Casting tube
Assignee: Daussan SAS
•
Filing: 1982-05-17
•
Granted: 1984-02-21
•
Expires: 2002-05-17
Abstract
Abstract The casting tube is constituted by a mixture of refractory particles and fibers embedded in a binder which is not capable of withstanding the temperature attained when liquid metal flows within the tube. The refractory particles are sinterable in a tube zone which is directly exposed to the heat of the liquid metal. At least in a zone which is not directly exposed to the heat of the liquid metal, the casting tube also contains a refractory binder which is capable of withstanding the heat in this zone.
Inventors
- 👤 Jean-Charles Daussan
- 👤 Gerard Daussan
- 👤 Andre Daussan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 08:34
CPC Classifications
B; B22; B22D; B22D41/00; B22D41/50; B22D41/52; B22D41/54
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
148 words
A casting tube to be engaged tightly around the casting nozzle of a first metallurgical vessel and to be immersed in the molten metal which is being poured into a second vessel placed beneath the first vessel, said casting tube being constituted by a mixture of refractory particles and fibers embedded in a binder which is not capable of withstanding the temperature to which the casting tube is heated when liquid metal flows within the interior of said tube whereas the refractory particles are sinterable in a tube zone which is directly exposed to the heat of the liquid metal, wherein said casting tube also contains a refractory binder which is resistant to the heat of the liquid metal and is provided at least in the end zone of said tube which is to be engaged around said casting nozzle, which is not directly exposed to said heat.
Claim 2
Dependent Claim
148 words
A casting tube to be engaged tightly around the casting nozzle of a first metallurgical vessel and to be immersed in the molten metal which is being poured into a second vessel placed beneath the first vessel, said casting tube being constituted by a mixture of refractory particles and fibers embedded in a binder which is not capable of withstanding the temperature to which the casting tube is heated when liquid metal flows within the interior of said tube whereas the refractory particles are sinterable in a tube zone which is directly exposed to the heat of the liquid metal, wherein said casting tube also contains a refractory binder which is resistant to the heat of the liquid metal and is provided at least in the end zone of said tube which is to be engaged around said casting nozzle, which is not directly exposed to said heat.
Claim 3
Dependent Claim
34 words
A casting tube according to claim 1, wherein the refractory binder is also present in the end zone of the tube which is to be immersed in the metal contained in the second vessel.
Claim 4
Dependent Claim
28 words
A casting tube according to claim 1, wherein the refractory binder is selected from the following compounds: aluminum phosphate, boric acid, ethyl silicate, silica sols and alkali silicates.
Claim 5
Dependent Claim
18 words
A casting tube according to claim 3, said refractory particles being acid, wherein the binder is aluminum monophosphate.
Claim 6
Dependent Claim
26 words
A casting tube according to claim 3, said refractory particles being basic, wherein the phosphate binder employed is aluminum monophosphate neutralized by an alkali metal oxide.
Claim 7
Dependent Claim
32 words
A casting tube according to claim 1, wherein the weight concentration of said refractory binder within said zone is within the range of approximately 0.2 to 13% by weight of dry substance.
Claim 8
Dependent Claim
55 words
A casting tube according to claim 1, having an end zone at each end thereof, said end zones being spaced apart by an intermediate zone, said refractory binder being provided only in at least that one of said end zone into which said nozzle is inserted, said intermediate zone being free from said refractory binder.
References Cited (Backward Citations)
US2892227A
Cited
US3529753A
Cited
US3793042A
Cited
US4165026A
Cited
DE2451935A1
Cited
FR2333599A1
Cited
SU607638A1
Cited
JPS53143614A
Cited
US4298554A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-02-20 | 1987-08-22 | 1988-02-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-02-20 | 1991-08-22 | 1992-02-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-02-20 | 1995-08-22 | 1996-02-21 | $7700.00 | Window Closed / Lapsed |