Process for producing a sintered article of a titanium alloy
Assignee: Mitsubishi Metal Corp
•
Filing: 1974-01-30
•
Granted: 1976-04-13
•
Expires: 1994-01-30
Abstract
Abstract A sintered article of a titanium alloy is produced by powder metallurgy techniques, the alloy having uniform structure, and improved mechanical properties, machinability and weldability. The process comprises; partially sintering a powder mixture of (a) at least one selected from the group consisting of powdered titanium and titanium hydride having a particle size of minus 60 mesh and (b) at least one powdered additive selected from the group consisting of powdered Ni, Al, Cu, Sn, Pd, Co, Fe, Cr, Mn, and Si having a particle size of minus 60 mesh, to partially alloy the titanium with one or more additives employed; after furnace cooling the partially sintered mass to room temperature, pulverizing it to powder of minus 60 mesh in particle size to prepare mother alloy powder; mixing (a) the mother alloy powder having a particle size of minus 60 mesh, (b) at least one selected from the group consisting of powdered titanium and titanium hydride having a particle size of minus 60 mesh, and (c), if necessary, at least one additional element selected from the group consisting of powdered V, Mo, Zr and Al-V alloy, which are added for the purpose of avoiding excess formation of a liquid phase during the subsequent sintering; compacting the thus formed powder mixture into a compact having a predetermined shape; and sintering the compact at a temperature ranging from 1000°C to 1500°C in a non-oxidizing and non-nitriding atmosphere for from 30 minutes to 2 hours.
Inventors
- 👤 Kunio Obara
- 👤 Yoshio Nishino
- 👤 Shoji Matsumoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 00:06
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/04; C22C1/045; C22C1/0458; B; B22; B22F; B22F2998/00
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
181 words
A process for producing an article of a titanium alloy by powder metallurgy techniques, comprising a first sintering stage in combination with a second sintering stage, in which said first sintering stage comprises the steps of: mixing at least one material selected from the group consisting of powdered titanium and titanium hydride and at least one powdered additive to provide a first powder mixture, sintering the first powder mixture at a temperature not more than 400° C. higher than the melting point of the additive and the eutectic point of the additive with titanium to partially alloy the titanium with the additive, and reducing in size the partically sintered mass to prepare a mother alloy powder; and said second sintering stage comprises the steps of: mixing said mother alloy powder with at least one material selected from the group consisting of powdered titanium and titanium hydride to provide a second powder mixture having a predetermined composition, compacting the second powder mixture to form a compact having a predetermined shape, and sintering the compact to provide the article of a titanium alloy.
Claim 2
Dependent Claim
181 words
A process for producing an article of a titanium alloy by powder metallurgy techniques, comprising a first sintering stage in combination with a second sintering stage, in which said first sintering stage comprises the steps of: mixing at least one material selected from the group consisting of powdered titanium and titanium hydride and at least one powdered additive to provide a first powder mixture, sintering the first powder mixture at a temperature not more than 400° C. higher than the melting point of the additive and the eutectic point of the additive with titanium to partially alloy the titanium with the additive, and reducing in size the partically sintered mass to prepare a mother alloy powder; and said second sintering stage comprises the steps of: mixing said mother alloy powder with at least one material selected from the group consisting of powdered titanium and titanium hydride to provide a second powder mixture having a predetermined composition, compacting the second powder mixture to form a compact having a predetermined shape, and sintering the compact to provide the article of a titanium alloy.
Claim 3
Dependent Claim
25 words
A process according to claim 1, in which the purity of the titanium used is in the range of from 99.0 percent to 99.9 percent.
Claim 4
Dependent Claim
161 words
A process according to claim 1, in which said first powder mixture for the first sintering stage comprises 20-90 percent by weight of at least one material selected from the group consisting of powdered titanium and titanium hydride having a particle size of at least minus 60 mesh, and 10-80% by weight of at least one powdered additive selected from the group consisting of powdered Ni, Al, Cu, Pd, Fe, Co, Cr, Mn and Si having a particle size of at least minus 60 mesh, said second powder mixture for the second sintering stage comprises said mother alloy powder having a particle size of at least minus 60 mesh and at least one material selected from the group consisting of powdered titanium and titanium hydride having a particle size of at least minus 60 mesh in an amount to make the additive content in the range of from 0.2 to 40 percent by weight of the total weight of the compact.
Claim 5
Dependent Claim
27 words
A process according to claim 3, in which the particle size of the powdery charge for each of the sintering stages is at least minus 100 mesh.
Claim 6
Dependent Claim
74 words
A process according to claim 3, in which the sintering of the first stage is carried out under conditions including a non-oxidizing and non-nitriding atmosphere, and a sintering period of from 10 minutes to 2 hours, and the sintering of the second stage is carried out under conditions including a non-oxidizing and non-nitriding atmosphere, a temperature ranging from 1000° C to 1500° C and a sintering time ranging from 30 minutes to 2 hours.
Claim 7
Dependent Claim
24 words
A process according to claim 3, in which the atmosphere for both sintering stages is a vacuum not more than 10 - 4 Torr.
Claim 8
Dependent Claim
28 words
A process according to claim 3, in which the atmosphere for both sintering stages is an Ar atmosphere having a dew point of not more than -50° C.
Claim 9
Dependent Claim
29 words
A process according to claim 3, in which the compacting pressure used for the second sintering stage is in the range of from 4 to 8 T/cm 2 .
Claim 10
Dependent Claim
247 words
A process for producing an article of a titanium alloy by powder metallurgy techniques comprising a first sintering stage in combination with a second sintering stage, in which said first sintering stage comprises the steps of: mixing 20-90 percent by weight of at least one material selected from the group consisting of powdered titanium and titanium hydride and 10-80 percent by weight of at least one powdered additive selected from the group consisting of powdered Ni, Al, Cu, Sn, Pd, Fe, Co, Cr, Mn and Si to provide a first powder mixture, sintering the first powder mixture at a temperature no more than 400° C. higher than the melting point of the additive and the eutectic point of the additive with titanium to partially alloy the titanium with the additive, and reducing in size the partially sintered mass to prepare a mother alloy powder; and said second sintering stage comprises the steps of: mixing said mother alloy powder with at least one material selected from the group consisting of powdered titanium and titanium hydride, and at least one material selected from the group consisting of powdered V, Mo, Zr and Al-V alloy to provide a second powder mixture, the additive content of which is in the range of from 0.2 to 40 percent by weight of the total weight of the mixture, compacting the second powder mixture to form a compact having a predetermined shape, and sintering the compact to provide the article of a titanium alloy.
Claim 11
Dependent Claim
247 words
A process for producing an article of a titanium alloy by powder metallurgy techniques comprising a first sintering stage in combination with a second sintering stage, in which said first sintering stage comprises the steps of: mixing 20-90 percent by weight of at least one material selected from the group consisting of powdered titanium and titanium hydride and 10-80 percent by weight of at least one powdered additive selected from the group consisting of powdered Ni, Al, Cu, Sn, Pd, Fe, Co, Cr, Mn and Si to provide a first powder mixture, sintering the first powder mixture at a temperature no more than 400° C. higher than the melting point of the additive and the eutectic point of the additive with titanium to partially alloy the titanium with the additive, and reducing in size the partially sintered mass to prepare a mother alloy powder; and said second sintering stage comprises the steps of: mixing said mother alloy powder with at least one material selected from the group consisting of powdered titanium and titanium hydride, and at least one material selected from the group consisting of powdered V, Mo, Zr and Al-V alloy to provide a second powder mixture, the additive content of which is in the range of from 0.2 to 40 percent by weight of the total weight of the mixture, compacting the second powder mixture to form a compact having a predetermined shape, and sintering the compact to provide the article of a titanium alloy.
Claim 12
Dependent Claim
25 words
A process according to claim 9, in which the purity of the titanium used is in the range of from 99.0 percent to 99.9 percent.
Claim 13
Dependent Claim
25 words
A process according to claim 9, the particle size of the powdery charge for each of the sintering stages is at least minus 100 mesh.
Claim 14
Dependent Claim
76 words
A process according to claim 9, in which the sintering of said first sintering stage is carried out under conditions including a non-oxidizing and non-nitriding atmosphere, and a sintering time of from 10 minutes to 2 hours, and the sintering of said second sintering stage is carried out under conditions including a non-oxidizing and non-nitriding atmosphere, a temperature ranging from 1000° C to 1500° C and a sintering period ranging from 30 minutes to 2 hours.
Claim 15
Dependent Claim
25 words
A process according to claim 9, in which the atmosphere for both sintering stages is a vacuum of not more than 10 - 4 Torr.
Claim 16
Dependent Claim
28 words
A process according to claim 9, in which the atmosphere for both sintering stages is an Ar atmosphere having a dew point of not more than -50° C.
Claim 17
Dependent Claim
27 words
A process according to claim 3, in which the particle size of the powdery charge for each of the sintering stages is at least minus 200 mesh.
Claim 18
Dependent Claim
27 words
A process according to claim 9, in which the particle size of the powdery charge for each of the sintering stages is at least minus 200 mesh.
References Cited (Backward Citations)
US2163224A
Cited
US2246387A
Cited
GB887922A
Cited
US3084042A
Cited
US3175903A
Cited
US3496036A
Cited
US3847603A
Cited
US3859087A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-13 | 1979-10-13 | 1980-04-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-13 | 1983-10-13 | 1984-04-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-13 | 1987-10-13 | 1988-04-13 | $7700.00 | Window Closed / Lapsed |