Welding alloy and method
Assignee: Individual
•
Filing: 1982-07-22
•
Granted: 1984-01-17
•
Expires: 2002-07-22
Abstract
Abstract Spheroidal graphite cast iron body can be welded using a welding alloy whose carbon diffusion rate is sufficiently high that cementite formation is prevented. The alloy has essentially the following composition: less than 0.2% manganese, less than 2.0% carbon, 2.5 to 3.2% silicon, up to 1.0% copper, up to 0.5% molybdenum, up to 2% aluminum, up to 30% nickel, up to 0.1% tungsten, up to 0.1% chromium, up to 0.1% vanadium, magnesium and/or rare earth elements in an amount up to and sufficient to promote the formation of graphite spherolites upon cooling, and balance substantially iron.
Inventors
- 👤 Horst Muhlberger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 07:57
CPC Classifications
C; C22; C22C; C22C37/00; C22C37/10; B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/30; B23K35/3053; B23K35/3066; B23K35/3093; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/923; Y10S428/924; Y10S428/925; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12951; Y10T428/12958
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
95 words
A welding member in a form for generating a weldment welding to a spheroidal graphite cast iron body, said member consisting by weight of an alloy of the following composition: less than 0.1% manganese, less than 1.0% carbon, 2.8 to 2.9% silicon, 0.6 to 0.8% copper, 0.1 to 0.25% molybdenum, 0.2 to 0.3% aluminum 1 to 3% nickel, up to 1% tungsten, up to 0.1% chromium, up to 0.1% vanadium, magnesium and/or rare earth elements in an amount up to and sufficient to promote the formation of graphite spherulites upon cooling, and balance substantially iron.
Claim 2
Dependent Claim
95 words
A welding member in a form for generating a weldment welding to a spheroidal graphite cast iron body, said member consisting by weight of an alloy of the following composition: less than 0.1% manganese, less than 1.0% carbon, 2.8 to 2.9% silicon, 0.6 to 0.8% copper, 0.1 to 0.25% molybdenum, 0.2 to 0.3% aluminum 1 to 3% nickel, up to 1% tungsten, up to 0.1% chromium, up to 0.1% vanadium, magnesium and/or rare earth elements in an amount up to and sufficient to promote the formation of graphite spherulites upon cooling, and balance substantially iron.
Claim 3
Dependent Claim
16 words
The autogenous welding or electric arc welding rod composed of the alloy defined in claim 1.
Claim 4
Dependent Claim
11 words
A welding wire composed of the alloy defined in claim 1.
Claim 5
Dependent Claim
47 words
A member consisting essentially of the body of spheroidal graphite cast iron as defined in claim 1 and a transition body of said alloy metallically bonded to said body of cast iron and connected therewith by casting the cast iron body against said body of said alloy.
Claim 6
Dependent Claim
39 words
The member defined in claim 4 wherein said alloy body has a wall thickness and dimension such that, upon the casting of said cast body thereagainst, a normal steel can be welded to said member at said alloy body.
Claim 7
Dependent Claim
66 words
A method of making a transition piece for the welding of normal steel to a cast body which comprises the steps of: preforming an alloy body of the alloy defined in claim 1; and casting a spherolitic cast iron body in a mold in contact with said alloy body to form a metallic bond between said alloy body and the resulting spheroidal graphite cast iron body.
Claim 8
Dependent Claim
31 words
A method of welding which comprises the steps of forming a pool of an alloy as defined in claim 1 adjacent a spheroidal graphite cast iron body and cooling said pool.
References Cited (Backward Citations)
US1352534A
Cited
US2354147A
Cited
US3935038A
Cited
US3855018A
Cited
US3855018B1
Cited
US3929522A
Cited
US4078952A
Cited
US4338143A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-01-16 | 1987-07-18 | 1988-01-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-01-16 | 1991-07-18 | 1992-01-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-01-16 | 1995-07-18 | 1996-01-17 | $7700.00 | Window Closed / Lapsed |