Method of producing green coatings on aluminum and aluminum alloys
Assignee: Individual
•
Filing: 1982-03-04
•
Granted: 1984-02-07
•
Expires: 2002-03-04
Abstract
Abstract A method of producing corrosion resistant, lightfast green coating on aluminum or an aluminum alloy wherein an initial anodic coating is formed on the aluminum or aluminum alloy. The anodized item is then placed in an electrolyte containing silver or silver and copper ions, and the metal ions or compounds thereof are electrolytically desposited into the pores of the anodic film which imparts a yellow color resembling gold to the anodic film. The colored anodic film is then dyed with a light fast blue organic dye. The resulting green colored coating is lightfast and corrosion resistant.
Inventors
- 👤 Jack L. Woods
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 20:39
CPC Classifications
C; C25; C25D; C25D11/00; C25D11/02; C25D11/04; C25D11/18; C25D11/24; C25D11/243; C25D11/20; C25D11/22
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
119 words
A process for producing a green colored coating on aluminum or aluminum alloys comprising the steps of: anodizing the aluminum or aluminum alloy article to form an anodic coating thereon; passing an alternating current between an electrode system comprising the previously anodized aluminum or aluminum alloy article and a counter electrode, while said electrode system is immersed in an aqueous, acidic bath comprising from about 0.2 to 0.4 grams per liter of a soluble silver salt, whereby the anodic coating on said anodized article is colored yellow; and immersing the yellow colored, anodized article in a dye bath containing a lightfast blue dye, whereby the yellow colored anodic coating on said anodized article is converted to a green color.
Claim 2
Dependent Claim
119 words
A process for producing a green colored coating on aluminum or aluminum alloys comprising the steps of: anodizing the aluminum or aluminum alloy article to form an anodic coating thereon; passing an alternating current between an electrode system comprising the previously anodized aluminum or aluminum alloy article and a counter electrode, while said electrode system is immersed in an aqueous, acidic bath comprising from about 0.2 to 0.4 grams per liter of a soluble silver salt, whereby the anodic coating on said anodized article is colored yellow; and immersing the yellow colored, anodized article in a dye bath containing a lightfast blue dye, whereby the yellow colored anodic coating on said anodized article is converted to a green color.
Claim 3
Dependent Claim
17 words
A process as claimed in claim 1, wherein said aqueous, acidic bath further includes a soluble salt.
Claim 4
Dependent Claim
41 words
A process as claimed in claim 1 wherein said aqueous, acidic bath comprises from about 0.2 to 0.4 grams per liter of silver sulfate and sufficient sulfuric acid to give said aqueous bath a pH of from about 1.0 to 1.4.
Claim 5
Dependent Claim
24 words
A process as claimed in claim 3, wherein said aqueous, acidic bath also contains about 10 to 20 grams per liter of copper sulfate.
Claim 6
Dependent Claim
24 words
A process as claimed in claim 4, wherein said aqueous, acidic bath also contains about 3 to 10 grams per liter of aluminum sulfate.
Claim 7
Dependent Claim
24 words
A process as claimed in claim 3, wherein said aqueous, acidic bath also contains about 3 to 10 grams per liter of aluminum sulfate.
Claim 8
Dependent Claim
82 words
A process as claimed in claim 3, wherein said aqueous acidic bath also contains about 10 to 20 grams per liter of copper sulfate and about 3 to 10 grams per liter of aluminum sulfate and further wherein the temperature of said aqueous, acidic bath is maintained at between about 14° C. and 25° C., and the current density of the current passing through said anodized article in the aqueous acidic bath is between about 0.2 and 0.4 amp per square decimeter.
Claim 9
Dependent Claim
46 words
A process as claimed in claim 3, wherein the anodizing of the aluminum or aluminum alloy is done in an anodizing electrolyte comprising from about 100 to 250 grams per liter of sulfuric acid and from about 0 to 10 grams per liter of oxalic acid.
Claim 10
Dependent Claim
59 words
A process as claimed in claim 3, wherein the anodizing of the aluminum or aluminum alloy is done in an anodizing electrolyte comprising from about 100 to 250 grams per liter of sulfuric acid, about 0 to 5 milliliters per liter of glycerol, and from about 0 to 10 milliliters per liter of a 70% aqueous glycolic acid solution.
Claim 11
Dependent Claim
27 words
A process as claimed in claim 1 wherein the lightfast blue dye is selected from the group consisting of phthalocyanine acid blue and anthraquinone acid blue dyes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-02-06 | 1987-08-08 | 1988-02-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-02-06 | 1991-08-08 | 1992-02-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-02-06 | 1995-08-08 | 1996-02-07 | $7700.00 | Window Closed / Lapsed |