Polyorganosiloxanes containing homogeneously distributed fillers
Assignee: Bayer AG
•
Filing: 1976-07-30
•
Granted: 1978-07-18
•
Expires: 1996-07-30
Abstract
Abstract A viscosity-stable composition comprising by weight A. about 20 to 100 parts of a linear polyorganosiloxane of the formula ##STR1## in which R is an optionally substituted hydrocarbon radical with up to 10 C atoms, R 1 has any of the definitions of R and in addition can be an OH radical, and n is a positive integer, B. about 5 to 50 parts of a highly disperse active filler with a surface area of at least 50 m 2 /g, C. about 1 to 5 parts of a modifying agent of the formula (R.sub.3 Si).sub.n X in which R is as defined above, X is halogen, OH, OR, S, OOCR, N or NY, Y is hydrogen or any of the definitions of R, and n is 1, 2 or 3, and D. about 0.1 to 10 parts of water (based on (a) + (b) + (c)), Is produced by treating the filler with the modifying agent, in the presence of water, during its incorporation into the polyorganosiloxane. The preferred filler is silica but may also comprise TiO 2 , Al 2 O 3 , Fe 2 O 3 and/or ZnO. Other additives may also be included.
Inventors
- 👤 Joachim Herzig
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 06:22
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/20; C08J3/201; C08K; C08K9/00; C08K9/04; C08K9/06; C08J2383/00; C08J2383/04
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
92 words
A process for the preparation of a storage-stable homogeneously filled polyorganosiloxane comprising forming a mixture of polyorganosiloxane, water and a modifying agent of the formula (R.sub.3 Si).sub.n X in which R is an optionally substituted hydrocarbon radical with up to 10 C atoms, X is a halogen, OH, OR, N, S, OOCR or NY, Y is hydrogen or any of the definitions of R, and n is 1, 2 or 3, adding thereto silica having a specific surface area of at least 50m 2/ g, and subsequently cold curing the filled polyorganosiloxane.
Claim 2
Dependent Claim
92 words
A process for the preparation of a storage-stable homogeneously filled polyorganosiloxane comprising forming a mixture of polyorganosiloxane, water and a modifying agent of the formula (R.sub.3 Si).sub.n X in which R is an optionally substituted hydrocarbon radical with up to 10 C atoms, X is a halogen, OH, OR, N, S, OOCR or NY, Y is hydrogen or any of the definitions of R, and n is 1, 2 or 3, adding thereto silica having a specific surface area of at least 50m 2/ g, and subsequently cold curing the filled polyorganosiloxane.
Claim 3
Dependent Claim
12 words
The process according to claim 1, wherein the modifying agent comprises hexamethyldisilazane.
Claim 4
Dependent Claim
19 words
The process according to claim 1, wherein the mixture of silica and modifying agent is subjected to mechanical stress.
Claim 5
Dependent Claim
27 words
The process according to claim 1, wherein about 0.1 to 10 parts by weight of water are added per 20 to 100 parts by weight of polyorganosiloxane.
Claim 6
Dependent Claim
41 words
The process according to claim 1, wherein the silica has a surface area of at least about 100 m 2 /g and is added in about 5 to 50 parts by weight per 20 to 100 parts by weight of polyorganosiloxane.
Claim 7
Dependent Claim
35 words
The process according to claim 1, wherein R is alkyl of up to 6 carbon atoms, phenyl, diphenyl, tolyl, xylyl, ethylphenyl, benzyl, phenylethyl, vinyl, allyl, cycloalkyl or cycloalkenyl, or a halogen or cyano-substitution product thereof.
Claim 8
Dependent Claim
77 words
The process according to claim 6, wherein the silica is added in about 10 to 100 parts by weight per 50 to 200 parts by weight of polyorganosiloxane, the modifying agent is added in about 1 to 50 parts by weight, about 2 to 6 parts of water are added, about 5 to 100 parts by weight of an additional filler, plasticizer, solvent, flame-proofing agent or pigment are added, and the mixture is subjected to mechanical stress.
Claim 9
Dependent Claim
141 words
A viscosity-stable composition comprising by weight a. about 20 to 100 parts of a linear polyorganosiloxane of the formula ##STR3## in which R is an optionally substituted hydrocarbon radical with up to 10 C atoms, R 1 has any of the definitions of R and in addition can be an OH radical, and n is a positive integer, b. about 5 to 50 parts of silica with a surface area of at least 50 m 2 /g, c. about 1 to 5 parts of a modifying agent of the formula (R.sub.3 Si).sub.n X in which R is as defined above, X is halogen, OH, OR, S, OOCR, N or NY, Y is hydrogen or any of the definitions of R, and n is 1, 2 or 3, and d. about 0.1 to 10 parts of water (based on (a) + (b).
Claim 10
Dependent Claim
141 words
A viscosity-stable composition comprising by weight a. about 20 to 100 parts of a linear polyorganosiloxane of the formula ##STR3## in which R is an optionally substituted hydrocarbon radical with up to 10 C atoms, R 1 has any of the definitions of R and in addition can be an OH radical, and n is a positive integer, b. about 5 to 50 parts of silica with a surface area of at least 50 m 2 /g, c. about 1 to 5 parts of a modifying agent of the formula (R.sub.3 Si).sub.n X in which R is as defined above, X is halogen, OH, OR, S, OOCR, N or NY, Y is hydrogen or any of the definitions of R, and n is 1, 2 or 3, and d. about 0.1 to 10 parts of water (based on (a) + (b).
Claim 11
Dependent Claim
86 words
A composition according to claim 8, comprising by weight a. about 50 to 100 parts of the polyorganosiloxane wherein R is alkyl of up to 6 carbon atoms, phenyl, diphenyl, tolyl, xylyl, ethylphenyl, benzyl, phenylethyl, vinyl, allyl, cycloalkyl or cycloalkenyl, or a halogen or cyano-substitution product thereof. b. about 10 to 50 parts of silica having a surface area of at least about 100 m 2 /g, c. about 3 to 5 parts of the modifying agent, and d. about 2 to 6 parts of water.
Claim 12
Dependent Claim
25 words
A composition according to claim 9, further including about 5 to 100 parts by weight of an additional filler, plasticizer, solvent, flameproofing agent or pigment.
Claim 13
Dependent Claim
9 words
The product produced by the process of claim 7.
References Cited (Backward Citations)
US3243404A
Cited
US3624023A
Cited
US3642685A
Cited
US3734882A
Cited
US3817910A
Cited
US3929718A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-17 | 1982-01-16 | 1982-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-17 | 1986-01-16 | 1986-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-17 | 1990-01-16 | 1990-07-18 | $7700.00 | Window Closed / Lapsed |