Patent US4426262A successfully refreshed from Google Patents.
US4426262A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Promotion of Pt-Ir catalytic electrodes with lead, tantalum, ruthenium and oxygen
Assignee: BASF Catalysts LLC
•
Filing: 1982-04-29
•
Granted: 1984-01-17
•
Expires: 2002-04-29
Abstract
Abstract Platinum and iridium in catalytic electrodes for electrochemical uses is partially replaced with lead ruthenate-tantalum oxide composite. Electrodes are fabricated by first coating a film-forming metal substrate with a platinum-iridium composite undercoat, then overcoating with a composite containing lead, ruthenium, tantalum, platinum, iridium and oxygen. The most preferred anodes have a titanium substrate initially coated with approximately at least 2 gm/m 2 of 70:30 w /o Pt:Ir composite, followed by about 20 gm/m 2 of a composite having the nominal composition of 22.2 w /o Pb 2 Ru 2 O 6 ; 66.6 w /o Ta 2 O 5 ; 7.9 w /o Pt and 3.4 w /o Ir. The outer layer of the prepared anode contains from about 10 to about 16 w /o lead, from about 40 to about 65 w /o tantalum, from about 5 to about 7.5 w /o ruthenium, from about 6.0 to about 10 w /o platinum, from about 2.5 to about 5 w /o iridium, and from about 10 to about 20 w /o oxygen. These electrodes may be used in acidic, neutral or alkaline solutions. Typical uses include production of chlorine and chlorine compounds and electrowinning of metals, such as zinc.
Inventors
- 👤 Robert C. Langley
- 👤 Herbert Myers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 20:15
CPC Classifications
C; C25; C25B; C25B11/00; C25B11/04; C25B11/051; C25B11/073; C25B11/091; C25B11/093
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
55 words
An electrode having a valve metal substrate and a lead-tantalum-titanium-platinum iridium ruthenium-oxygen composite layer formed on said valve metal substrate, the composite layer having a platinum-iridium rich zone adjacent the substrate, the concentrations of platinum and iridium being higher in the platinum-iridium rich zone than throughout the rest of the lead-tantalum-titanium-platinum iridium ruthenium-oxygen composite layer.
Claim 2
Dependent Claim
55 words
An electrode having a valve metal substrate and a lead-tantalum-titanium-platinum iridium ruthenium-oxygen composite layer formed on said valve metal substrate, the composite layer having a platinum-iridium rich zone adjacent the substrate, the concentrations of platinum and iridium being higher in the platinum-iridium rich zone than throughout the rest of the lead-tantalum-titanium-platinum iridium ruthenium-oxygen composite layer.
Claim 3
Dependent Claim
50 words
An electrode having a valve metal substrate and a catalytic layer formed thereon, the catalytic layer having a platinim-iridium rich zone and a lead-ruthenium-tantalum-oxygen rich zone, the platinum-iridium rich zone being adjacent to the valve metal substrate and the lead-ruthenium-tantalum-oxygen rich zone being disposed exterior to the platinum iridium zone.
Claim 4
Dependent Claim
50 words
An electrode having a valve metal substrate and a catalytic layer formed thereon, the catalytic layer having a platinim-iridium rich zone and a lead-ruthenium-tantalum-oxygen rich zone, the platinum-iridium rich zone being adjacent to the valve metal substrate and the lead-ruthenium-tantalum-oxygen rich zone being disposed exterior to the platinum iridium zone.
Claim 5
Dependent Claim
43 words
The electrode of claim 2 wherein the lead-ruthenium-tantalum-oxygen rich zone containing from about 10 to about 16 w/o lead; from about 40 to about 65 w/o tantalum; from about 5 to about 7.5 w/o ruthenium; from about 10 to about 20 w/o oxygen.
Claim 6
Dependent Claim
223 words
The electrode of claim 2 wherein the catalytic layer is formed by the process comprising: (a) applying from about 2 to about 6 g/m 2 (calculated as metal) of an admixture of platinum-iridium compounds to the valve metal substrate, the platinum-iridium compound admixture consisting essentially of from about 20 to about 40 w/o thermally decomposable iridium compound, and from about 60 to 80 w/o thermally decomposable platinum compound (both calculated as metal) (b) firing the electrode at a temperature of from about 350° C. to about 550° C.; (c) then applying an admixture of lead-ruthenate and thermally decomposable tantalum and platinum group metal compounds, the admixture of lead ruthenate and thermally decomposable tantalum and platinum group metal compounds consisting essentially of: from about 20 to about 25 w/o lead ruthenate; from about 60 to about 75 w/o thermally decomposable tantalum compound from about 6 to about 11 w/o thermally decomposable platinum compound; and from about 2.5 to about 5 w/o thermally decomposable iridium compound (the respective percentage being calculated as lead ruthenate, tantalum oxide, platinum and iridium) (d) firing the electrode at a temperature of from about 350° to about 550° C., the total amount of lead ruthenate and thermally decomposable tantalum and platinum and iridium compounds applied being sufficient to result in a loading of at least about 10 g/m 2 .
Claim 7
Dependent Claim
11 words
The electrode of claim 4 wherein said valve metal is titanium.
Claim 8
Dependent Claim
11 words
The electrode of claim 2 wherein said valve metal is titanium.
Claim 9
Dependent Claim
19 words
The electrode of claim 2 wherein the total thickness of said catalytic layer is less than about 5 microns.
Claim 10
Independent Claim
63 words
A method of electrolyzing an aqueous halide salt solution, comprising passing an electrolysis current through the halide salt solution between an anode and a cathode, said anode comprising a valve metal substrate having a catalytic layer thereon, the catalytic layer having a platinum-iridium rich zone adjacent the valve metal substrate and a lead-ruthenium valve metal oxygen rich zone upon the platinum-iridium rich zone.
Claim 11
Independent Claim
63 words
A method of electrolyzing an aqueous halide salt solution, comprising passing an electrolysis current through the halide salt solution between an anode and a cathode, said anode comprising a valve metal substrate having a catalytic layer thereon, the catalytic layer having a platinum-iridium rich zone adjacent the valve metal substrate and a lead-ruthenium valve metal oxygen rich zone upon the platinum-iridium rich zone.
Claim 12
Dependent Claim
17 words
The method of claim 8 wherein the valve metal is titanium and said halide is a chloride.
Claim 13
Dependent Claim
40 words
The method of claim 9 wherein the electric current is passed through the chloride solution at a current density of between about 1 and 7 amp/in 2 , based on the geometric area of the catalytically-coated portion of the substrate.
Claim 14
Dependent Claim
21 words
The electrode of claim 1 wherein at least a portion of said lead-tantalum-titanium-platinum iridium ruthenium-oxygen composite is present as lead ruthenate.
Claim 15
Dependent Claim
26 words
The electrode of claim 2 wherein at least a portion of the lead, ruthenium and oxygen in said lead-ruthenium-tantalum-oxygen rich zone is present as lead ruthenate.
Claim 16
Dependent Claim
27 words
The electrode of claim 3 wherein at least a portion of the lead, ruthenium and oxygen in said lead-tantalum-ruthenium oxygen rich zone is present as lead ruthenate.
Claim 17
Dependent Claim
28 words
The method of claim 8 wherein at least a portion of the lead, ruthenium and oxygen in said lead-ruthenium valve metal-oxygen rich zone is present as lead ruthenate.
References Cited (Backward Citations)
US3177131A
Cited
US3778307A
Cited
US3718551A
Cited
US3773555A
Cited
US3603414A
Cited
US4203810A
Cited
US3691052A
Cited
US3926751A
Cited
US4157943A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-01-16 | 1987-07-18 | 1988-01-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-01-16 | 1991-07-18 | 1992-01-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-01-16 | 1995-07-18 | 1996-01-17 | $7700.00 | Window Closed / Lapsed |