Potentially non-linear resistor and process for producing the same
Assignee: Hitachi Ltd
•
Filing: 1981-10-30
•
Granted: 1983-12-13
•
Expires: 2001-10-30
Abstract
Abstract A sintered product composed chiefly of zinc oxide. A paste composed of a glass powder, an organic binder and tin oxide having a catalytic activity for promoting the combustion of organic binder, is coated on the side surfaces of the sintered product. The paste coated on the sintered product is baked to remove by burning the organic binder in the paste. Then, electrodes are attached to the main surfaces of the sintered product to complete a non-linear resistor.
Inventors
- 👤 Tadahiko Miyoshi
- 👤 Takeo Yamazaki
- 👤 Kunihiro Maeda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 11:37
CPC Classifications
H; H01; H01C; H01C7/00; H01C7/10; H01C7/102; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49082
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
62 words
A potentially non-linear resistor comprising a sintered product formed chiefly of a zine oxide sintered body, the side surfaces of said product being provided with a glass layer and the end surfaces of said product being provided with electrodes, wherein said glass layer comprises a lead borosilicate glass that further contains tin oxide in an amount of 0.4 to 10% by weight.
Claim 2
Dependent Claim
62 words
A potentially non-linear resistor comprising a sintered product formed chiefly of a zine oxide sintered body, the side surfaces of said product being provided with a glass layer and the end surfaces of said product being provided with electrodes, wherein said glass layer comprises a lead borosilicate glass that further contains tin oxide in an amount of 0.4 to 10% by weight.
Claim 3
Dependent Claim
41 words
A potentially non-linear resistor as set forth in claim 1, wherein a high-resistance layer comprised of zinc antimonate and zinc silicate is provided on a side surface of said sintered body, and said glass layer is coated on said high-resistance layer.
Claim 4
Dependent Claim
23 words
A potentially non-linear resistor as set forth in claim 1, wherein said glass layer has a thickness of 30 μm to 1 mm.
Claim 5
Dependent Claim
41 words
A potentially non-linear resistor as set forth in claim 1, wherein said lead borosilicate glass comprises 40 to 85% by weight of lead oxide, 3 to 25% by weight of boron oxide, and 1.5 to 25% by weight of silicon oxide.
Claim 6
Dependent Claim
28 words
A potentially non-linear resistor as set forth in claim 1 or claim 4, wherein the lead borosilicate glass further contains 4 to 30% by weight of zinc oxide.
Claim 7
Dependent Claim
28 words
A potentially non-linear resistor as set forth in claim 1 or claim 4, wherein the lead borosilicate glass further contains 5 to 30% by weight of zirconium oxide.
Claim 8
Dependent Claim
26 words
A potentially non-linear resistor as set forth in claim 2, wherein the weight ratio of said zinc antimonate to zinc silicate ranges from 1:1 to 16:1.
Claim 9
Dependent Claim
23 words
A potentially non-linear resistor as set forth in claim 2, wherein the thickness of said high-resistance layer ranges from 10 to 200 μm.
Claim 10
Dependent Claim
58 words
A potentially non-linear resistor comprising a zinc oxide sintered body, the opposite end surfaces of said body each being provided with electrodes and a side surface located between said end surfaces being coated with a glass layer, wherein said glass layer comprises a lead borosilicate glass containing tin oxide in an amount of 0.4 to 10% by weight.
Claim 11
Dependent Claim
58 words
A potentially non-linear resistor comprising a zinc oxide sintered body, the opposite end surfaces of said body each being provided with electrodes and a side surface located between said end surfaces being coated with a glass layer, wherein said glass layer comprises a lead borosilicate glass containing tin oxide in an amount of 0.4 to 10% by weight.
Claim 12
Dependent Claim
40 words
A potentially non-linear resistor as set forth in claim 9, wherein a high-resistance layer comprising zinc antimonate and zinc silicate is provided on said side surface and said glass layer is coated on said side surface via said high-resistant layer.
Claim 13
Dependent Claim
41 words
A potentially non-linear resistor as set forth in claim 9, wherein said lead borosilicate glass comprises 40 to 85% by weight of lead oxide, 3 to 25% by weight of boron oxide and 1.5 to 25% by weight of silicon oxide.
Claim 14
Dependent Claim
25 words
A potentially non-linear resistor as set forth in claim 9, wherein the lead borosilicate glass further contains 4 to 30% by weight of zinc oxide.
Claim 15
Dependent Claim
25 words
A potentially non-linear resistor as set forth in claim 9, wherein the lead borosilicate glass further contains 5 to 30% by weight of zirconium oxide.
Claim 16
Dependent Claim
26 words
A potentially non-linear resistor as set forth in claim 10, wherein the weight ratio of said zinc antimonate to zinc silicate ranges from 1:1 to 16:1.
Claim 17
Dependent Claim
23 words
A potentially non-linear resistor as set forth in claim 10, wherein the thickness of said high-resistance layer ranges from 10 to 200 μm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-12 | 1987-06-13 | 1987-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-12 | 1991-06-13 | 1991-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-12 | 1995-06-13 | 1995-12-13 | $7700.00 | Window Closed / Lapsed |