Abstract
Abstract Process for making porous, substantially spherical particles having high bulk density of vinyl polymers or resins by the use of the suspension polymerization technique. In the polymerization there is employed a water-insoluble dispersant comprised of a substantially unneutralized crosslinked interpolymer of one or more carboxylic acid monomers with a polyunsaturated compound having a plurality of terminally unsaturated polymerizable groups and a surfactant system comprising at least one surfactant selected from the group consisting of a polyethylene oxide containing surfactant and a non-polyethylene oxide containing surfactant. Excellent results are obtained when both a polyethylene oxide and a non-polyethylene oxide containing surfactant are used in the process of the invention. Rapid stirring or high agitation is used while employing a monomer-soluble free radical yielding polymerization catalyst.
Inventors
- 👤 Kornelius Dinbergs
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 17:15
CPC Classifications
C; C08; C08F; C08F14/00; C08F14/02; C08F14/04; C08F14/06; C08F2/00; C08F2/12; C08F2/16; C08F2/22; C08F2/24; C08F2/30; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
185 words
A process for producing spherical particles of polymer having a high porosity which comprises polymerizing in an aqueous medium, in a reaction vessel having an agitator position therein, one or more ethylenically unsaturated monomers having a terminal CH 2 ═C< grouping in the form of discrete particles having a diameter in the range of about 30 microns to about 1000 microns, said aqueous medium containing a monomer-soluble free radical yielding catalyst, a dispersant comprising a substantially unneutralized, water-insoluble, cross-linked polymer of one or moe carboxylic acid monomers with a polyunsaturated crosslinking monomer havng a plurality of terminally unsaturated polymerizable groups, at least one non-polyethylene oxide containing surfactant selected from the group consisting of the sorbitan ester family, glycerol ester family, and polyglycerol ester family, and at least one polyethylene oxide containing surfactant selected from the group consisting of polyoxyethylene alkylphenols, polyoxyethylene alcohols, polyoxyethylene esters of fatty acids, polyoxyethylene alkylamines, and polyoxyethylene alkylamides and polyoxyethylene sorbitan ester, conducting the polymerization at a temperature in the range of about 0° C. to about 150° C. with vigorous agitation in said aqueous medium throughout the entire polymerization reaction.
Claim 2
Dependent Claim
185 words
A process for producing spherical particles of polymer having a high porosity which comprises polymerizing in an aqueous medium, in a reaction vessel having an agitator position therein, one or more ethylenically unsaturated monomers having a terminal CH 2 ═C< grouping in the form of discrete particles having a diameter in the range of about 30 microns to about 1000 microns, said aqueous medium containing a monomer-soluble free radical yielding catalyst, a dispersant comprising a substantially unneutralized, water-insoluble, cross-linked polymer of one or moe carboxylic acid monomers with a polyunsaturated crosslinking monomer havng a plurality of terminally unsaturated polymerizable groups, at least one non-polyethylene oxide containing surfactant selected from the group consisting of the sorbitan ester family, glycerol ester family, and polyglycerol ester family, and at least one polyethylene oxide containing surfactant selected from the group consisting of polyoxyethylene alkylphenols, polyoxyethylene alcohols, polyoxyethylene esters of fatty acids, polyoxyethylene alkylamines, and polyoxyethylene alkylamides and polyoxyethylene sorbitan ester, conducting the polymerization at a temperature in the range of about 0° C. to about 150° C. with vigorous agitation in said aqueous medium throughout the entire polymerization reaction.
Claim 3
Dependent Claim
13 words
A process as defined in claim 1 wherein the monomer is vinyl chloride.
Claim 4
Dependent Claim
27 words
A process as defined in claim 1 wherein the monomer(s) to water ratio is in the range of about 1.0 to 1.0 to about 1.0 to 10.0.
Claim 5
Dependent Claim
30 words
A process as defined in claim 1 wherein the dispersant is employed in the range of about 0.02% to about 2.00% by weight, based on the weight of the monomer(s).
Claim 6
Dependent Claim
25 words
A process as defined in claim 1 wherein the polymerization reaction is conducted at a pH in the range of about 3.0 to about 4.3.
Claim 7
Dependent Claim
35 words
A process as defined in claim 1 wherein the crosslinking monomer is employed in the range of about 0.1% to 4.0% by weight, based on the weight of the monomers used in making the dispersant.
Claim 8
Dependent Claim
18 words
A process as defined in claim 1 wherein the dispersant is a lightly crosslinked interpolymer of acrylic acid.
Claim 9
Dependent Claim
25 words
A process as defined in claim 1 wherein the dispersant is polyacrylic acid crosslinked with 0.2 to 0.3 part/100 parts of monomer of allyl pentaerythritol.
Claim 10
Dependent Claim
23 words
A process as defined in claim 1 wherein the dispersant is polyacrylic acid crosslinked with 1.3 parts/100 parts of monomer of allyl sucrose.
Claim 11
Dependent Claim
23 words
A process as defined in claim 1 wherein the dispersant is polyacrylic acid crosslinked with 0.7 part/100 parts of monomer of allyl pentaerythritol.
Claim 12
Dependent Claim
19 words
A process as defined in claim 1 wherein the polyethylene oxide containing surfactant is polyoxyethylene (20 ) sorbitan monooleate.
Claim 13
Dependent Claim
18 words
A process as defined in claim 1 wherein the polyethylene oxide containing surfactant is polyoxyethylene (21) coconut ester.
Claim 14
Dependent Claim
40 words
A process as defined in claim 1 wherein said agitator is operated at an rpm of from about 10 rpm to 275 rpm with a blade tip speed in the range of from about 2 ft./sec. to about 65 ft./sec.
Claim 15
Dependent Claim
23 words
A process as defined in claim 1 wherein said reaction vessel has a capacity of from about 30 gallons to about 40,000 gallons.
Claim 16
Dependent Claim
28 words
A process as defined in claim 2 wherein the monomer(s) to water ratio is in the range of about 1.0 to 1.0 to about 1.0 to about 4.0.
Claim 17
Dependent Claim
30 words
A process as defined in claim 15 wherein the dispersant is employed in the range of about 0.04% to about 0.50% by weight, based on the weight of the monomer(s).
Claim 18
Dependent Claim
25 words
A process as defined in claim 16 wherein the polymerization reaction is conducted at a pH in the range of about 3.0 to about 4.3.
Claim 19
Dependent Claim
40 words
A process as defined in claim 17 wherein the crosslinking monomer is a polyalkenyl polyether and employed in the range of about 0.20% to about 2.5% by weight, based on the weight of the monomers used in making the dispersant.
Claim 20
Dependent Claim
18 words
A process as defined in claim 18 wherein the dispersant is a lightly crosslinked interpolymer of acrylic acid.
Claim 21
Dependent Claim
23 words
A process as defined in claim 19 wherein the dispersant is polyacrylic acid crosslinked with 1.3 parts/100 parts of monomer of allyl sucrose.
Claim 22
Dependent Claim
25 words
A process as defined in claim 19 wherein the dispersant is polyacrylic acid crosslinked with 0.2 to 0.3 part/100 parts of monomer of allyl pentaerythritol.
Claim 23
Dependent Claim
36 words
A process as defined in claim 1 wherein the non-polyethylene oxide containing surfactant is selected from the group consisting of sorbitan trioleate, sorbitan tristearate, sorbitan monooleate, and sorbitan monopalmitate, glycerol monooleate, glycerol monostearate, and triglycerol monooleate.
Claim 24
Dependent Claim
36 words
A process as defined in claim 1 wherein the polyethylene oxide containing surfactant is used at a level of from about 0.005 to about 1.0 parts by weight per 100 parts by weight of the monomer(s).
Claim 25
Dependent Claim
36 words
A process as defined in claim 1 wherein the non-polyethylene oxide containing surfactant is used at a level of from about 0.005 to about 0.20 parts by weight per 100 parts by weight of the monomer(s).
References Cited (Backward Citations)
US4360651A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-03-06 | 1987-09-05 | 1988-03-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-03-06 | 1991-09-05 | 1992-03-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-03-06 | 1995-09-05 | 1996-03-06 | $7700.00 | Window Closed / Lapsed |