Catalyst composition
Assignee: USI CHEMICALS Co Inc
•
Filing: 1982-11-24
•
Granted: 1984-03-06
•
Expires: 2002-11-24
Abstract
Abstract Vanadium compound/organometallic compound/inorganic oxide catalyst compositions useful for the polymerization of ethylene to polymers having an intermediate molecular weight distribution that can be predictably controlled by the use of a "tunable" variable are obtained by using, as the vanadium component, a mixture of about 10-90 mol percent of VOCl 3 and, correspondingly, about 90-10 mol percent of VCl 4 . The molecular weight distributions of polymers formed in the presence of the catalyst compositions are narrowed as the proportionation of VCl 4 in the vanadium component is increased.
Inventors
- 👤 David E. Aylward
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 04:28
CPC Classifications
C; C08; C08F; C08F10/00
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
188 words
A catalyst composition consisting essentially of the product obtained by: (1) drying an inorganic oxide having surface hydroxyl groups to form a support that is substantially free of adsorbed water, (2) reacting the surface hydroxyl groups of the support with at least about 0.5 mol, per mol of surface hydroxyl groups, of at least one organometallic compound corresponding to the formula R x MR' y R" z , wherein M is a metal of Group III of the periodic table, R is an alkyl group containing 1 to 12 carbon atoms, R' and R" are independently selected from the group consisting of H, Cl, and alkyl and alkoxy groups containing 1 to 12 carbon atoms, x has a value of 1 to 3, and y and z both represent values of 0 to 2, the sum of which is not greater than 3-x, and (3) reacting the thus-treated support with at least about 0.001 molar proportion, per mol of organometallic compound, of a vanadium component consisting essentially of a mixture of about 10-90 mol percent of VOCl 3 and, correspondingly, about 90-10 mol percent of VCl 4 .
Claim 2
Dependent Claim
188 words
A catalyst composition consisting essentially of the product obtained by: (1) drying an inorganic oxide having surface hydroxyl groups to form a support that is substantially free of adsorbed water, (2) reacting the surface hydroxyl groups of the support with at least about 0.5 mol, per mol of surface hydroxyl groups, of at least one organometallic compound corresponding to the formula R x MR' y R" z , wherein M is a metal of Group III of the periodic table, R is an alkyl group containing 1 to 12 carbon atoms, R' and R" are independently selected from the group consisting of H, Cl, and alkyl and alkoxy groups containing 1 to 12 carbon atoms, x has a value of 1 to 3, and y and z both represent values of 0 to 2, the sum of which is not greater than 3-x, and (3) reacting the thus-treated support with at least about 0.001 molar proportion, per mol of organometallic compound, of a vanadium component consisting essentially of a mixture of about 10-90 mol percent of VOCl 3 and, correspondingly, about 90-10 mol percent of VCl 4 .
Claim 3
Dependent Claim
24 words
The composition of claim 1 wherein the support is an inorganic oxide selected from the group consisting of silica, alumina, magnesia, and mixtures thereof.
Claim 4
Dependent Claim
11 words
The composition of claim 2 wherein the inorganic oxide is silica.
Claim 5
Dependent Claim
62 words
The composition of claim 1 wherein the organometallic compound is a compound corresponding to the formula RAlR'R", wherein at least one of the R, R', and R" substituents is an alkyl group containing 1 to 12 carbon atoms and the remaining substituents are independently selected from the group consisting of hydrogen and alkyl and alkoxy groups containing 1 to 12 carbon atoms.
Claim 6
Dependent Claim
12 words
The composition of claim 4 wherein the organometallic compound is a trialkylaluminum.
Claim 7
Dependent Claim
10 words
The composition of claim 5 wherein the trialkylaluminum is triethylaluminum.
Claim 8
Dependent Claim
20 words
The composition of claim 1 wherein the vanadium component contains at least about 40 mol percent of VCl 4 .
Claim 9
Dependent Claim
35 words
The composition of claim 1 wherein the amounts of materials employed in its preparation are such as to provide, as starting materials, about 5 to 30 mols of organometallic compound per mol of vanadium compound.
Claim 10
Dependent Claim
32 words
The composition of claim 1 wherein the organometallic compound is employed in an amount such as to provide at least about one mol of organometallic compound per mol of surface hydroxyl groups.
Claim 11
Dependent Claim
25 words
The composition of claim 9 wherein the amount of organometallic compound reacted with the surface hydroxyl groups of the support is the substantially stoichiometric amount.
Claim 12
Dependent Claim
81 words
A process for preparing the catalyst composition of claim 1 which consists essentially of (1) drying the inorganic oxide to remove substantially all adsorbed water, (2 ) slurrying the dried inorganic oxide in an inert liquid hydrocarbon, (3) adding at least a substantially stoichiometric amount of the organometallic compound to react it with the surface hydroxyl groups of the inorganic oxide, (4) adding the vanadium component to react it with the treated inorganic oxide, and (5) drying the composition thus formed.
Claim 13
Dependent Claim
34 words
The process of claim 11 wherein the inorganic oxide is dried at about 100° to 1000° C. until substantially all adsorbed water is removed and is then cooled to ambient temperature before being slurried.
Claim 14
Dependent Claim
21 words
The process of claim 12 wherein the inorganic oxide is silica and the drying temperature is about 200° to 600° C.
Claim 15
Dependent Claim
21 words
The process of claim 12 wherein the inorganic oxide is magnesia and the drying temperature is about 200° to 600° C.
Claim 16
Dependent Claim
21 words
The process of claim 12 wherein the inorganic oxide is alumina and the drying temperature is about 200° to 600° C.
Claim 17
Dependent Claim
20 words
The process of claim 11 wherein the organometallic and vanadium compounds are added to the reaction mixture in neat form.
Claim 18
Dependent Claim
30 words
The process of claim 11 wherein at least one of the organometallic and vanadium compounds is added to the reaction mixture in the form of an inert liquid hydrocarbon solution.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-03-06 | 1987-09-05 | 1988-03-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-03-06 | 1991-09-05 | 1992-03-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-03-06 | 1995-09-05 | 1996-03-06 | $7700.00 | Window Closed / Lapsed |