US4421717A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making wear resistant ferrous based parts
Assignee: Ford Global Technologies LLC
•
Filing: 1982-06-10
•
Granted: 1983-12-20
•
Expires: 2002-06-10
Abstract
Abstract A method is disclosed for making wear resistant, ferrous based parts (10) by molding a uniform mixture of ferrous based powder and binder material into a compacted shape, heating the compacted shape to remove the binder and to partially sinter the mixture to a strength of 1000-8000 psi, while maintaining a porosity of 20-40% at least along the outer region of the part, depositing a fluid suspension of wear resistant particles onto a surface zone of the shape, and heating the coated shape to bond the particles to the surface and fully sinter the part.
Inventors
- 👤 Vemulapalli D. N. Rao
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 10:24
CPC Classifications
F; F01; F01L; F01L1/00; F01L1/12; F01L1/18; F01L1/185; C; C23; C23C; C23C24/00; C23C24/08; C23C24/10; F01L2301/00
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
140 words
A method of making a wear resistant, ferrous based part, comprising the steps of: (a) molding a uniform mixture of ferrous based powder and binder material into a compacted shape; (b) heating said compacted shape to remove said binder material and to partially sinter said mixture to a strength of about 1000-8000 psi, while maintaining a porosity of 20-40% at least along the outer region of said part; (c) depositing a fluid suspension of refractory wear resistant powder particles onto at least a selected surface zone of said partially sintered shape, said particles coating said zone and permeating the surface region of said zone by absorption as permitted by said porosity; and (d) heating said coated shape to remove said fluid, to bond said particles to said shape, and to fuse said powder and particles together to define said part.
Claim 2
Independent Claim
140 words
A method of making a wear resistant, ferrous based part, comprising the steps of: (a) molding a uniform mixture of ferrous based powder and binder material into a compacted shape; (b) heating said compacted shape to remove said binder material and to partially sinter said mixture to a strength of about 1000-8000 psi, while maintaining a porosity of 20-40% at least along the outer region of said part; (c) depositing a fluid suspension of refractory wear resistant powder particles onto at least a selected surface zone of said partially sintered shape, said particles coating said zone and permeating the surface region of said zone by absorption as permitted by said porosity; and (d) heating said coated shape to remove said fluid, to bond said particles to said shape, and to fuse said powder and particles together to define said part.
Claim 3
Dependent Claim
27 words
The method as in claim 1, in which in step (a) said ferrous based powder and binder are mixed in a ratio of about 70/30% by weight.
Claim 4
Dependent Claim
21 words
The method as in claim 1, in which in step (a) said ferrous powder is constituted of SAE 52100 steel particles.
Claim 5
Dependent Claim
26 words
The method as in claim 1, in which in step (a) said mixture is formed into pellets prior to being molded to form said compacted shape.
Claim 6
Dependent Claim
30 words
The method as in claim 1, in which in step (b) said heating is carried out in the range of 1700°-2150° F. (926°-1176.7° C.) for a period of 15-30 minutes.
Claim 7
Dependent Claim
38 words
The method as in claim 1, in which in step (b) said heating is carried out in the range of 1950°-2150° F. (926°-1176.7° C.) and in a nitrogen atmosphere with the total heatup period being about 2-6 hours.
Claim 8
Dependent Claim
86 words
The method as in claim 1, in which in step (b) said heating is carried out in increments, with a first increment from room temperature to 300° F. for about one hour, a second increment from 300°-450° F. for about one hour, a third increment from 450°-1950° F. for about two hours, and a last increment from 1950°-2150° F. for about one-quarter hour, said partial sintering taking place during said last increment and the removal of said binder being accomplished substantially during the other increments. PG,13
Claim 9
Dependent Claim
56 words
The method as in claim 1, in which in step (c) said wear resistant powder particles are selected of a material to have a hardness value of at least RC-55, a thermal expansion mismatch of less than 4×10 -6 in/in/°F., and a coefficient of friction of less than 0.1 against lubricated cast iron or hardened steel.
Claim 10
Dependent Claim
29 words
The method as in claim 1, in which in step (c) said depositing is carried out by spraying an aqueous slurry of said wear resistant particles onto said zone.
Claim 11
Dependent Claim
30 words
The method as in claim 1, in which in step (c) said depositing is carried out by dipping said partially sintered shape into a slurry containing said wear resistant particles.
Claim 12
Dependent Claim
29 words
The method as in claim 1, in which in step (c) said depositing is carried out to provide a coating thickness in the range of 2-20 mils (0.002-0.020 inch).
Claim 13
Dependent Claim
51 words
The method as in claim 1, in which in step (c) said wear resistant particles are selected from the group consisting essentially of Cr 2 O 3 , Al 2 O 3 and SiC, and including a binder material selected from the group consisting of cobalt, nickel or equivalent brazing material.
Claim 14
Dependent Claim
30 words
The method as in claim 1, in which in step (c) said depositing is carried out in sequential increments, the final increment providing a resulting thickness of about 0.010 inch.
Claim 15
Dependent Claim
25 words
The method as in claim 1, in which in step (c) the wear resistant particles have an average particle size of 10 microns or less.
Claim 16
Dependent Claim
34 words
The method as in claim 1, in which in step (c) the wear resistant particles are comprised of an alloy consisting essentially of by weight 45-70% cobalt, 28-48% molybdenum, 2-10% Si, and 0.5-10% Cr.
Claim 17
Dependent Claim
49 words
The method as in claim 1, in which in step (c) said wear resistant particles are prepared by ball milling with media consisting essentially of either silicon carbide or chromium containing steel, along with 0.5 gram of methyl cellulose per 100 grams of particles in 100 cc's of water.
Claim 18
Dependent Claim
42 words
The method as in claim 1, in which in step (d) heating is carried out by rapidly heating to 2000° F. (1093.3° C.) and holding for 15-30 minutes, then raising to the temperature of 2100° F. (1148.9° C.) for about one hour.
Claim 19
Dependent Claim
24 words
The method as in claim 1, in which in step (d) heating is carried out in a dry hydrogen atmosphere (-70° F. dew point).
Claim 20
Dependent Claim
25 words
The method as in claim 1, in which the resulting heated coated shape of step (d) is slowly cooled for a period of 4-10 hours.
References Cited (Backward Citations)
US2299192A
Cited
US2775531A
Cited
US3684498A
Cited
US3743556A
Cited
US3929476A
Cited
US4062678A
Cited
US4158689A
Cited
US4035159A
Cited
US4124737A
Cited
US4147074A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-19 | 1987-06-20 | 1987-12-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-19 | 1991-06-20 | 1991-12-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-19 | 1995-06-20 | 1995-12-20 | $7700.00 | Window Closed / Lapsed |