Method for producing prepreg rovings
Assignee: DIC Corp
•
Filing: 1981-02-20
•
Granted: 1984-01-24
•
Expires: 2001-02-20
Abstract
Abstract A method for producing a prepreg roving, which comprises impregnating a composition comprising an unsaturated polyester, an unsaturated monomer and a polyisocynate compound in a filamentary reinforcing material, and then heating the impregnated reinforcing material to react the unsaturated polyester with the polyisocyanate compound; and a method for producing a fiber-reinforced plastic article, which comprises disposing prepreg rovings (A), said prepreg rovings being prepared by the above method between at least two plies of sheet molding compound (B) obtained by impregnating a composition comprising an unsaturated polyester and an unsaturated monomer in glass fibers and forming the impregnated product into a sheet; and consolidating the resulting assembly under heat and pressure.
Inventors
- 👤 Fumiyoshi Yamada
- 👤 Shunichi Hiraishi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 15:07
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/003; B29B; B29B15/00; B29B15/08; B29B15/10; B29B15/12; B29B15/122; B29B15/125; B29C70/04; B29C70/06; B29C70/08; B29C70/083; B29C70/10; B29C70/16; B29C70/22; B32; B32B; B32B38/00; B32B38/08; B32B5/00; B32B5/02; B32B5/028; B32B5/22; C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/67; C08G18/6705; C08G18/68; C08J; C08J5/00; C08J5/04; B29K; B29K2309/00; B29K2309/08; B32B2262/00; B32B2262/10; B32B2262/101; B32B2305/00; B32B2305/08; B32B2305/38; C08J2375/00; C08J2375/04; C08J2375/06; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24132
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
155 words
A method for producing a fiber-reinforced plastic article, which comprises disposing prepreg rovings, said prepreg rovings being prepared by impregnating a composition comprising an unsaturated polyester having a hydroxyl value of at least 20, and a hydroxyl value/acid value ratio of at least 1.5, an unsaturated monomer, and a polyisocyanate compound, the amount of said polyisocyanate compound being such that the mole ratio of the hydroxyl groups of the unsaturated polyester to the isocyanate groups of the polyisocyanate compound is from 0.7 to 1.3, into a filamentary reinforcing material and heating the impregnated reinforcing material at a temperature of 60° C. to 110° C. to react the unsaturated polyester with the polyisocyanate compound, between at least two plies of sheet molding compound obtained by impregnating a composition comprising an unsaturated polyester and an unsaturated monomer in glass fibers and forming the impregnated product into a sheet; and consolidating the resulting assembly under heat and pressure.
Claim 2
Independent Claim
155 words
A method for producing a fiber-reinforced plastic article, which comprises disposing prepreg rovings, said prepreg rovings being prepared by impregnating a composition comprising an unsaturated polyester having a hydroxyl value of at least 20, and a hydroxyl value/acid value ratio of at least 1.5, an unsaturated monomer, and a polyisocyanate compound, the amount of said polyisocyanate compound being such that the mole ratio of the hydroxyl groups of the unsaturated polyester to the isocyanate groups of the polyisocyanate compound is from 0.7 to 1.3, into a filamentary reinforcing material and heating the impregnated reinforcing material at a temperature of 60° C. to 110° C. to react the unsaturated polyester with the polyisocyanate compound, between at least two plies of sheet molding compound obtained by impregnating a composition comprising an unsaturated polyester and an unsaturated monomer in glass fibers and forming the impregnated product into a sheet; and consolidating the resulting assembly under heat and pressure.
Claim 3
Dependent Claim
25 words
The method of claim 1 wherein said prepreg rovings are aligned parallel to each other between at least two plies of said sheet molding compound.
Claim 4
Dependent Claim
25 words
The method of claim 1 wherein said prepreg rovings are arranged in a lattice form between at least two plies of said sheet molding compound.
Claim 5
Dependent Claim
26 words
The method of claim 1 wherein a net-like article made of the prepreg rovings is disposed between at least two plies of said sheet molding compound.
Claim 6
Dependent Claim
110 words
A continuous method for producing a prepreg roving having reduced tack, which comprises impregnating into a filamentary reinforcing material a composition comprising (1) unsaturated polyester having a hydroxyl value of at least 20, and a hydroxyl value/acid value ratio of at least 1.5, (2) an unsaturated monomer and (3) a polyisocyanate compound, the amount of said polyisocyanate compound being such that the mole ratio of the hydroxyl groups of the unsaturated polyester to the isocyanate groups of the polyisocyanate compound is from 0.7 to 1.3, and then heating the impregnated reinforcing material at a temperature of 60° C. to 110° C. to react the unsaturated polyester with the polyisocyanate compound.
Claim 7
Dependent Claim
110 words
A continuous method for producing a prepreg roving having reduced tack, which comprises impregnating into a filamentary reinforcing material a composition comprising (1) unsaturated polyester having a hydroxyl value of at least 20, and a hydroxyl value/acid value ratio of at least 1.5, (2) an unsaturated monomer and (3) a polyisocyanate compound, the amount of said polyisocyanate compound being such that the mole ratio of the hydroxyl groups of the unsaturated polyester to the isocyanate groups of the polyisocyanate compound is from 0.7 to 1.3, and then heating the impregnated reinforcing material at a temperature of 60° C. to 110° C. to react the unsaturated polyester with the polyisocyanate compound.
Claim 8
Dependent Claim
35 words
The method of claim 5 wherein said polyisocyanate compound is a diisocyanate compound of the general formula OCN--R--NCO wherein R represents an aliphatic, aromatic or alicyclic divalent group having not more than 20 carbon atoms.
Claim 9
Dependent Claim
30 words
The method of claim 5 wherein said filamentary reinforcing material is a roving of filaments selected from the group consisting of glass filaments, carbon filaments, metallic filaments and polyamide filaments.
Claim 10
Dependent Claim
31 words
The method of claim 5 wherein the amount of said unsaturated polyester resin composition impregnated in said filamentary reinforcing material is 35 to 85% by volume of the resulting prepreg roving.
Claim 11
Dependent Claim
67 words
A method according to claim 5, which comprises impregnating a filamentary reinforcing material with a composition comprising an unsaturated polyester, an unsaturated monomer and a polyisocyanate compound placed in a tank, then molding the impregnated reinforcing material and simultaneously adjusting the amount of the composition impregnated to a fixed value, and then passing the product through a heating oven thereby to bring the resin to a B-stage.
References Cited (Backward Citations)
US2596162A
Cited
US2861910A
Cited
US3008917A
Cited
US2977630A
Cited
US3361845A
Cited
US3222237A
Cited
US3442739A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-01-23 | 1987-07-25 | 1988-01-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-01-23 | 1991-07-25 | 1992-01-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-01-23 | 1995-07-25 | 1996-01-24 | $7700.00 | Window Closed / Lapsed |