Abstract A sintered powdered titanium alloy article is provided which has a density approaching theoretical and which is characterized by having physical properties similar to those of a wrought titanium alloy article having the same chemical composition. This unique article is produced by a novel process which comprises (a) providing milled alloy forming particles having a median particle size by weight of 20 microns or less, with the alloy forming particles being alloyable with titanium; (b) mixing the as milled alloy forming particles with titanium base particles having a median particle size by weight of greater than 40 microns so as to form a particle mixture capable of being sintered to near theoretical density which mixture contains a minor amount of alloy forming particles; (c) compacting the mixture of as milled alloy forming particles and titanium base particles into an article of the desired configuration having a green density sufficient to render the so-produced article capable of being sintered to near theoretical density; and (d) sintering the article at a temperature below that at which any liquid phase is formed in the article to produce a sintered article which has a density approaching that of theoretical.
A process for producing a sintered powdered titanium alloy article having a density near theoretical while minimizing the amount of fine particles required to obtain satisfactory densification which comprises: (a) providing alloy-forming particles which have been milled to an average particle size ranging from about 0.5 to 20.0 microns, said particles being capable of alloying with titanium; (b) mixing said alloy-forming particles in the as-milled condition with titanium-base particles having an average particle size ranging from about 40 to 177 microns so as to form a powder mixture containing about 70-95 weight percent of said titanium-base particles and the balance substantially said alloy-forming particles; (c) compacting said powder mixture into an article of the desired configuration having a green density ranging from about 80 to 90 percent of theoretical density sufficient to render said article capable of being sintered to near theoretical density; and (d) sintering said article at an elevated temperature below that at which any liquid phase is formed in said article, whereby said article has physical properties similar to a wrought produced article.
Claim 2
Dependent Claim
176 words
A process for producing a sintered powdered titanium alloy article having a density near theoretical while minimizing the amount of fine particles required to obtain satisfactory densification which comprises: (a) providing alloy-forming particles which have been milled to an average particle size ranging from about 0.5 to 20.0 microns, said particles being capable of alloying with titanium; (b) mixing said alloy-forming particles in the as-milled condition with titanium-base particles having an average particle size ranging from about 40 to 177 microns so as to form a powder mixture containing about 70-95 weight percent of said titanium-base particles and the balance substantially said alloy-forming particles; (c) compacting said powder mixture into an article of the desired configuration having a green density ranging from about 80 to 90 percent of theoretical density sufficient to render said article capable of being sintered to near theoretical density; and (d) sintering said article at an elevated temperature below that at which any liquid phase is formed in said article, whereby said article has physical properties similar to a wrought produced article.
Claim 3
Dependent Claim
12 words
The process of claim 1, wherein said alloy-forming particles are pre-alloyed particles.
Claim 4
Dependent Claim
18 words
The process of claim 2, wherein said pre-alloyed particles are comprised of an alloy of aluminum and vanadium.
Claim 5
Dependent Claim
24 words
The process of claim 3, wherein the composition of said pre-alloyed particles comprises about 60 weight percent aluminum and about 40 weight percent vanadium.
Claim 6
Dependent Claim
18 words
The process of claim 1, wherein said titanium-base particles contain in excess of about 99 weight percent titanium.
Claim 7
Dependent Claim
40 words
The process of claim 1, wherein the alloy-forming particles are provided with said average particle size of about 0.5 to 20 microns by milling a charge of said alloy-forming particles in an attritor mill containing grinding balls and a liquid.
Claim 8
Dependent Claim
10 words
The process of claim 6, wherein said liquid is Freon.