-20 | $7700.00 | Window Closed / Lapsed |