Assignee: Dow Silicones Corp
•
Filing: 1983-03-14
•
Granted: 1984-02-14
•
Expires: 2003-03-14
Abstract
Abstract A method of producing a silicone polymer-filler mixture in powder form has been developed. The method combines an oligomer consisting of a polydiorganosiloxane, sufficient acidic or neutral reinforcing filler to yield a powder, and a catalytic amount of a catalyst consisting of (a) sulfuric acid or a sulfonic acid of the formula XSO 3 H wherein X is selected from the group consisting of halogen, alkyl, aryl, alkoxy and alkaryl radicals, (b) perfluorinated alkane sulfonic acid, and (c) a combination of quaternary ammonium carboxylate and carboxylic acid, to give a powdery mixture. The powdery mixture is polymerized, then the catalyst is inactivated while maintaining a powdery state. The method requires a minimum of energy for mixing.
Inventors
- 👤 James R. Falender
- 👤 John C. Saam
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 19:26
CPC Classifications
C; C08; C08L; C08L83/00; C08L83/04; C08L83/06; C08G; C08G85/00; C08G77/00; C08G77/04; C08G77/06; C08G77/08; C08K; C08K3/00; C08K3/01; C08K3/013
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
180 words
A method of producing a silicone polymer-filler mixture in powdered form comprising (A) combining (i) 100 parts by weight of a polydiorganosiloxane oligomer of the formula HO(R.sub.2 SiO).sub.x H wherein each R is a radical selected from the group consisting of methyl, ethyl, propyl, phenyl, vinyl, allyl, and 3,3,3-trifluoropropyl and x is from 3 to 100 inclusive; (ii) sufficient reinforcing filler, said filler being acidic or neutral, to yield a powder when (i) and (ii) are mixed together ; and (iii) a catalytic amount of a catalyst selected from the group consisting of (a) sulfuric acid or a sulfonic acid of the formula XSO 3 H, wherein X is selected from the group consisting of halogen, alkyl, aryl, alkoxy, and alkaryl radicals, (b) perfluorinated alkane sulfonic acid, and (c) a combination of quaternary ammonium carboxylate and carboxylic acid, to yield a powdery mixture, (B) polymerizing the oligomer while maintaining the mixture in a powdery state, and (C) inactivating the catalyst to yield a storage stable silicone polymer-filler mixture in the powdery state in which (i) has increased in molecular weight.
Claim 2
Independent Claim
180 words
A method of producing a silicone polymer-filler mixture in powdered form comprising (A) combining (i) 100 parts by weight of a polydiorganosiloxane oligomer of the formula HO(R.sub.2 SiO).sub.x H wherein each R is a radical selected from the group consisting of methyl, ethyl, propyl, phenyl, vinyl, allyl, and 3,3,3-trifluoropropyl and x is from 3 to 100 inclusive; (ii) sufficient reinforcing filler, said filler being acidic or neutral, to yield a powder when (i) and (ii) are mixed together ; and (iii) a catalytic amount of a catalyst selected from the group consisting of (a) sulfuric acid or a sulfonic acid of the formula XSO 3 H, wherein X is selected from the group consisting of halogen, alkyl, aryl, alkoxy, and alkaryl radicals, (b) perfluorinated alkane sulfonic acid, and (c) a combination of quaternary ammonium carboxylate and carboxylic acid, to yield a powdery mixture, (B) polymerizing the oligomer while maintaining the mixture in a powdery state, and (C) inactivating the catalyst to yield a storage stable silicone polymer-filler mixture in the powdery state in which (i) has increased in molecular weight.
Claim 3
Dependent Claim
16 words
The method of claim 1 in which (B) is carried out in a fluidized bed reactor.
Claim 4
Dependent Claim
16 words
The method of claim 1 in which (B) is carried out in a stirred powder reactor.
Claim 5
Dependent Claim
15 words
The method of claim 1 in which (B) is carried out in a tumbling reactor.
Claim 6
Dependent Claim
54 words
The method of claim 2 in which the catalyst in (iii) is selected from a sulfonic acid of the formula XSO 3 H, wherein X is selected from the group consisting of halogen, alkyl, aryl, alkoxy, and alkaryl radicals and in which step (C) comprises mixing the powder of (B) with a Lewis base.
Claim 7
Dependent Claim
80 words
The method of claim 5 in which the reinforcing filler in (ii) is colloidal silica present in an amount of from 35 to 100 parts by weight, the sulfonic acid in (iii) is a monoalkyl substituted benzene sulfonic acid of the formula R 2 C 6 H 4 SO 3 H, wherein R 2 is a monovalent hydrocarbon radical of at least 6 carbon atoms, and the Lewis base is selected from the group consisting of diethylamine and magnesium oxide.
Claim 8
Dependent Claim
62 words
The method of claim 6 in which step (B) comprises heating the mixture to a temperature of from 100° to 170° C. while removing water from the system, then cooling to a temperature of from 30° C. to 35° C. and holding at temperature for a period of greater than of 15 minutes until the desired increase in molecular weight is reached.
Claim 9
Dependent Claim
24 words
The method of claim 7 in which the Lewis base is magnesium oxide in an amount of from 0.4 to 5.0 parts by weight.
Claim 10
Dependent Claim
50 words
The method of claim 2 in which the catalyst in (iii) is a perfluorinated alkane sulfonic acid present in an amount of at least 400 parts by weight per million parts by weight of (i) and in which step (C) comprises mixing the powder of (B) with a Lewis base.
Claim 11
Dependent Claim
61 words
The method of claim 9 in which the reinforcing filler in (ii) is colloidal silica present in an amount of from 35 to 100 parts by weight, the perfluorinated alkane sulfonic acid in (iii) is of the formula C n F 2n+1 SO 3 H wherein n is from 1 to 30 inclusive, and the Lewis base is calcined magnesium oxide.
Claim 12
Dependent Claim
72 words
The method of claim 10 in which the perfluorinated alkane sulfonic acid is trifluoromethane sulfonic acid, and in which step (B) comprises heating the mixture of step (A) to a temperature of from about 70° C. to 150° C. to initiate polymerization and remove water, then adjusting the temperature to from 20° C. to 100° C. while removing water and maintaining at temperature until the desired degree of polymerization has been reached.
Claim 13
Dependent Claim
186 words
The method of claim 2 in which the catalyst in (iii) is a mixture of from 0.05 to 5.0 parts by weight of quaternary ammonium carboxylate of the formula ##STR2## where each R' is selected from the group consisting of monovalent aliphatic radicals having from 1 to 20 carbon atoms and aralkyl radicals and each R 3 is selected from the group consisting of monovalent aliphatic hydrocarbon radicals of 5 or less carbon atoms, phenyl radical, and benzyl radical, at least one R' having 4 or greater carbon atoms, the quaternary ammonium carboxylate being soluble in (i) and from 0.05 to 50 parts by weight of carboxylic acid of the formula R.sup.3 COOH where R 3 is selected from the group consisting of monovalent aliphatic hydrocarbon radicals of 5 or less carbon atoms, phenyl radical, and benzyl radical; step (B) comprises heating to a temperature of from 90° C. to 150° C. and removing water until the desired degree of condensation is reached; and step (C) comprises heating to a temperature sufficient to cause the polymerization to cease, removing volatile products, then cooling to room temperature.
Claim 14
Dependent Claim
67 words
The method of claim 12 in which the reinforcing filler in (ii) is colloidal silica present in an amount of from 35 to 100 parts by weight; the quaternary ammonium carboxylate is lauryltrimethyl ammonium acetate and the carboxylic acid is acetic acid; the temperature in step (B) is from 110° C. to 130° C., and the temperature of step (C) is from 150° C. to 200° C.
Claim 15
Dependent Claim
10 words
The polymer-filler mixture produced by the method of claim 1.
Claim 16
Dependent Claim
10 words
The polymer-filler mixture produced by the method of claim 6.
Claim 17
Dependent Claim
10 words
The polymer-filler mixture produced by the method of claim 11.
Claim 18
Dependent Claim
10 words
The polymer-filler mixture produced by the method of claim 13.
Claim 19
Dependent Claim
22 words
The method of claim 1 in which the silicone polymer-filler mixture is further mixed with curing agent to yield a curable composition.
Claim 20
Dependent Claim
22 words
The method of claim 6 in which the silicone polymer-filler mixture is further mixed with curing agent to yield a curable composition.
Claim 21
Dependent Claim
22 words
The method of claim 11 in which the silicone polymer-filler mixture is further mixed with curing agent to yield a curable composition.
Claim 22
Dependent Claim
22 words
The method of claim 13 in which the silicone polymer-filler mixture is further mixed with curing agent to yield a curable composition.
Claim 23
Dependent Claim
15 words
The elastomeric product obtained by curing the composition produced by the method of claim 18.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-02-13 | 1987-08-15 | 1988-02-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-02-13 | 1991-08-15 | 1992-02-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-02-13 | 1995-08-15 | 1996-02-14 | $7700.00 | Window Closed / Lapsed |