Multiple-stage hydroprocessing of hydrocarbon oil

Claim 2

A process for the catalytic hydroprocessing of a hydrocarbon oil comprising successively contacting said oil in the presence of hydrogen under hydroprocessing conditions with a first hydroprocessing catalyst in a first reaction zone and, subsequently, a second hydroprocessing catalyst in a second reaction zone, said first catalyst and said second catalyst comprising one or more hydrogenation metal components on a porous refractory oxide support material with essentially all the pores having diameters greater than about 100 angstroms, and with less than 10 percent of the total pore volume being in pores of diameter greater than 300 angstroms, and with at least about 35 percent of the total pore volume being in pores of diameter about 150 to about 200 angstroms, said first hydroprocessing catalyst having an average pore diameter at least about 30 angstroms larger than the average pore diameter of said second hydroprocessing catalyst.

Claim 3

The process as defined in claim 1 wherein the volume ratio of said first hydroprocessing catalyst to said second hydroprocessing catalyst is between about 1:10 and 10:1.

Claim 4

The process as defined in claim 1 wherein said catalysts have a total pore volume less than about 1.2 cc/gram.

Claim 5

The process as defined in claim 1 wherein said first hydroprocessing catalyst has an average pore diameter greater than about 180 angstroms.

Claim 6

The process as defined in claim 1 wherein said second hydroprocessing catalyst has an average pore diameter less than about 180 angstroms.

Claim 7

The process as defined in claim 1 wherein said first hydroprocessing catalyst has at least 80 percent of the total pore volume in pores of diameter from about 150 angstroms to about 300 angstroms and a surface area less than about 200 m 2 /gram.

Claim 8

The process as defined in claim 1 wherein said second hydroprocessing catalyst has at least about 80 percent of the total pore volume in pores of diameter from about 100 angstroms to about 200 angstroms and a surface area less than about 300 m 2 /gram.

Claim 9

The process as defined in claim 1 wherein said refractory oxide support material consists essentially of gamma alumina.

Claim 10

The process as defined in claim 1 wherein said hydrogenation metal components are selected from the group consisting of Group VIB and Group VIII metals.

Claim 11

The process as defined in claim 1 wherein said second hydroprocessing catalyst has a total pore volume less than about 0.65 cc/gram.

Claim 12

The process as defined in claim 4 wherein said first hydroprocessing catalyst has an average pore diameter about 180 angstroms to about 220 angstroms.

Claim 13

The process as defined in claim 5 wherein said second hydroprocessing catalyst has an average pore diameter about 140 angstroms to about 180 angstroms.

Claim 14

The process as defined in claim 1 wherein said catalytic hydroprocessing includes demetallization and desulfurization.

Claim 15

The process as defined in claim 1 wherein said first and second hydroprocessing catalysts both have at least about 40 percent of their pore volumes in pores with diameters about 150 angstroms to about 200 angstroms.

Claim 16

A process for the hydrodesulfurization of a hydrocarbon oil containing a substantial proportion of contaminant metals, said process comprising the steps of: (1) contacting said oil in the presence of hydrogen under reaction conditions with a hydrodemetallization catalyst comprising an alumina support and one or more hydrogenation components selected from the group consisting of Group VIB metal components and Group VIII metal components, said catalyst with essentially all the pores having diameters greater than about 100 angstroms, at least about 80 percent of the total pore volume being in pores of diameter about 150 angstroms to about 300 angstroms, with at least about 35 percent of the total pore volume being in pores of diameter from about 150 to about 200 angstroms, less than about 10 percent of the total pore volume being in pores of diameter greater than 300 angstroms, and a surface area about 75 m 2 /gram to about 200 m 2 /gram, so as to produce a first hydrocarbon product having a lower contaminant metals content than said oil; and (2) contacting at least a portion of the hydrocarbon product from said step (1) in the presence of hydrogen under reaction conditions with a hydrodesulfurization catalyst comprising an alumina support and one or more hydrogenation components selected from the group consisting of Group VIB metal components and Group VIII metal components, said hydrodesulfurization catalyst with essentially all the total pore volume in pores having diameters greater than about 100 angstroms, at least about 80 percent of the total pore volume being in pores of diameter about 100 angstroms to about 200 angstroms, with at least about 35 percent of the total pore volume being in pores of diameter about 150 to about 200 angstroms, less than about 10 percent of the total pore volume being in pores of diameter greater than 300 angstroms, and a surface area about 100 m 2 /gram to about 200 m 2 /gram, said hydrodesulfurization catalyst having an average pore diameter at least about 35 angstroms smaller than the average pore diameter of said hydrodemetallization catalyst, so as to produce a second product hydrocarbon having substantially less sulfur and contaminant metals content than said oil.

Claim 17

A process for the hydrodesulfurization of a hydrocarbon oil containing a substantial proportion of contaminant metals, said process comprising the steps of: (1) contacting said oil in the presence of hydrogen under reaction conditions with a hydrodemetallization catalyst comprising an alumina support and one or more hydrogenation components selected from the group consisting of Group VIB metal components and Group VIII metal components, said catalyst with essentially all the pores having diameters greater than about 100 angstroms, at least about 80 percent of the total pore volume being in pores of diameter about 150 angstroms to about 300 angstroms, with at least about 35 percent of the total pore volume being in pores of diameter from about 150 to about 200 angstroms, less than about 10 percent of the total pore volume being in pores of diameter greater than 300 angstroms, and a surface area about 75 m 2 /gram to about 200 m 2 /gram, so as to produce a first hydrocarbon product having a lower contaminant metals content than said oil; and (2) contacting at least a portion of the hydrocarbon product from said step (1) in the presence of hydrogen under reaction conditions with a hydrodesulfurization catalyst comprising an alumina support and one or more hydrogenation components selected from the group consisting of Group VIB metal components and Group VIII metal components, said hydrodesulfurization catalyst with essentially all the total pore volume in pores having diameters greater than about 100 angstroms, at least about 80 percent of the total pore volume being in pores of diameter about 100 angstroms to about 200 angstroms, with at least about 35 percent of the total pore volume being in pores of diameter about 150 to about 200 angstroms, less than about 10 percent of the total pore volume being in pores of diameter greater than 300 angstroms, and a surface area about 100 m 2 /gram to about 200 m 2 /gram, said hydrodesulfurization catalyst having an average pore diameter at least about 35 angstroms smaller than the average pore diameter of said hydrodemetallization catalyst, so as to produce a second product hydrocarbon having substantially less sulfur and contaminant metals content than said oil.

Claim 18

The process as defined in claim 1 or 15 wherein said hydrocarbon oil contains at least about 50 ppmw of total contaminant metals.

Claim 19

The process as defined in claim 1 or 15 wherein said hydrocarbon oil comprises a substantial proportion of asphaltenes.

Claim 20

The process as defined in claim 15 wherein said first hydrodesulfurization catalyst has a total pore volume about 0.4 cc/gram to about 0.8 cc/gram.

Claim 21

The process as defined in claim 15 wherein said second hydrodesulfurization catalyst has a total pore volume about 0.25 cc/gram to about 0.65 cc/gram.

Claim 22

The process as defined in claim 15 wherein said first hydrodesulfurization catalyst has an average pore diameter about 190 angstroms to about 210 angstroms.

Claim 23

The process as defined in claim 15 wherein said second hydrodesulfurization catalyst has an average pore diameter about 150 angstroms to about 170 angstroms.

Claim 24

A process for the catalytic hydrodesulfurization of a hydrocarbon residuum oil containing at least about 100 ppmw of contaminant metals and at least about one weight percent of sulfur, said process comprising the steps of: (1) contacting said oil in the presence of hydrogen under hydrodemetallization conditions with a hydrodemetallizion catalyst comprising about 8 to about 16 weight percent of molybdenum components, calculated as MoO 3 , about 1 to about 8 weight percent of cobalt components, calculated as CoO, on a support consisting essentially of gamma alumina, said hydrodemetallization catalyst with essentially all the pores having diameters greater than about 100 angstroms, at least about 85 percent of the total pore volume being in pores of diameter about 150 angstroms to about 300 angstroms, with at least about 35 percent of the total pore volume being in pores of diameter about 150 to about 200 angstroms, less than 10 percent of the total pore volume being in pores of diameter greater than 300 angstroms and a surface area about 90 m 2 /gram to about 150 m 2 /gram; and (2) contacting at least a portion of the hydrocarbon product from said step (1) under reaction conditions with a second catalyst useful for both hydrodemetallization and hydrodesulfurization, said catalyst comprising about 8 to about 16 weight percent of molybdenum components, calculated as MoO 3 , about 1 to about 8 weight percent of cobalt components, calculated as CoO, on a refractory oxide support comprising gamma alumina, said catalyst with essentially all the pores having diameters greater than about 100 angstroms, at least 80 percent of the total pore volume being in pores of diameter about 100 angstroms to about 200 angstroms, with at least about 35 percent of the total pore volume being in pores of diameter about 150 to about 200 angstroms, less than 6 percent of the total pore volume in pores of diameter greater than 300 angstroms and a surface area about 100 m 2 /gram to about 200 m 2 /gram, said catalyst having an average pore diameter at least about 35 angstroms smaller than the average pore diameter of said first hydrodemetallization catalyst, so as to remove at least 85 percent of said contaminant metals and at least 85 percent of said sulfur from said residuum oil.

Claim 25

A process for the catalytic hydrodesulfurization of a hydrocarbon residuum oil containing at least about 100 ppmw of contaminant metals and at least about one weight percent of sulfur, said process comprising the steps of: (1) contacting said oil in the presence of hydrogen under hydrodemetallization conditions with a hydrodemetallizion catalyst comprising about 8 to about 16 weight percent of molybdenum components, calculated as MoO 3 , about 1 to about 8 weight percent of cobalt components, calculated as CoO, on a support consisting essentially of gamma alumina, said hydrodemetallization catalyst with essentially all the pores having diameters greater than about 100 angstroms, at least about 85 percent of the total pore volume being in pores of diameter about 150 angstroms to about 300 angstroms, with at least about 35 percent of the total pore volume being in pores of diameter about 150 to about 200 angstroms, less than 10 percent of the total pore volume being in pores of diameter greater than 300 angstroms and a surface area about 90 m 2 /gram to about 150 m 2 /gram; and (2) contacting at least a portion of the hydrocarbon product from said step (1) under reaction conditions with a second catalyst useful for both hydrodemetallization and hydrodesulfurization, said catalyst comprising about 8 to about 16 weight percent of molybdenum components, calculated as MoO 3 , about 1 to about 8 weight percent of cobalt components, calculated as CoO, on a refractory oxide support comprising gamma alumina, said catalyst with essentially all the pores having diameters greater than about 100 angstroms, at least 80 percent of the total pore volume being in pores of diameter about 100 angstroms to about 200 angstroms, with at least about 35 percent of the total pore volume being in pores of diameter about 150 to about 200 angstroms, less than 6 percent of the total pore volume in pores of diameter greater than 300 angstroms and a surface area about 100 m 2 /gram to about 200 m 2 /gram, said catalyst having an average pore diameter at least about 35 angstroms smaller than the average pore diameter of said first hydrodemetallization catalyst, so as to remove at least 85 percent of said contaminant metals and at least 85 percent of said sulfur from said residuum oil.

Claim 26

The process as defined in claim 22 wherein said hydrodemetallization catalyst has an average pore diameter from about 190 angstroms to about 210 angstroms.

Claim 27

The process as defined in claim 22 wherein said catalyst in step (2) has an average pore diameter from about 150 angstroms to about 170 angstroms.

Claim 28

The process as defined in claim 15 or 22 wherein said catalyst in step (1) has at least about 40 percent of the total pore volume in pores of diameter about 200 angstroms to about 300 angstroms.

Claim 29

The process as defined in claim 15 or 22 wherein said catalyst in step (2) has at least about 40 percent of the total pore volume in pores of diameter about 100 angstroms to about 150 angstroms.

Claim 30

The process as defined in claim 1, 15 or 22 wherein said catalysts further comprise particulates having a cross-sectional diameter about 1/40 to about 1/8 inches.

Claim 31

The process as defined in claim 22 wherein said second catalyst contains about 11 to about 14 weight percent of said molybdenum components, about 2.5 to about 5.5 weight percent of said cobalt components on said refractory oxide support further comprising components selected from the group consisting of phosphorus and lithium.

Claim 32

A process for the catalytic hydroprocessing of a hydrocarbon oil, said process consisting essentially of successively contacting said oil in the presence of hydrogen under hydroprocessing conditions with a first hydroprocessing catalyst in a first reaction zone and, subsequently, a second hydroprocessing catalyst in a second reaction zone, said first catalyst and said second catalyst comprising one or more hydrogenation metal components on a porous refractory oxide support material with essentially all the pores having diameters greater than about 100 angstroms, and with less than 10 percent of the total pore volume being in pores of diameter greater than 300 angstroms, and with at least about 35 percent of the total pore volume being in pores of diameter about 150 to about 200 angstroms, said first hydroprocessing catalyst having an average pore diameter at least about 30 angstroms larger than the average pore diameter of said second hydroprocessing catalyst.

Claim 33

A process for the catalytic hydroprocessing of a hydrocarbon oil, said process consisting essentially of successively contacting said oil in the presence of hydrogen under hydroprocessing conditions with a first hydroprocessing catalyst in a first reaction zone and, subsequently, a second hydroprocessing catalyst in a second reaction zone, said first catalyst and said second catalyst comprising one or more hydrogenation metal components on a porous refractory oxide support material with essentially all the pores having diameters greater than about 100 angstroms, and with less than 10 percent of the total pore volume being in pores of diameter greater than 300 angstroms, and with at least about 35 percent of the total pore volume being in pores of diameter about 150 to about 200 angstroms, said first hydroprocessing catalyst having an average pore diameter at least about 30 angstroms larger than the average pore diameter of said second hydroprocessing catalyst.

Claim 34

The process as defined in claim 29 wherein the volume ratio of said first hydroprocessing catalyst to said second hydroprocessing catalyst is between about 1:10 and 10:1.

Claim 35

The process as defined in claim 29 wherein said first hydroprocessing catalyst has an average pore diameter greater than about 180 angstroms.

Claim 36

The process as defined in claim 29 wherein said second hydroprocessing catalyst has an average pore diameter less than about 180 angstroms.

Claim 37

The process as defined in claim 29 wherein said first hydroprocessing catalyst has at least 80 percent of the total pore volume in pores of diameter from about 150 angstroms to about 300 angstroms and a surface area less than about 200 m 2 /gram.

Claim 38

The process as defined in claim 29 wherein said second hydroprocessing catalyst has at least about 80 percent of the total pore volume in pores of diameter from about 100 angstroms to about 200 angstroms and a surface area less than about 300 m 2 /gram.

Claim 39

The process as defined in claim 29 wherein said hydrogenation metal components are selected from the group consisting of Group VIB and Group VIII metals.

Claim 40

The process as defined in claim 29 wherein said catalytic hydroprocessing includes demetallization and desulfurization.