Process for continuous production of high impact polystyrene
Assignee: Hitachi Ltd
•
Filing: 1982-04-07
•
Granted: 1983-12-06
•
Expires: 2002-04-07
Abstract
Abstract High impact polystyrene having excellent properties is produced by a continuous process comprising feeding rubber and styrene continuously to a multistage horizontal dissolving tank to dissolve the rubber completely with stirring by increasing the temperature of each stage stepwise along the liquid flow direction, feeding the rubber solution to a first polymerizer to effect phase inversion of the rubber and preliminary polymerization of styrene; feeding the pre-polymerized solution to one or more horizontal type polymerizers to undergo bulk polymerization while removing the heat generated therein; and feeding the polymerized solution to a monomer separator to remove the remaining monomer.
Inventors
- 👤 Chihiro Fukumoto
- 👤 Tokinobu Furukawa
- 👤 Chikao Oda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 11:32
CPC Classifications
C; C08; C08F; C08F291/00; C08F291/02; B; B01; B01F; B01F27/00; B01F27/60; B01F27/70; B01F27/701; B01F27/702; B01J; B01J19/00; B01J19/18; B01J19/20; C08F2/00; C08F2/02; C08F279/00; C08F279/02; B01J2219/00; B01J2219/18; B01J2219/182
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
196 words
A process for continuously producing a high impact polystyrene which comprises: a step of feeding rubber and styrene monomer continuously to a multistage horizontal rubber dissolving tank to dissolve the rubber completely with stirring by increasing the temperature of each stage along the direction of the liquid flow therethrough to provide a rubber solution, a step of feeding the rubber solution to a first multistage horizontal type polymerizer operating at a temperature of from 100° to 200° C. to effect phase inversion of the rubber and preliminary polymerization of styrene, thereby providing a conversion of 25 to 40% by weight at the outlet of said first polymerizer, a step of feeding the resulting preliminary polymerized solution to one or more horizontal type polymerizers successively to undergo bulk polymerization at a temperature of from 100° to 230° C. while removing the heat generated therein by spraying styrene monomer over the exposed surface of the polymerization solution and evaporating the monomer to attain a conversion of about 70 to 85% by weight at the polymerization solution outlet of a final polymerizer, and a step of feeding the polymerization solution to a monomer separator to remove the remaining monomer.
Claim 2
Dependent Claim
196 words
A process for continuously producing a high impact polystyrene which comprises: a step of feeding rubber and styrene monomer continuously to a multistage horizontal rubber dissolving tank to dissolve the rubber completely with stirring by increasing the temperature of each stage along the direction of the liquid flow therethrough to provide a rubber solution, a step of feeding the rubber solution to a first multistage horizontal type polymerizer operating at a temperature of from 100° to 200° C. to effect phase inversion of the rubber and preliminary polymerization of styrene, thereby providing a conversion of 25 to 40% by weight at the outlet of said first polymerizer, a step of feeding the resulting preliminary polymerized solution to one or more horizontal type polymerizers successively to undergo bulk polymerization at a temperature of from 100° to 230° C. while removing the heat generated therein by spraying styrene monomer over the exposed surface of the polymerization solution and evaporating the monomer to attain a conversion of about 70 to 85% by weight at the polymerization solution outlet of a final polymerizer, and a step of feeding the polymerization solution to a monomer separator to remove the remaining monomer.
Claim 3
Dependent Claim
34 words
A process according to claim 1, wherein the styrene monomer from the gas phase portion of the polymerizer is condensed and is returned to be sprayed on to the surface of the polymerization solution.
Claim 4
Dependent Claim
16 words
A process according to claim 1, wherein the monomer separator is a centrifugal-force thin film evaporator.
Claim 5
Dependent Claim
49 words
A process according to claim 1, wherein the rubber dissolving tank has three stages and the temperature in the first stage is 20° to 40° C., the temperature in the second stage is 40° to 60° C. and the temperature in the third stage is 80° to 110° C.
Claim 6
Dependent Claim
21 words
A process according to claim 1, wherein 2 or 3 horizontal type polymerizers are used as the second to final polymerizers.
Claim 7
Dependent Claim
44 words
A process according to claim 1, wherein the rubber is at least one member selected from the group consisting of a polybutadiene, polyisoprene, a styrene-butadiene random copolymer, a styrene-butadiene block copolymer, a chlorinated polyethylene, an ethylene-vinyl acetate copolymer, an ethylene-propylenediene terpolymer and nitrile rubber.
Claim 8
Dependent Claim
24 words
A process according to claim 1, wherein the weight ratio of the rubber to styrene is 1/99 to 25/75 in the rubber dissolving tank.
References Cited (Backward Citations)
US3945976A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-05 | 1987-06-06 | 1987-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-05 | 1991-06-06 | 1991-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-05 | 1995-06-06 | 1995-12-06 | $7700.00 | Window Closed / Lapsed |