Process for producing articles from polytetrafluoroethylene
Assignee: Geon Co
•
Filing: 1982-04-19
•
Granted: 1983-12-13
•
Expires: 2002-04-19
Abstract
Abstract A process for producing articles of polytetrafluoroethylene (PTFE) is disclosed. The process allows some of the conventional plastic fabrication techniques to be used with PTFE which until now have not been possible. The process comprises the steps of intensively mixing and thermokinetically heating PTFE resin in an enclosed container with a plurality of blades attached to arms rotating about an axis, with a blade tip speed of at least 30 meters/second, to a predetermined discharge temperature of above 370° C., discharging the resin at the discharge temperature, forming the resin into a desired shape at a temperature at or below the discharge temperature, holding the resin in the desired shape above a predetermined forming temperature for a predetermined time, and cooling the resin in the desired shape.
Inventors
- 👤 Zenas Crocker
- 👤 A. Nelson Wright
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 05:41
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/18; B; B01; B01F; B01F35/00; B01F35/20; B01F35/21; B01F35/211; B01F35/2115; B01F35/21151; B01F35/22; B01F35/221; B01F35/2214; B01F35/22142; B01F35/221421; B01F35/2216; B01F35/22161; B29; B29B; B29B13/00; B29B13/02; B29B13/021; B29B7/00; B29B7/002; B29B7/005; B29B7/02; B29B7/06; B29B7/10; B29B7/12; B29B7/16; B29B7/80; B29B7/82; B29C; B29C48/00; B29C48/022; B29C48/25; B29C48/36; B29C48/475; B29C67/00; B29C67/24; B29C43/00; B29C43/02; B29C43/16; B29C48/001; B29C48/0011; B29C48/03; B29C48/04; B29C48/07; B29C48/08; B29K; B29K2027/00; B29K2027/12; B29K2027/18; B29K2105/00; B29K2105/0005; B29K2105/0032; B29K2105/25; B29K2105/251; C08J2327/00; C08J2327/02; C08J2327/12; C08J2327/18
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
111 words
A process for production of a shaped polytetrafluoroethylene article comprising: introducing polytetrafluoroethylene granules into a high intensity mixer comprising an enclosed container having a plurality of blades rotatable on arms about a central axis; rotating said blades at a blade tip speed of at least 30 meters per second whereby the polytetrafluoroethylene granules are subjected to an intense mixing and thermokenetic heating action of the rotating blades until the granules become heated to a predetermined discharge temperature of above 370° C.; discharging the polytetrafluoroethylene granules at said discharge temperature; forming the discharged, heated, granules into an article of desired shape at or below said discharge temperature; and cooling the shaped article.
Claim 2
Dependent Claim
111 words
A process for production of a shaped polytetrafluoroethylene article comprising: introducing polytetrafluoroethylene granules into a high intensity mixer comprising an enclosed container having a plurality of blades rotatable on arms about a central axis; rotating said blades at a blade tip speed of at least 30 meters per second whereby the polytetrafluoroethylene granules are subjected to an intense mixing and thermokenetic heating action of the rotating blades until the granules become heated to a predetermined discharge temperature of above 370° C.; discharging the polytetrafluoroethylene granules at said discharge temperature; forming the discharged, heated, granules into an article of desired shape at or below said discharge temperature; and cooling the shaped article.
Claim 3
Dependent Claim
17 words
The process according to claim 1 wherein the blade tip speed is at least about 40 meters/second.
Claim 4
Dependent Claim
17 words
The process according to claim 1 wherein the predetermined discharge temperature is at least about 450° C.
Claim 5
Dependent Claim
41 words
The process according to claim 3 wherein the blade tip speed is about 35 meters/second, the predetermined discharge temperature is about 450° C. and the time period for the mixing and heating step is in the range of about 80-120 seconds.
Claim 6
Dependent Claim
45 words
The process according to claim 3 wherein the blade tip speed is about 40 meters/second, the predetermined discharge temperature is in the range of about 475°-480° C. and the time period for the mixing and heating step is in the range of about 60-80 seconds.
Claim 7
Dependent Claim
29 words
The process according to claim 1 wherein the article comprises a sheet of polytetrafluoroethylene and the forming step comprises pressing the dischanged resin between platens to form said sheet.
Claim 8
Dependent Claim
50 words
The process according to claim 6 wherein the pressing step occurs between hot plates at a temperature of at least about 150° C. at a pressure of at least about 320 psi, the pressing step occurring for about 3 minutes followed by the cooling step occurring for about 2 minutes.
Claim 9
Dependent Claim
28 words
The process according to any of claims 1, 6 or 7 wherein the total processing time for making the article is in the range of about 6-7 minutes.
Claim 10
Dependent Claim
24 words
The process according to claim 1, including the addition of pigments and/or other additives to the polytetrafluoroethylene resin for the mixing and heating step.
Claim 11
Dependent Claim
25 words
The process according to claim 1, wherein the forming takes place in a press and the desired shape is a coating layer on a substrate.
Claim 12
Dependent Claim
31 words
The process according to claim 1, wherein the desired shape is a billet which is cooled to a temperature suitable for forming into a finished article by direct stamping or forging.
Claim 13
Dependent Claim
22 words
The process according to claim 1 wherein the resin is discharged from the intensive mixing step directly into a compression moulding step.
Claim 14
Dependent Claim
17 words
The process according to claim 1 wherein forming comprises extruding the discharged resin in a ram extruder.
Claim 15
Dependent Claim
30 words
The process according to claim 1 wherein the article formed into desired shape is held at an elevated temperature above a predetermined forming temperature prior to cooling the shaped article.
Claim 16
Dependent Claim
16 words
The process according to claim 14 wherein said predetermined forming temperature is at least 150° C.
Claim 17
Dependent Claim
16 words
The process according to claim 14 wherein said predetermined forming temperature is at least 170° C.
References Cited (Backward Citations)
US2782180A
Cited
US3087921A
Cited
US3266738A
Cited
US3278661A
Cited
US3262834A
Cited
US4230615A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-12 | 1987-06-13 | 1987-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-12 | 1991-06-13 | 1991-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-12 | 1995-06-13 | 1995-12-13 | $7700.00 | Window Closed / Lapsed |