Aqueous acid plating bath and brightener mixture for producing semibright to bright electrodeposits of tin

Claim 2

A primary tin plating brightening mixture, comprising: from about 1 to about 25 percent by weight of a chlorinated acetophenone having the formula: ##STR4## where X 1 and X 2 are ring substituted chlorine atoms or hydrogen atoms, and from about 1 to about 97 percent by weight of a compound selected from the group consisting of acrylic acid, methacrylic acid, and combinations thereof.

Claim 3

The mixture according to claim 1 including from 1 to about 96 percent by weight of at least one emulsifying agent selected from the group consisting of nonionic, modified nonionic, cationic, anionic, and amphoteric emulsifying agents, and combinations thereof.

Claim 4

The mixture according to claim 2 wherein said emulsifying agent is selected from the group consisting of a nonionic or a modified nonionic emulsifying agent.

Claim 5

The mixture according to claim 3, wherein said nonionic emulsifying agent is made by condensing ethylene oxide with a lipophilic compound, said lipophilic compound selected from the group consisting of a long chain fatty alcohol, a long chain fatty amine, a long chain fatty acid, a long chain alkylphenol, naphthol, and polysaccharides, said long chain containing from about 2 to 30 carbon atoms, and wherein from about 10 to about 30 moles of said ethylene oxide are used per mole of said lipophilic compound.

Claim 6

The mixture according to claim 4, wherein said chlorinated acetophenone compound has a chlorine atom substituted in the para position or in the ortho position, or in both the para and one ortho position.

Claim 7

The mixture according to claim 1, 2, 3, 4, or 5, including from about 1 to about 25 percent of at least one aromatic aldehyde selected from the group consisting of salicylaldehyde, o-methoxybenzaldehyde, o-chlorobenzaldehyde, 2,4-dichlorobenzaldehyde, 2-hydroxy-1-naphthaldehyde, o-anisaldehyde, and combinations thereof.

Claim 8

The mixture according to claim 6, wherein the amount of said chlorinated acetophenone ranges from about 1 to about 10 percent by weight, wherein the amount of said emulsifying agent ranges from about 20 to about 50 percent by weight, and wherein the amount of said acrylic or methacrylic acid ranges from about 5 to about 30 percent by weight, based upon the total weight of said additive.

Claim 9

The mixture according to claim 7, wherein said chlorinated acetophenone is selected from the group consisting of 2,4-dichloroacetophenone, 2,3,4-trichloroacetophenone, o-chloroacetophenone, and p-chloroacetophenone, and wherein the amount of said aromatic aldehyde is from about 1 to about 15 percent.

Claim 10

The mixture according to claim 8, wherein said acid is methacrylic acid.

Claim 11

An aqueous acid electroplating bath containing stannous ions and sulfuric acid for producing electrodeposits of tin, comprising: from about 0.005 to about 0.2 grams per liter of bath solution of a chlorinated acetophenone having the formula: ##STR5## wherein X 1 and X 2 are ring substituted chlorine atoms or hydrogen atoms.

Claim 12

An aqueous acid electroplating bath containing stannous ions and sulfuric acid for producing electrodeposits of tin, comprising: from about 0.005 to about 0.2 grams per liter of bath solution of a chlorinated acetophenone having the formula: ##STR5## wherein X 1 and X 2 are ring substituted chlorine atoms or hydrogen atoms.

Claim 13

The bath according to claim 10, including from about 2 to about 40 grams per liter of an emulsifying agent, said emulsifying agent is selected from the group consisting of nonionic, modified nonionic, anionic, cationic, and amphoteric emulsifying agents, and combinations thereof.

Claim 14

The bath according to claim 11, including from about 0.02 to about 5 grams per liter of a compound selected from the group consisting of acrylic acid, methacrylic acid, and combinations thereof.

Claim 15

The bath according to claim 12, wherein said emulsifying agent is selected from the group consisting of a nonionic or a modified nonionic emulsifying agent.

Claim 16

The bath according to claim 13, wherein said nonionic emulsifying agent is made by condensing ethylene oxide with a lipophilic compound, said lipophilic compound selected from the group consisting of a long chain fatty alcohol, a long chain fatty amine, a long chain fatty acid, a long chain alkylphenol, naphthol, and polysaccharides, said long chain containing from about 2 to 30 carbon atoms, and wherein from about 10 to about 30 moles of said ethylene oxide are used per mole of said lipophilic compound.

Claim 17

The bath according to claim 14, wherein said chlorinated acetophenone compound has a chlorine atom substituted in the para position or the ortho position, or in both the para and one ortho position.

Claim 18

The bath according to claim 10, 11, 12, 13, 14, or 15, including from about 0.005 to about 0.2 grams/liter of at least one aromatic aldehyde selected from the group consisting of salicylaldehyde, o-methoxybenzaldehyde, o-chlorobenzaldehyde, 2,4-dichlorobenzaldehyde, 2-hydroxy-1-naphthaldehyde, o-anisaldehyde, and combinations thereof.

Claim 19

The bath according to claim 16, wherein the amount of said chlorinated acetophenone ranges from about 0.01 to about 0.05 grams per liter, wherein the amount of said emulsifying agent ranges from about 2 to about 10 grams per liter, and wherein the amount of acrylic or methacrylic acid ranges from about 0.02 to about 1.0 grams per liter, of plating bath.

Claim 20

The bath according to claim 17, wherein the amount of stannous ions ranges from about 10 to about 100 grams per liter and wherein the amount of said sulfuric acid ranges from about 50 to about 260 grams per liter of plating bath solution.

Claim 21

The bath according to claim 18, wherein said chlorinated acetophenone is selected from the group consisting of 2,4-dichloroacetophenone, 2,3,4-trichloroacetophenone, o-chloroacetophenone, and p-chloroacetophenone, and wherein the amount of said aromatic aldehyde is from about 0.005 to about 0.5 grams/liter.