Process for selectively producing para-xylene

Claim 2

A process for selectively preparing para-xylene which comprises contacting toluene with a methylating agent, under methylation conditions, in the presence of a phosphorus-modified catalyst comprising a silica polymorph in combination with an inorganic refractory oxide, said catalyst having an alkali content of less than about 1.3 milliequivalents per gram as available alkali.

Claim 3

The process of claim 1 wherein the silica polymorph is a member selected from the group consisting essentially of silicalite, UCS-3, and UCS-4 and mixtures thereof.

Claim 4

The process of claim 1 wherein the inorganic refractory oxide is a member selected from the group consisting essentially of bentonite clay, boehmite alumina, silica hydrosol and colloidal silica and mixtures thereof.

Claim 5

The process of claim 1 wherein the methylating agent is a member selected from the group consisting essentially of methanol, methyl chloride, methyl bromide, dimethyl ether, and dimethyl sulfate and mixtures thereof.

Claim 6

The process of claim 1 wherein the methylating agent is methanol.

Claim 7

The process of claim 1 wherein the toluene and methylating agent are contacted in a molar ratio range of from about 6:1 to about 1:2.

Claim 8

The process of claim 1 wherein the toluene and methylating agent are contacted in a molar ratio range of from about 3:1 to about 1:1.

Claim 9

The process of claim 1 having a reaction temperature of from about 400° C. to about 600° C.; a reaction pressure of from about 5 p.s.i.a. to about 250 p.s.i.a.; a WHSV of from about 1 to about 10; and a catalyst contact time of from about 2 to about 30 minutes.

Claim 10

The process of claim 1 having a reaction temperature of from about 450° C. to about 550° C.; a reaction pressure of from 5 p.s.i.a. to about 250 p.s.i.a.; a WHSV of about 2 to about 6; and a catalyst contact time of from about 2 to about 30 minutes.

Claim 11

The process of claim 1 wherein the catalyst is modified with a phosphorus compound selected from the group consisting of phosphoric acid, phosphorus acid, trimethylphosphate, ethylphosphate and monophenylphosphate and mixtures thereof.

Claim 12

The process of claim 1 wherein the catalyst has a silica polymorph to inorganic refractory oxide weight ratio range of from about 1:10 to about 10:1; a phosphorus content of from about 2% to about 35% by weight; a bulk density of from about 0.5 gm cm -3 to about 2.5 gm cm -3 ; an average pore radius of from about 30 Å to about 200 Å; a surface area ranging from about 100 M 2 /gm to about 500 M 2 /gm; and a pore volume of from about 0.3 cc/gm to about 1.0 cc/gm.

Claim 13

The process of claim 1 wherein the catalyst has a silica polymorph to inorganic refractory oxide weight ration range of from about 1:4 to about 4:1; a phosphorus content of from about 5% to about 25%; a bulk density of from about 0.5 gm cm -3 ; an average pore radius of from about 50 Å to about 150 Å; a surface area ranging from about 150 M 2 /gm to about 350 M 2 /gm; and a pore volume of from about 0.5 cc/gm to about 0.8 cc/gm.

Claim 14

A process for selectively preparing paraxylene which comprises contacting toluene with a methylating agent in a molar ratio range of from about 6:1 to about 1:2, at a temperature of from about 400° C. to about 600° C., a pressure of from about 5 p.s.i.a. to about 250 p.s.i.a., a WHSV of from about 1 to about 10, in the presence of a phosphorus-modified catalyst comprising a silica polymorph in combination with an inorganic refractory oxide, at a catalyst contact time of from about 2 to about 30 minutes, said catalyst having an alkali content of less than about 1.3 milliequivalents per gram as available alkali.

Claim 15

A process for selectively preparing paraxylene which comprises contacting toluene with a methylating agent in a molar ratio range of from about 6:1 to about 1:2, at a temperature of from about 400° C. to about 600° C., a pressure of from about 5 p.s.i.a. to about 250 p.s.i.a., a WHSV of from about 1 to about 10, in the presence of a phosphorus-modified catalyst comprising a silica polymorph in combination with an inorganic refractory oxide, at a catalyst contact time of from about 2 to about 30 minutes, said catalyst having an alkali content of less than about 1.3 milliequivalents per gram as available alkali.

Claim 16

The process of claim 13 wherein the methylating agent is a member selected from the group consisting essentially of methanol, methyl chloride, methyl bromide, dimethyl ether, and dimethyl sulfate and mixtures thereof.

Claim 17

The process of claim 13 wherein the silica polymorph is selected from silicalite, UCS-3, and UCS-4 and mixtures thereof.

Claim 18

The process of claim 13 wherein the inorganic refractory oxide is selected from bentonite clay, boehmite alumina, silica hydrosol and colloidal silica and mixtures thereof.

Claim 19

A process for selectively preparing paraxylene which comprises contacting toluene and methanol in a molar ratio range of from about 3:1 to about 1:1, at a temperature of from about 450° C. to about 550° C., a pressure of from about 5 p.s.i.a. to about 250 p.s.i.a., a WHSV of from about 2 to about 6, in the presence of a phosphorus-modified catalyst comprising a silica polymorph selected from silicalite, UCS-3 and UCS-4 and mixtures thereof, in combination with an inorganic refractory oxide comprising boehmite alumina, said catalyst having an alkali content of less than about 1.3 milliequivalents per gram as available alkali.

Claim 20

A process for selectively preparing paraxylene which comprises contacting toluene and methanol in a molar ratio range of from about 3:1 to about 1:1, at a temperature of from about 450° C. to about 550° C., a pressure of from about 5 p.s.i.a. to about 250 p.s.i.a., a WHSV of from about 2 to about 6, in the presence of a phosphorus-modified catalyst comprising a silica polymorph selected from silicalite, UCS-3 and UCS-4 and mixtures thereof, in combination with an inorganic refractory oxide comprising boehmite alumina, said catalyst having an alkali content of less than about 1.3 milliequivalents per gram as available alkali.

Claim 21

A process for preparing paraxylene which comprises contacting under methylating conditions toluene, a methylating agent and a crystalline silica having a compound of phosphorus combined therewith as a promoter.

Claim 22

A process for preparing paraxylene which comprises contacting under methylating conditions toluene, a methylating agent and a crystalline silica having a compound of phosphorus combined therewith as a promoter.