Delta-alpha bond/superplastic forming method of fabricating titanium structures and the structures resulting therefrom
Assignee: Rohr Inc
•
Filing: 1981-09-17
•
Granted: 1984-02-07
•
Expires: 2001-09-17
Abstract
Abstract Method of manufacturing structures from sheets of material having superplasticity as well as diffusion bonding capabilities wherein a combination of diffusion bonding and superplastic forming is performed concurrently with the use of low pressures and a simple heat furnace. The material to be formed and bonded is placed between and sealed in tooling constructed of materials having different degrees of thermal expansion. A low pressure from an external source is applied between the sheets of material to be formed during heating. Forming shims positioned within the tooling provide areas of diffusion bonding when the applied pressure and differential of tooling expansion force the sheets of material together at the shim locations.
Inventors
- 👤 James R. Woodward
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 03:34
CPC Classifications
B; B21; B21D; B21D26/00; B21D26/02; B21D26/053; B21D26/055; B23; B23K; B23K20/00; B23K20/22; B23K20/233
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
190 words
Method of manufacturing structures from sheets of material with superplasticity characteristics comprising the steps of: placing at least two overlapping sheets of said material between an inner and outer mandrel tool, said inner mandrel tool having a greater coefficient of thermal expansion than said outer mandrel tool; placing forming shims between one of said mandrel tools and the adjacent sheet at locations where said sheets of material are overlapping and to be joined by diffusion bonding; sealing the sheets of material from the atmosphere; applying inert gas under pressure between said sheets when the sealing of the sheets of material from the atmosphere is complete to provide separation of sheets at regions not sandwiched by said shims, and elevating said temperature sufficiently to render said sheets of material to a state of superplasticity to cause said inner mandrel tool to expand toward said outer mandrel tool compressing said sheet material therebetween and causing the contacting surface of said sheets of material to bond together by diffusion means, said gas pressure being sufficient to cause said sheet material to form into the voids between said tooling shims and said mandrel tools.
Claim 2
Dependent Claim
190 words
Method of manufacturing structures from sheets of material with superplasticity characteristics comprising the steps of: placing at least two overlapping sheets of said material between an inner and outer mandrel tool, said inner mandrel tool having a greater coefficient of thermal expansion than said outer mandrel tool; placing forming shims between one of said mandrel tools and the adjacent sheet at locations where said sheets of material are overlapping and to be joined by diffusion bonding; sealing the sheets of material from the atmosphere; applying inert gas under pressure between said sheets when the sealing of the sheets of material from the atmosphere is complete to provide separation of sheets at regions not sandwiched by said shims, and elevating said temperature sufficiently to render said sheets of material to a state of superplasticity to cause said inner mandrel tool to expand toward said outer mandrel tool compressing said sheet material therebetween and causing the contacting surface of said sheets of material to bond together by diffusion means, said gas pressure being sufficient to cause said sheet material to form into the voids between said tooling shims and said mandrel tools.
Claim 3
Dependent Claim
146 words
Tooling for combined diffusion bonding and superplastic forming titanium alloy sheet material comprising: an inner and outer mandrel, said inner mandrel having a relatively high coefficient of thermal expansion and said outer mandrel having a relatively low coefficient of thermal expansion; at least two overlapping sheets of titanium material with superplasticity characteristics disposed between said inner and outer mandrel; means for supplying gas under pressure between said at least two sheets of said titanium material when they are positioned between said mandrels; means for sealing said at least two sheets of titanium alloy material from the atmosphere when they are positioned between said mandrels; and shim means placed between one of said sheets and the adjacent mandrel at locations where the joining of the two sheets of titanium alloy material is desired and omitted from locations where forming of the two sheets of titanium is desired.
Claim 4
Dependent Claim
146 words
Tooling for combined diffusion bonding and superplastic forming titanium alloy sheet material comprising: an inner and outer mandrel, said inner mandrel having a relatively high coefficient of thermal expansion and said outer mandrel having a relatively low coefficient of thermal expansion; at least two overlapping sheets of titanium material with superplasticity characteristics disposed between said inner and outer mandrel; means for supplying gas under pressure between said at least two sheets of said titanium material when they are positioned between said mandrels; means for sealing said at least two sheets of titanium alloy material from the atmosphere when they are positioned between said mandrels; and shim means placed between one of said sheets and the adjacent mandrel at locations where the joining of the two sheets of titanium alloy material is desired and omitted from locations where forming of the two sheets of titanium is desired.
Claim 5
Dependent Claim
51 words
The invention as defined in claim 1 wherein the pressure of said gas under pressure is at a first level to cause a slight separation of said material between said shims at an intermediate temperature and is at a second elevated level for forming said material at a superplastic forming temperature.
Claim 6
Dependent Claim
20 words
The invention as defined in claim 2 wherein said inner mandrel is constructed of a T-300 series austenitic stainless steel.
Claim 7
Dependent Claim
20 words
The invention as defined in claim 2 wherein said outer mandrel is constructed of a T-400 series ferritic stainless steel.
Claim 8
Dependent Claim
32 words
The invention as defined in claim 2 wherein said means for supplying gas under pressure is a pressure tube passing between said sheets of titanium material in an atmosphere sealed relationship therewith.
Claim 9
Dependent Claim
31 words
The invention as defined in claim 2 wherein said means for sealing said two sheets comprises a sealing ring positioned between said inner and outer mandrel at each end surface thereof.
Claim 10
Independent Claim
127 words
A system in which flat mandrels sandwich at least two overlapping superplastic material sheets with intervening forming shims placed in locations of overlap to be diffusion bonded together, the mandrels and assemblage being secured together by low thermally expanding refractory metal bolts which upon heating clamp the assemblage with a pressure which causes diffusion bonding of the areas compressed by the shims and other areas being pressurized by an inert gas to cause superplastic forming of the metals into the cavity caused by the mandrels when the temperature of the assemblage is suitably elevated, said inert gas being admitted by a small tube placed between said material sheets at their outer edges and sealed thereto by the differential in thermal expansion between said bolts and said mandrel.
Claim 11
Independent Claim
127 words
A system in which flat mandrels sandwich at least two overlapping superplastic material sheets with intervening forming shims placed in locations of overlap to be diffusion bonded together, the mandrels and assemblage being secured together by low thermally expanding refractory metal bolts which upon heating clamp the assemblage with a pressure which causes diffusion bonding of the areas compressed by the shims and other areas being pressurized by an inert gas to cause superplastic forming of the metals into the cavity caused by the mandrels when the temperature of the assemblage is suitably elevated, said inert gas being admitted by a small tube placed between said material sheets at their outer edges and sealed thereto by the differential in thermal expansion between said bolts and said mandrel.
Claim 12
Dependent Claim
24 words
The invention as defined in claim 8 wherein said bolts are constructed of molybdenum and the mandrels are constructed of austenitic stainless steel material.
Claim 13
Dependent Claim
16 words
The invention as defined in claim 8 wherein said bolts are constructed of super alloy material.
Claim 14
Dependent Claim
31 words
The invention as defined in claim 8 wherein the differential of thermal expansion is amplified by the addition of relatively high expanding sleeves or tubes positioned between said bolts and mandrel.
Claim 15
Dependent Claim
9 words
A structure formed from the method of claim 1.
Claim 16
Dependent Claim
48 words
The method of claim 1 wherein said step of sealing the sheets of material from the atmosphere comprises providing means for sealing said sheets from the atmosphere when the temperature of said tools is elevated to a predetermined level below the temperature at which said sheets become superplastic.
Claim 17
Dependent Claim
12 words
The method of claim 1 wherein said mandrels are annular and concentric.
Claim 18
Dependent Claim
12 words
The method of claim 2 wherein said mandrels are annular and concentric.
References Cited (Backward Citations)
GB1398929A
Cited
US3927817A
Cited
US4046305A
Cited
US4087037A
Cited
US4029254A
Cited
US4089456A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-02-06 | 1987-08-08 | 1988-02-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-02-06 | 1991-08-08 | 1992-02-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-02-06 | 1995-08-08 | 1996-02-07 | $7700.00 | Window Closed / Lapsed |