US4431623A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the production of carbon fibres from petroleum pitch
Assignee: BP PLC
•
Filing: 1982-06-04
•
Granted: 1984-02-14
•
Expires: 2002-06-04
Abstract
Abstract A method of producing carbon or graphite fibres from a pitch obtained from a steam cracking residue of a petroleum fraction which pitch has a β resin content of from 2 to 40% by weight, comprises spinning the pitch into fibres at a temperature higher than the softening point, the fibres being treated to render them infusible and then subjecting the fibres to carbonization by heating, followed by graphitization if desired, characterized in that the treatment to infusibilize the fibres is controlled such that the resin content of the fibres does not exceed 30% by weight. The invention includes carbon and graphite fibres produced by the process.
Inventors
- 👤 Gerrard Fug
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 11:58
CPC Classifications
D; D01; D01F; D01F9/00; D01F9/08; D01F9/12; D01F9/14; D01F9/145
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
154 words
A method of producing carbon from a pitch obtained from a steam cracking residue of a petroleum fraction, which pitch has a β resin content of from 2 to 40% by weight, comprising spinning the pitch into fibres at a temperature higher than the softening point, treating the fibres to render them infusible and then subjecting the fibres to carbonisation by heating, characterised in that the treatment to infusibilize the fibres is controlled such that the α resin content of the fibres does not exceed 30% by weight and said infusibilizing treatment comprising (a) treatment with a mixture of NO and O 2 at a temperature not exceeding 200° C., or (b) treatment with a halogen in gaseous form followed by a treatment with O 2 at a temperature not exceeding 250° C., or (c) treatment with SO 2 , alone or mixed with O 2 , at a temperature not exceeding 300° C.
Claim 2
Independent Claim
154 words
A method of producing carbon from a pitch obtained from a steam cracking residue of a petroleum fraction, which pitch has a β resin content of from 2 to 40% by weight, comprising spinning the pitch into fibres at a temperature higher than the softening point, treating the fibres to render them infusible and then subjecting the fibres to carbonisation by heating, characterised in that the treatment to infusibilize the fibres is controlled such that the α resin content of the fibres does not exceed 30% by weight and said infusibilizing treatment comprising (a) treatment with a mixture of NO and O 2 at a temperature not exceeding 200° C., or (b) treatment with a halogen in gaseous form followed by a treatment with O 2 at a temperature not exceeding 250° C., or (c) treatment with SO 2 , alone or mixed with O 2 , at a temperature not exceeding 300° C.
Claim 3
Dependent Claim
28 words
A method claimed in claim 1 characterised in that the infusibilisation treatment is such that the α resin content of the fibres does not exceed 25% by weight.
Claim 4
Dependent Claim
41 words
A method as claimed in claim 1 characterised in that the infusibilised pitch fibres are carbonised under a tension of from 2 to 100 mg/denier by heating up to 1000° C. at a rate of temperature increase greater than 300° C./hour.
Claim 5
Dependent Claim
21 words
A method as in claim 1, 2 or 3 in which the carbon fibres are subsequently subjected to a graphitising step.
Claim 6
Dependent Claim
27 words
A method as claimed in claim 4 characterised in that the carbon fibres are graphitised by heating under tension at a temperature of at least 2500° C.
References Cited (Backward Citations)
US3595946A
Cited
GB1307392A
Cited
US3656904A
Cited
JPS51105418A
Cited
US4197283A
Cited
US4351816A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-02-13 | 1987-08-15 | 1988-02-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-02-13 | 1991-08-15 | 1992-02-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-02-13 | 1995-08-15 | 1996-02-14 | $7700.00 | Window Closed / Lapsed |