Abrasion resistant silicon nitride based articles

Claim 2

A densified composite ceramic article consisting essentially of particles of hard refractory material uniformly distributed in a two phase matrix, said two phase matrix consisting essentially of a first phase and a second intergranular phase, said particles of hard refractory material being present in an amount from about 1 to about 60 volume percent of said densified composite ceramic article, said particles of hard refractory material selected from the group consisting of the carbides, nitrides, and mixtures thereof of titanium, vanadium, chromium, zirconium, niobium, molybdenum, hafnium, tantalum, tungsten, and combinations thereof, said particles having an average size of less than about 20 microns, said first phase consisting essentially of crystalline silicon nitride, said second intergranular phase consisting essentially of silicon nitride and a densification aid, said densification aid selected from the group consisting of yttrium oxide, hafnium oxide, the lanthanide rare earth oxides, and mixtures thereof, wherein said densification aid comprises from about 1 to about 25 weight percent of said two phase matrix, said densified composite ceramic article having a high density, a high abrasion resistance, a high hardness, a high fracture strength and a resistance to oxidation at temperatures greater than 1200° C.

Claim 3

A densified composite ceramic article in accordance with claim 1 wherein said particles of hard refractory material are selected from the carbides of titanium, vanadium, chromium, zirconium, niobium, molybdenum, hafnium, tantalum, tungsten, and combinations thereof.

Claim 4

A densified composite ceramic article in accordance with claim 1 wherein said particles of hard refractory material are selected from the nitrides of titanium, vanadium, chromium, zirconium, niobium, molybdenum, hafnium, tantalum, tungsten, and combinations thereof.

Claim 5

A densified composite ceramic article in accordance with claim 1 wherein said densification aid is yttrium oxide or hafnium oxide.

Claim 6

A densified composite ceramic article in accordance with claim 1 wherein said particles of hard refractory material comprise from about 15 to about 50 volume percent of said article.

Claim 7

A densified composite ceramic article in accordance with claim 1 wherein said particles of hard refractory material consist essentially of titanium carbide.

Claim 8

A densified composite ceramic article in accordance with claim 1 wherein said densification aid consists essentially of a mixture of hafnium oxide and yttrium oxide.

Claim 9

A densified composite ceramic cutting tool consisting essentially of particles of hard refractory material uniformly distributed in a two phase matrix, said two phase matrix consisting essentially of a first phase and a second intergranular phase, said particles of hard refractory material being present in an amount from about 1 to about 60 volume percent of said densified composite ceramic cutting tool, said particles of hard refractory material selected from the group consisting of the carbides, nitrides, and mixtures thereof of titanium, vanadium, chromium, zirconium, niobium, molybdenum, hafnium, tantalum, tungsten, and combinations thereof, said particles having an average size of less than about 20 microns, said first phase consisting essentially of crystalline silicon nitride, said second intergranular phase consisting essentially of silicon nitride and a densification aid, said densification aid selected from the group consisting of yttrium oxide, hafnium oxide, and lanthanide rare earth oxides, and mixtures thereof, wherein said densification aid comprises from about 1 to about 25 weight percent of said two phase matrix, said two phase matrix containing less than 3 weight percent aluminum oxide, said densified composite ceramic article having a high density, a high abrasion resistance, a high hardness, a high fracture strength and a resistance to oxidation at temperatures greater than 1200° C.

Claim 10

A densified composite ceramic cutting tool consisting essentially of particles of hard refractory material uniformly distributed in a two phase matrix, said two phase matrix consisting essentially of a first phase and a second intergranular phase, said particles of hard refractory material being present in an amount from about 1 to about 60 volume percent of said densified composite ceramic cutting tool, said particles of hard refractory material selected from the group consisting of the carbides, nitrides, and mixtures thereof of titanium, vanadium, chromium, zirconium, niobium, molybdenum, hafnium, tantalum, tungsten, and combinations thereof, said particles having an average size of less than about 20 microns, said first phase consisting essentially of crystalline silicon nitride, said second intergranular phase consisting essentially of silicon nitride and a densification aid, said densification aid selected from the group consisting of yttrium oxide, hafnium oxide, and lanthanide rare earth oxides, and mixtures thereof, wherein said densification aid comprises from about 1 to about 25 weight percent of said two phase matrix, said two phase matrix containing less than 3 weight percent aluminum oxide, said densified composite ceramic article having a high density, a high abrasion resistance, a high hardness, a high fracture strength and a resistance to oxidation at temperatures greater than 1200° C.

Claim 11

A densified composite ceramic cutting tool in accordance with claim 8 wherein said particles of hard refractory material are selected from the group consisting of the carbides of titanium, vanadium, chromium, zirconium, niobium, molybdenum, hafnium, tantalum, tungsten and combinations thereof.

Claim 12

A densified composite ceramic cutting tool in accordance with claim 8 wherein said particles of hard refractory material are selected from the groups consisting of the nitrides of titanium, vanadium, chromium, zirconium, niobium, molybdenum, hafnium, tantalum, tungsten, and combinations thereof.

Claim 13

A densified composite ceramic cutting tool in accordance with claim 8 wherein said particles of hard refractory material comprise from about 15 to about 50 volume percent of said composite ceramic cutting tool.

Claim 14

A densified composite ceramic cutting tool in accordance with claim 8 wherein said densification aid is yttrium oxide or hafnium oxide.

Claim 15

A densified composite ceramic cutting tool in accordance with claim 8 wherein said densification aid is a mixture of yttrium oxide and hafnium oxide.

Claim 16

A densified composite ceramic cutting tool in accordance with claim 8 wherein said particles of hard refractory material consist essentially of titanium carbide.

Claim 17

A densified composite ceramic article in accordance with claim 1 wherein said high hardness of said densified composite ceramic article is greater than the combined individual hardness of the fractional weight of silicon nitride times the hardness of silicon nitride plus the fractional weight of hard refractory material times the hardness of the hard refractory material.

Claim 18

A densified composite ceramic article in accordance with claim 1 wherein said high density is approximately 100 percent of theoretical density.

Claim 19

A densified composite ceramic article in accordance with claim 1 wherein said high hardness is greater than 91 on the Rockwell A scale.

Claim 20

A densified composite ceramic article in accordance with claim 1 wherein said particles of hard refractory material and said two phase matrix are selected to obtain a hardness of said densified composite ceramic article being greater than 91 on the Rockwell A scale and greater than the combined individual hardness of silicon nitride plus the fractional weight of hard refractory material times the hardness of the hard refractory material, said particles of hard refractory material selected from the group consisting of titanium carbide, tantalum carbide, tungsten carbide and combinations thereof.

Claim 21

A densified composite ceramic article in accordance with claim 1 wherein said particles have an average size of less than 5 microns.

Claim 22

A densified composite ceramic article in accordance with claim 1 wherein said particles have an average size from about 5 microns to about 20 microns.

Claim 23

A densified composite ceramic cutting tool in accordance with claim 8 wherein said high hardness of said densified composite ceramic cutting tool is greater than the combined individual hardness of the fractional weight of silicon nitride times the hardness of silicon nitride plus the fractional weight of hard refractory material times the hardness of the hard refractory material, said hard refractory material selected from the group consisting of titanium carbide, tantalum carbide, tungsten carbide and combinations thereof.

Claim 24

A densified composite ceramic cutting tool in accordance with claim 8 wherein said high density is approximately 100 percent of theoretical density.

Claim 25

A densified composite ceramic cutting tool in accordance with claim 8 wherein said high hardness is greater than 91 on the Rockwell A scale.

Claim 26

A densified composite ceramic cutting tool in accordance with claim 8 wherein said particles of hard refractory material and said two phase matrix are selected to obtain a hardness of said densified composite ceramic cutting tool being greater than 91 on the Rockwell A scale and greater than the combined individual hardness of silicon nitride plus the fractional weight of hard refractory material times the hardness of the hard refractory material.

Claim 27

A densified composite ceramic cutting tool in accordance with claim 8 wherein said particles have an average size of less than 5 microns.

Claim 28

A densified composite ceramic cutting tool consisting essentially of particles of titanium carbide uniformly distributed in a two phase matrix, said two phase matrix consisting essentially of a first phase and a second intergranular phase, said particles of titanium carbide being present in an amount from about 15 to about 50 volume percent of said densified composite ceramic cutting tool, said particles of titanium carbide having an average size of less than about 20 microns, said first phase consisting essentially of crystalline silicon nitride, said second intergranular phase consisting essentially of silicon nitride, yttrium oxide and aluminum oxide, wherein said yttrium oxide comprises from about 1 to about 25 weight percent of said two phase matrix, said two phase matrix containing less than 3 weight percent of said aluminum oxide, said densified composite ceramic cutting tool having a high density, a high abrasion resistance, a high hardness, a high fracture strength and a resistance to oxidation at temperatures greater than 1200° C., said high hardness of said densified composite ceramic cutting tool being greater than 91 on the Rockwell A scale and greater than the combined individual hardness of silicon nitride plus the fractional weight of hard refractory material times the hardness of the hard refractory material, and said high density being approximately 100 percent of theoretical density.

Claim 29

A densified composite ceramic cutting tool consisting essentially of particles of titanium carbide uniformly distributed in a two phase matrix, said two phase matrix consisting essentially of a first phase and a second intergranular phase, said particles of titanium carbide being present in an amount from about 15 to about 50 volume percent of said densified composite ceramic cutting tool, said particles of titanium carbide having an average size of less than about 20 microns, said first phase consisting essentially of crystalline silicon nitride, said second intergranular phase consisting essentially of silicon nitride, yttrium oxide and aluminum oxide, wherein said yttrium oxide comprises from about 1 to about 25 weight percent of said two phase matrix, said two phase matrix containing less than 3 weight percent of said aluminum oxide, said densified composite ceramic cutting tool having a high density, a high abrasion resistance, a high hardness, a high fracture strength and a resistance to oxidation at temperatures greater than 1200° C., said high hardness of said densified composite ceramic cutting tool being greater than 91 on the Rockwell A scale and greater than the combined individual hardness of silicon nitride plus the fractional weight of hard refractory material times the hardness of the hard refractory material, and said high density being approximately 100 percent of theoretical density.