Modified laser-annealing process for improving the quality of electrical P-N junctions and devices
Assignee: ENERGY United States, Department of
•
Filing: 1982-02-19
•
Granted: 1984-03-13
•
Expires: 2002-02-19
Abstract
Abstract The invention is a process for producing improved electrical-junction devices. The invention is applicable, for example, to a process in which a light-sensitive electrical-junction device is produced by (1) providing a body of crystalline semiconductor material having a doped surface layer, (2) irradiating the layer with at least one laser pulse to effect melting of the layer, (3) permitting recrystallization of the melted layer, and (4) providing the resulting body with electrical contacts. In accordance with the invention, the fill-factor and open-circuit-voltage parameters of the device are increased by conducting the irradiation with the substrate as a whole at a selected elevated temperature, the temperature being selected to effect a reduction in the rate of the recrystallization but insufficient to effect substantial migration of impurities within the body. In the case of doped silicon substrates, the substrate may be heated to a temperature in the range of from about 200 DEG C. to 500 DEG C.
Inventors
- 👤 Richard F. Wood
- 👤 Rosa T. Young
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 17:38
CPC Classifications
H; H10; H10F; H10F71/00; H10F71/121; H10F10/00; H10F10/10; H10F10/14; H10F71/128; H10F71/133; H10F71/134; H10P; H10P34/00; H10P34/40; H10P34/42; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/547; Y02P; Y02P70/00; Y02P70/50; Y10; Y10S; Y10S148/00; Y10S148/09; Y10S148/092; Y10S148/093
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
118 words
In a process for producing a light-responsive electrical-junction device, said process including the steps of providing a body of crystalline semiconductor material having a doped surface layer, irradiating said layer with at least one laser pulse to effect melting of the same, permitting recrystallization of the material so melted, and providing the resulting body with electrical contacts, the method of increasing the open-circuit-voltage parameter for said device, comprising: heating said body to a selected temperature and conducting said irradiating operation while said body is so heated to effect an increase in said parameter, said temperature being sufficient to effect a reduction in the rate of said recrystallization but insufficient to effect substantial migration of impurities within said body.
Claim 2
Dependent Claim
118 words
In a process for producing a light-responsive electrical-junction device, said process including the steps of providing a body of crystalline semiconductor material having a doped surface layer, irradiating said layer with at least one laser pulse to effect melting of the same, permitting recrystallization of the material so melted, and providing the resulting body with electrical contacts, the method of increasing the open-circuit-voltage parameter for said device, comprising: heating said body to a selected temperature and conducting said irradiating operation while said body is so heated to effect an increase in said parameter, said temperature being sufficient to effect a reduction in the rate of said recrystallization but insufficient to effect substantial migration of impurities within said body.
Claim 3
Dependent Claim
14 words
The process of claim 1 wherein said material is one of silicon and germanium.
Claim 4
Dependent Claim
20 words
The process of claim 1 wherein said temperature is in the range from about 100° C. to about 500° C.
Claim 5
Dependent Claim
15 words
The process of claim 1 wherein said laser pulse is generated by a Q-switched laser.
Claim 6
Dependent Claim
19 words
The process of claim 3 wherein said temperature is in the range from about 400° C. to 500° C.
Claim 7
Dependent Claim
111 words
In a process for producing an electrical-junction device, said process including the steps of providing a body of crystalline semiconductor material having a doped surface layer, irradiating said layer with at least one laser pulse to effect melting of the same, permitting recrystallization of the material so melted, and providing the resulting body with electrical contacts, the method of decreasing the reverse-saturation-current parameter for said device, comprising: heating said body to a temperature in the range from about 100° C. to 500° C. and conducting said irradiating operation with one of a Q-switched ruby laser and Nd:YAG laser while said body is so heated to effect a decrease in said parameter.
Claim 8
Dependent Claim
111 words
In a process for producing an electrical-junction device, said process including the steps of providing a body of crystalline semiconductor material having a doped surface layer, irradiating said layer with at least one laser pulse to effect melting of the same, permitting recrystallization of the material so melted, and providing the resulting body with electrical contacts, the method of decreasing the reverse-saturation-current parameter for said device, comprising: heating said body to a temperature in the range from about 100° C. to 500° C. and conducting said irradiating operation with one of a Q-switched ruby laser and Nd:YAG laser while said body is so heated to effect a decrease in said parameter.
Claim 9
Dependent Claim
14 words
The process of claim 6 wherein said material is one of silicon and germanium.
Claim 10
Dependent Claim
121 words
In a process for producing an electrical-junction device, said process including the steps of providing a body of crystalline semiconductor material having a film of dopant deposited on a surface layer thereof, irradiating said film and layer with at least one laser pulse to effect melting of the same, permitting recrystallization of the material so melted, and providing the resulting body with electrical contacts, the method of increasing the fill-factor parameter for said device, comprising: conducting said irradiating operation a Q-switched laser while said body is heated to a temperature effecting an increased in said parameter, said temperature being sufficient to effect a reduction in the rate of recrystallization but not sufficient to effect substantial migration of impurities within said body.
Claim 11
Dependent Claim
121 words
In a process for producing an electrical-junction device, said process including the steps of providing a body of crystalline semiconductor material having a film of dopant deposited on a surface layer thereof, irradiating said film and layer with at least one laser pulse to effect melting of the same, permitting recrystallization of the material so melted, and providing the resulting body with electrical contacts, the method of increasing the fill-factor parameter for said device, comprising: conducting said irradiating operation a Q-switched laser while said body is heated to a temperature effecting an increased in said parameter, said temperature being sufficient to effect a reduction in the rate of recrystallization but not sufficient to effect substantial migration of impurities within said body.
Claim 12
Dependent Claim
19 words
The process of claim 8 wherein said temperature is in the range from about 100° C. to 550° C.
Claim 13
Dependent Claim
20 words
The process of claim 9 wherein said temperature is in the range from about 400° C. to about 500° C.
Claim 14
Dependent Claim
125 words
In a process for producing a light-responsive electrical-junction device, said process including the steps of providing a body of crystalline semiconductor material selected from the group consisting of silicon and germanium and having a doped surface layer, irradiating said layer with at least one laser pulse to effect melting of the same, permitting recrystallization of the material so melted, and providing the resulting body with electrical contacts, the method of increasing the fill-factor parameter for said device, comprising: heating said body to a selected temperature and conducting said irradiating operation while said body is so heated to increase said parameter, said temperature being sufficient to effect a reduction in the rate of said recrystallization but insufficient to effect substantial migration of impurities within said body.
Claim 15
Dependent Claim
125 words
In a process for producing a light-responsive electrical-junction device, said process including the steps of providing a body of crystalline semiconductor material selected from the group consisting of silicon and germanium and having a doped surface layer, irradiating said layer with at least one laser pulse to effect melting of the same, permitting recrystallization of the material so melted, and providing the resulting body with electrical contacts, the method of increasing the fill-factor parameter for said device, comprising: heating said body to a selected temperature and conducting said irradiating operation while said body is so heated to increase said parameter, said temperature being sufficient to effect a reduction in the rate of said recrystallization but insufficient to effect substantial migration of impurities within said body.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-03-13 | 1987-09-12 | 1988-03-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-03-13 | 1991-09-12 | 1992-03-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-03-13 | 1995-09-12 | 1996-03-13 | $7700.00 | Window Closed / Lapsed |