Alumina compounds in ion exchange resins

Claim 2

In a process for recovering Li + from brine by the use of a composite comprising an ion exchange resin having dispersed therein crystalline LiX.2Al(OH) 3 , where X is halide, the improvement which comprises the use of a composite prepared by: precipitating Al(OH) 3 in the reticules of a weak-base anion exchange resin by the in-situ ammonia precipitation of Al halide in aqueous media, thereby forming a composite of anion exchange resin having Al(OH) 3 dispersed therein, followed by the additional steps of (a) slightly acidifying the so-formed composite in an aqueous medium with HX, X being halide, where the amount of HX is an amount sufficient to provide an acid pH of not lower than about 5.0, thereby converting the anion exchange resin to the halide salt form, (b) subtantially separating the composite from the aqueous portion, (c) substantially flooding the composite with an aqueous solution of Al halide, draining the excess solution, (d) adding NH 4 OH to precipitate additional Al(OH) 3 in the resin, and (e) reacting with a Li compound at elevated temperature to form crystalline LiX.2Al(OH) 3 dispersed in the resin.

Claim 3

The process of claim 1 wherein ammonium halide is employed along with the HX during the acidifying step.

Claim 4

The process of claim 1 wherein ammonium halide, in an amount of about 5% to about 25% of the aqueous portion is employed along with the HX during the acidifying step.

Claim 5

The process of claim 1 wherein the steps (a) through (d) are repeated one or more times.

Claim 6

The process of claim 1 wherein each halide is chloride.

Claim 7

The process of claim 1 wherein the acidifying step is performed in the temperature range of about 20° C. to about 100° C.

Claim 8

The process of claim 1 wherein the acidifying step is performed in the temperature range of about 45° C. to about 100° C.

Claim 9

The process of claim 1 wherein step (e) comprises reacting, in aqueous media at elevated temperature, the so-formed composite of resin and Al(OH) 3 with LiOH and/or LiX, where X is halogen, to convert the Al(OH) 3 to crystalline LiOH.2Al(OH) 3 and/or LiX.2Al(OH) 3 , thereafter contacting with acidic LiX to convert any crystalline LiOH.2Al(OH) 3 to crystalline LiX.2Al(OH) 3 .

Claim 10

In the process for recovering Li + from brine by the use of a composite comprising an ion exchange resin having dispersed therein crystalline LiCl.2Al(OH) 3 , the improvement which comprises the use of a composite prepared by: precipitating Al(OH) 3 in the reticules of a weak-base anion exchange resin by the in-situ ammonia precipitation of AlCl 3 in aqueous solution, thereby forming a composite of anion exchange resin having Al(OH) 3 dispersed therein, followed by the additional steps of (a) acidifying the so-formed composite in an aqueous medium with HCl to a pH of not lower than about 5.0, at a temperature in the range of about 20° C. to 100° C., thereby converting the anion exchange resin to the chloride salt form, (b) substantially separating the composite from the aqueous portion, (c) substantially flooding the composite with an aqueous solution of AlCl 3 , draining the excess solution, (d) adding NH 4 OH to precipitate additional Al(OH) 3 in the resin, (e) repeating steps (a) through (d) one or more times, and (f) reacting the so-formed composite, in aqueous media at elevated temperature, with LiOH and/or LiCl to convert the Al(OH) 3 to crystalline LiOH.2Al(OH) 3 and/or LiCl.2Al(OH) 3 , thereafter contacting with acidic LiCl to convert any crystalline LiOH.2Al(OH) 3 to crystalline LiCl.2Al(OH) 3 .

Claim 11

In the process for recovering Li + from brine by the use of a composite comprising an ion exchange resin having dispersed therein crystalline LiCl.2Al(OH) 3 , the improvement which comprises the use of a composite prepared by: precipitating Al(OH) 3 in the reticules of a weak-base anion exchange resin by the in-situ ammonia precipitation of AlCl 3 in aqueous solution, thereby forming a composite of anion exchange resin having Al(OH) 3 dispersed therein, followed by the additional steps of (a) acidifying the so-formed composite in an aqueous medium with HCl to a pH of not lower than about 5.0, at a temperature in the range of about 20° C. to 100° C., thereby converting the anion exchange resin to the chloride salt form, (b) substantially separating the composite from the aqueous portion, (c) substantially flooding the composite with an aqueous solution of AlCl 3 , draining the excess solution, (d) adding NH 4 OH to precipitate additional Al(OH) 3 in the resin, (e) repeating steps (a) through (d) one or more times, and (f) reacting the so-formed composite, in aqueous media at elevated temperature, with LiOH and/or LiCl to convert the Al(OH) 3 to crystalline LiOH.2Al(OH) 3 and/or LiCl.2Al(OH) 3 , thereafter contacting with acidic LiCl to convert any crystalline LiOH.2Al(OH) 3 to crystalline LiCl.2Al(OH) 3 .

Claim 12

The process of claim 9 wherein ammonium chloride is employed along with the HCl during the acidifying step.

Claim 13

The process of claim 9 wherein ammonium chloride in an amount of about 5% to about 25% of the aqueous portion is employed along with the HCl during the acidifying step.

Claim 14

The process of claim 9 wherein the acidifying step is performed at a temperature in the range of about 45° C. to about 100° C.