Impact-resistant methacrylic resin composition
Assignee: Mitsubishi Chemical Corp
•
Filing: 1983-05-26
•
Granted: 1984-02-21
•
Expires: 2003-05-26
Abstract
Abstract An impact-resistant methacrylic resin composition comprising a multilayer structure methacrylic resin [II] is provided. The resin [II] is obtained by the following sequential four polymerization stages (i) through (iv): (i) forming 5-50 wt. parts of a hard crosslinked resin (A) containing at least 80 wt. % of methyl methacrylate units; (ii) obtaining 100 wt. parts of a multilayer structure acrylic elastomer [I] by forming on the periphery of resin (A) 95-50 wt. parts of a crosslinked acrylic acid ester copolymer (B) by polymerizing a monomer mixture comprising 69.9-89.9 wt. % of at least one alkyl (C1-8) acrylate, 10-30 wt. % of styrene or a mixture of styrene and a derivative thereof and 0.1-10 wt. % of <IMAGE> +TR <IMAGE> (iii) forming on the periphery of elastomer [I] 5-100 wt. parts of a hard crosslinked resin (C) by polymerizing a crosslinkable monomer mixture comprising 80-99.9 wt. % of methyl methacrylate, 0-19.9 wt. % of at least one alkyl (C1-8) acrylate, 0-10 wt. % of other copolymerizable vinyl monomer and 0.1-10 wt. % of a copolymerizable polyfunctional monomer having at least two C-C double bonds in the molecule; and then (iv) forming on the periphery of resin (C) 5-1000 wt. parts of a hard non-crosslinked resin (D) by polymerizing a non-crosslinkable monomer or non-crosslinkable monomer mixture comprising 80-100 wt. % of methyl methacrylate, 0-20 wt. % of at least one alkyl (C1-8) acrylate and 0-10 wt. % of another copolymerizable vinyl monomer, the resin (D)/resin (C) weight ratio being from 0.5 to 200. The resin [II] may be blended with a methacrylic resin [III] formed by polymerizing 80-100 wt. % of methyl methacrylate and 0-20 wt. % of a vinyl or vinylidene monomer in such a proportion that the content of the acrylic elastomer [I] is 1-70 wt. % based on the total composition.
Inventors
- 👤 Kazumasa Kamata
- 👤 Masamitsu Tateyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:55
CPC Classifications
C; C08; C08F; C08F285/00
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
359 words
An impact-resistant methacrylic resin composition comprising a multilayer structure methacrylic resin composition [II] obtained by the following sequential four polymerization stages (i) through (iv): (i) the first stage of forming 5 to 50 parts by weight of a hard crosslinked resin (A) containing at least 80% by weight of methyl methacrylate units; (ii) the second stage of obtaining 100 parts by weight of a multilayer structure acrylic elastomer [I] by forming on the periphery of said hard crosslinked resin (A) 95 to 50 parts by weight of a layer of a crosslinked acrylic acid ester copolymer (B) by polymerizing a monomer mixture comprising 69.9 to 89.9% by weight of at least one alkyl acrylate having 1 to 8 carbon atoms in the alkyl group, 10 to 30% by weight of styrene or a mixture of styrene and a derivative thereof and 0.1 to 10% by weight of at least one compound selected from the group consisting of a compound of the formula: ##STR6## and a compound of the formula: ##STR7## (iii) the third stage of forming on the periphery of said elastomer [I] 5 to 100 parts by weight of a layer of a hard crosslinked resin (C) by polymerizing a crosslinkable monomer mixture comprising 80 to 99.9% by weight of methyl methacrylate, 0 to 19.9% by weight of at least one alkyl acrylate having 1 to 8 carbon atoms in the alkyl group, 0 to 10% by weight of other copolymerizable vinyl monomer and 0.1 to 10% by weight of a copolymerizable polyfunctional monomer having at least two carbon-to-carbon double bonds in the molecule; and (iv) the fourth stage of forming on the periphery of said resin (C) 5 to 1000 parts by weight of a layer of a hard non-crosslinked resin (D) by polymerizing a non-crosslinkable monomer or non-crosslinkable monomer mixture comprising 80 to 100% by weight of methyl methacrylate, 0 to 20% by weight of at least one alkyl acrylate having 1 to 8 carbon atoms in the alkyl group and 0 to 10% by weight of other copolymerizable vinyl monomer, the resin (D)/resin (C) weight ratio being in the range of from 0.5 to 200.
Claim 2
Dependent Claim
359 words
An impact-resistant methacrylic resin composition comprising a multilayer structure methacrylic resin composition [II] obtained by the following sequential four polymerization stages (i) through (iv): (i) the first stage of forming 5 to 50 parts by weight of a hard crosslinked resin (A) containing at least 80% by weight of methyl methacrylate units; (ii) the second stage of obtaining 100 parts by weight of a multilayer structure acrylic elastomer [I] by forming on the periphery of said hard crosslinked resin (A) 95 to 50 parts by weight of a layer of a crosslinked acrylic acid ester copolymer (B) by polymerizing a monomer mixture comprising 69.9 to 89.9% by weight of at least one alkyl acrylate having 1 to 8 carbon atoms in the alkyl group, 10 to 30% by weight of styrene or a mixture of styrene and a derivative thereof and 0.1 to 10% by weight of at least one compound selected from the group consisting of a compound of the formula: ##STR6## and a compound of the formula: ##STR7## (iii) the third stage of forming on the periphery of said elastomer [I] 5 to 100 parts by weight of a layer of a hard crosslinked resin (C) by polymerizing a crosslinkable monomer mixture comprising 80 to 99.9% by weight of methyl methacrylate, 0 to 19.9% by weight of at least one alkyl acrylate having 1 to 8 carbon atoms in the alkyl group, 0 to 10% by weight of other copolymerizable vinyl monomer and 0.1 to 10% by weight of a copolymerizable polyfunctional monomer having at least two carbon-to-carbon double bonds in the molecule; and (iv) the fourth stage of forming on the periphery of said resin (C) 5 to 1000 parts by weight of a layer of a hard non-crosslinked resin (D) by polymerizing a non-crosslinkable monomer or non-crosslinkable monomer mixture comprising 80 to 100% by weight of methyl methacrylate, 0 to 20% by weight of at least one alkyl acrylate having 1 to 8 carbon atoms in the alkyl group and 0 to 10% by weight of other copolymerizable vinyl monomer, the resin (D)/resin (C) weight ratio being in the range of from 0.5 to 200.
Claim 3
Dependent Claim
104 words
An impact resistant methacrylic resin composition as set forth in claim 1, wherein the multilayer structure methacrylic resin composition [II] comprises 5 to 30 parts by weight of the hard crosslinked resin (A), 95 to 70 parts by weight of the crosslinked acrylic acid ester copolymer (B), 5 to 40 parts by weight of the hard crosslinked resin (C) and 10 to 500 parts by weight of the hard non-crosslinked resin (D), the total amount of the resin (A) and the copolymer (B) being 100 parts by weight and the resin (D)/resin (C) weight ratio being in the range of from 0.5 to 100.
Claim 4
Dependent Claim
25 words
An impact resistant methacrylic resin composition as set forth in claim 1, wherein the multilayer structure methacrylic resin composition [II] is prepared by emulsion polymerization.
Claim 5
Dependent Claim
61 words
An impact resistant methacrylic resin composition as set forth in claim 1, wherein the hard crosslinked resin (A) in the multilayer structure methacrylic resin composition [II] is prepared by polymerizing a monomer mixture comprising 99 to 93% by weight of methyl methacrylate, 0.5 to 7.0% by weight of an alkyl acrylate and 0.5 to 5% by weight of a polyfunctional monomer.
Claim 6
Dependent Claim
26 words
An impact resistant methacrylic resin composition as set forth in claim 4, wherein the polyfunctional monomer used for the hard crosslinked resin (A) is 1,3-butylene dimethacrylate.
Claim 7
Dependent Claim
81 words
An impact resistant methacrylic resin composition as set forth claim 1, wherein the crosslinked acrylic acid ester copolymer (B) in the multilayer structure methacrylic resin composition [II] is prepared by polymerizing a monomer mixture comprising 75 to 85% by weight of the alkyl acrylate, 14.9 to 24.9% by weight of styrene and 0.1 to 5% by weight of at least one compound selected from the group consisting of a compound of the formula ##STR8## and the compound of the formula ##STR9##
Claim 8
Dependent Claim
31 words
An impact resistant methacrylic resin composition as set forth in claim 1, wherein the alkyl acrylate used for the formation of the crosslinked acrylic acid ester copolymer (B) is butyl acrylate.
Claim 9
Dependent Claim
40 words
An impact resistant methacrylic resin composition as set forth in claim 1, wherein the crosslinked acrylic acid ester copolymer (B) is prepared by polymerizing a monomer mixture comprising butyl acrylate, styrene, the compound of the formula ##STR10## and 1,3-butylene dimethacrylate.
Claim 10
Dependent Claim
60 words
An impact resistant methacrylic resin composition as set forth in claim 1, wherein the hard crosslinked resin (C) in the multilayer structure resin composition [II] is prepared by polymerizing a crosslinkable monomer mixture comprising 99 to 93% by weight of methyl methacrylate, 0.5 to 7.0% by weight of the alkyl acrylate and 0.5 to 5% by weight of 1,3-butylene dimethacrylate.
Claim 11
Dependent Claim
52 words
An impact resistant methacrylic resin composition as set forth in claim 1, wherein the hard non-crosslinked resin (D) in the multilayer structure methacrylic resin composition [II] is prepared by polymerizing a monomer mixture comprising 94 to 99.5% by weight of methyl methacrylate and 6 to 0.5% by weight of the alkyl acrylate.
Claim 12
Dependent Claim
36 words
An impact resistant methacrylic resin composition as set forth in claim 1, wherein the resin (D)/resin (C) weight ratio in the multilayer structure methacrylic resin composition [II] is in the range of from 6 to 14.
Claim 13
Dependent Claim
47 words
An impact resistant methacrylic resin composition as set forth in claim 1, wherein the multilayer structure methacrylic resin composition [II] is prepared by emulsion polymerization and the particle size of the multilayer structure methacrylic resin composition [II] is in the range of from 0.2 to 0.35 μm.
Claim 14
Dependent Claim
414 words
An impact-resistant methacrylic resin composition comprising: a multilayer structure methacrylic resin composition [II] obtained by the following sequential four polymerization stages (i) through (iv): (i) the first stage of forming 5 to 50 parts by weight of a hard crosslinked resin (A) containing at least 80% by weight of methyl methacrylate units; (ii) the second stage of obtaining 100 parts by weight of a multilayer structure acrylic elastomer [I] by forming on the periphery of said hard crosslinked resin (A) 95 to 50 parts by weight of a layer of a crosslinked acrylic acid ester copolymer (B) by polymerizing a monomer mixture comprising 69.9 to 89.9% by weight of at least one alkyl acrylate having 1 to 8 carbon atoms in the alkyl group, 10 to 30% by weight of styrene or a mixture of styrene and a derivative thereof and 0.1 to 10% by weight of at least one compound selected from the group consisting of a compound of the formula: ##STR11## and a compound of the formula ##STR12## (iii) the third stage of forming on the periphery of said elastomer [I] 5 to 100 parts by weight of a layer of a hard crosslinked resin (C) by polymerizing a crosslinkable monomer mixture comprising 80 to 99.9% by weight of methyl methacrylate, 0 to 19.9% by weight of at least one alkyl acrylate having 1 to 8 carbon atoms in the alkyl group, 0 to 10% by weight of other copolymerizable vinyl monomer and 0.1 to 10% by weight of a copolymerizable polyfunctional monomer having at least two carbon-to-carbon double bonds in the molecule; and (iv) the fourth stage of forming on the periphery of said resin (C) 5 to 1000 parts by weight of a layer of a hard non-crosslinked resin (D) by polymerizing a non-crosslinkable monomer or non-crosslinkable monomer mixture comprising 80 to 100% by weight of methyl methacrylate, 0 to 20% by weight of at least one alkyl acrylate having 1 to 8 carbon atoms in the alkyl group and 0 to 10% by weight of other copolymerizable vinyl monomer, the resin (D)/resin (C) weight ratio being in the range of from 0.5 to 200; and a methacrylic resin [III] formed by polymerizing 80 to 100% by weight of methyl methacrylate and 0 to 20% by weight of a vinyl or vinylidene monomer; wherein the content of the multilayer structure acrylic elastomer [I] is 1 to 70% by weight based on the total weight of the impact-resistant methacrylic resin composition.
Claim 15
Dependent Claim
414 words
An impact-resistant methacrylic resin composition comprising: a multilayer structure methacrylic resin composition [II] obtained by the following sequential four polymerization stages (i) through (iv): (i) the first stage of forming 5 to 50 parts by weight of a hard crosslinked resin (A) containing at least 80% by weight of methyl methacrylate units; (ii) the second stage of obtaining 100 parts by weight of a multilayer structure acrylic elastomer [I] by forming on the periphery of said hard crosslinked resin (A) 95 to 50 parts by weight of a layer of a crosslinked acrylic acid ester copolymer (B) by polymerizing a monomer mixture comprising 69.9 to 89.9% by weight of at least one alkyl acrylate having 1 to 8 carbon atoms in the alkyl group, 10 to 30% by weight of styrene or a mixture of styrene and a derivative thereof and 0.1 to 10% by weight of at least one compound selected from the group consisting of a compound of the formula: ##STR11## and a compound of the formula ##STR12## (iii) the third stage of forming on the periphery of said elastomer [I] 5 to 100 parts by weight of a layer of a hard crosslinked resin (C) by polymerizing a crosslinkable monomer mixture comprising 80 to 99.9% by weight of methyl methacrylate, 0 to 19.9% by weight of at least one alkyl acrylate having 1 to 8 carbon atoms in the alkyl group, 0 to 10% by weight of other copolymerizable vinyl monomer and 0.1 to 10% by weight of a copolymerizable polyfunctional monomer having at least two carbon-to-carbon double bonds in the molecule; and (iv) the fourth stage of forming on the periphery of said resin (C) 5 to 1000 parts by weight of a layer of a hard non-crosslinked resin (D) by polymerizing a non-crosslinkable monomer or non-crosslinkable monomer mixture comprising 80 to 100% by weight of methyl methacrylate, 0 to 20% by weight of at least one alkyl acrylate having 1 to 8 carbon atoms in the alkyl group and 0 to 10% by weight of other copolymerizable vinyl monomer, the resin (D)/resin (C) weight ratio being in the range of from 0.5 to 200; and a methacrylic resin [III] formed by polymerizing 80 to 100% by weight of methyl methacrylate and 0 to 20% by weight of a vinyl or vinylidene monomer; wherein the content of the multilayer structure acrylic elastomer [I] is 1 to 70% by weight based on the total weight of the impact-resistant methacrylic resin composition.
Claim 16
Dependent Claim
104 words
An impact resistant methacrylic resin composition as set forth in claim 13, wherein the multilayer structure methacrylic resin composition [II] comprises 5 to 30 parts by weight of the hard crosslinked resin (A), 95 to 70 parts by weight of the crosslinked acrylic acid ester copolymer (B), 5 to 40 parts by weight of the hard crosslinked resin (C) and 10 to 500 parts by weight of the hard non-crosslinked resin (D), the total amount of the resin (A) and the copolymer (B) being 100 parts by weight, and the resin (D)/resin (C) weight ratio being in the range of from 0.5 to 100.
Claim 17
Dependent Claim
25 words
An impact resistant methacrylic resin composition as set forth in claim 13, wherein the multilayer structure methacrylic resin composition [II] is prepared by emulsion polymerization.
Claim 18
Dependent Claim
61 words
An impact resistant methacrylic resin composition as set forth in claim 13, wherein the hard crosslinked resin (A) in the multilayer structure methacrylic resin composition [II] is prepared by polymerizing a monomer mixture comprising 99 to 93% by weight of methyl methacrylate, 0.5 to 7.0% by weight of an alkyl acrylate and 0.5 to 5% by weight of a polyfunctional monomer.
Claim 19
Dependent Claim
26 words
An impact resistant methacrylic resin composition as set forth in claim 16, wherein the polyfunctional monomer used for the hard crosslinked resin (A) is 1,3-butylene dimethacrylate.
Claim 20
Dependent Claim
82 words
An impact resistant methacrylic resin composition as set forth in claim 13, wherein the crosslinked acrylic acid ester copolymer (B) in the multilayer structure methacrylic resin composition [II] is prepared by polymerizing a monomer mixture comprising 75 to 85% by weight of the alkyl acrylate, 14.9 to 24.9% by weight of styrene and 0.1 to 5% by weight of at least one compound selected from the group consisting of a compound of the formula ##STR13## and the compound of the formula ##STR14##
Claim 21
Dependent Claim
31 words
An impact resistant methacrylic resin composition as set forth in claim 13, wherein the alkyl acrylate used for the formation of the crosslinked acrylic acid ester copolymer (B) is butyl acrylate.
Claim 22
Dependent Claim
40 words
An impact resistant methacrylic resin composition as set forth in claim 13, wherein the crosslinked acrylic acid ester copolymer (B) is prepared by polymerizing a monomer mixture comprising butyl acrylate, styrene, the compound of the formula ##STR15## and 1,3-butylene dimethacrylate.
Claim 23
Dependent Claim
60 words
An impact resistant methacrylic resin composition as set forth in claim 13, wherein the hard crosslinked resin (C) in the multilayer structure resin composition [II] is prepared by polymerizing a crosslinkable monomer mixture comprising 99 to 93% by weight of methyl methacrylate, 0.5 to 7.0% by weight of the alkyl acrylate and 0.5 to 5% by weight of 1,3-butylene dimethacrylate.
Claim 24
Dependent Claim
52 words
An impact resistant methacrylic resin composition as set forth in claim 13, wherein the hard non-crosslinked resin (D) in the multilayer structure methacrylic resin composition [II] is prepared by polymerizing a monomer mixture comprising 94 to 99.5% by weight of methyl methacrylate and 6 to 0.5% by weight of the alkyl acrylate.
Claim 25
Dependent Claim
36 words
An impact resistant methacrylic resin composition as set forth in claim 13, wherein the resin (D)/resin (C) weight ratio in the multilayer structure methacrylic resin composition [II] is in the range of from 6 to 14.
Claim 26
Dependent Claim
47 words
An impact resistant methacrylic resin composition as set forth in claim 13, wherein the multilayer structure methacrylic resin composition [II] is prepared by emulsion polymerization and the particle size of the multilayer structure methacrylic resin composition [II] is in the range of from 0.2 to 0.35 μm.
Claim 27
Dependent Claim
43 words
An impact resistant methacrylic resin composition as set forth in claim 13, wherein the methacrylic resin [III] is obtained by polymerizing a monomer mixture comprising 85 to 99.5% by weight of methyl methacrylate and 15 to 0.5% by weight of an alkyl acrylate.
Claim 28
Dependent Claim
56 words
An impact resistant methacrylic resin composition as set forth in claim 13, wherein the multilayer structure methacrylic resin composition [II] is mixed with the methacrylic resin [III] so that the content of the multilayer structure acrylic elastomer [I] is 5 to 355 by weight based on the total weight of the impact resistant methacrylic resin composition.
Claim 29
Dependent Claim
20 words
A molded article obtained by injection molding or extrusion molding of the resin composition as set forth in claim 13.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-02-20 | 1987-08-22 | 1988-02-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-02-20 | 1991-08-22 | 1992-02-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-02-20 | 1995-08-22 | 1996-02-21 | $7700.00 | Window Closed / Lapsed |