Gas sensor elements and methods of manufacturing them
Assignee: International Gas Detectors Ltd
•
Filing: 1980-12-30
•
Granted: 1983-11-22
•
Expires: 2000-12-30
Abstract
Abstract A gas sensor element for detecting the presence of a flammable gas comprises an electrical resistance filament surrounded by a bead which is formed by an array of alumina particles interspersed between and bound together only by particles of a catalyst for inducing catalytic oxidation of flammable gases to form an open porous gas diffusive skeletal matrix having a mean particle size of less than 20 nm. When the bead includes such a matrix, the number of active sites at which catalytic oxidation of flammable gases can take place is greatly increased with the result that the sensor element is very resistant to poisoning by atmospheric contaminants such as traces of silicone and sulphur compounds. The sensor thus has a very much longer life and does not require such frequent recalibration.
Inventors
- 👤 Gordon S. Wilkinson-Tough
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 21:32
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/02; G01N27/04; G01N27/14; G01N27/16
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
124 words
A method of making a gas sensor element comprising the steps of: providing an electrical resistance filament; preparing a slurry from a mixture of alumina and at least one catalyst precursor in a substantially non-aqueous organic liquid, the mean particle size in the slurry being less than 20 nm; depositing said slurry on said electrical resistance filament; and, removing said non-aqueous organic liquid and decomposing said at least one catalyst precursor whereby said filament is surrounded by a bead which includes an array of said alumina particles interspersed between and bound together only by particles of a catalyst for inducing catalytic oxidation of flammable gases to form an open porous gas diffusive skeletal matrix having a mean particle size of less than 20 nm.
Claim 2
Independent Claim
124 words
A method of making a gas sensor element comprising the steps of: providing an electrical resistance filament; preparing a slurry from a mixture of alumina and at least one catalyst precursor in a substantially non-aqueous organic liquid, the mean particle size in the slurry being less than 20 nm; depositing said slurry on said electrical resistance filament; and, removing said non-aqueous organic liquid and decomposing said at least one catalyst precursor whereby said filament is surrounded by a bead which includes an array of said alumina particles interspersed between and bound together only by particles of a catalyst for inducing catalytic oxidation of flammable gases to form an open porous gas diffusive skeletal matrix having a mean particle size of less than 20 nm.
Claim 3
Dependent Claim
23 words
The method of claim 1, wherein said slurry is subjected to a wet grinding stage before said deposition on said electrical resistance filament.
Claim 4
Dependent Claim
22 words
The method of claim 1, wherein said mean particle size of said at least one catalyst precursor is reduced to 5 nm.
Claim 5
Dependent Claim
62 words
The method of claim 1, wherein said alumina is subjected to pre-treatment steps, said pre-treatment steps comprising: mixing said alumina into a slurry with a substantially non-aqueous organic liquid; subjecting said slurry to ultrasonic vibrations; allowing said vibrated slurry to sediment; and, separating the upper fraction of said slurry, said upper fraction then being mixed with said at least one catalyst precursor.
Claim 6
Dependent Claim
23 words
The method of claim 1, wherein said slurry contains a mixture of equal parts by weight of alumina, ammonium chloropalladite, and thorium nitrate.
Claim 7
Dependent Claim
20 words
The method of claim 1, wherein said non-aqueous organic liquid is taken from a group consisting of ethanol and methanol.
Claim 8
Dependent Claim
19 words
The method of claim 1, wherein said electrical resistance filament is supported horizontally whilst said slurry is deposited thereon.
Claim 9
Dependent Claim
25 words
The method of claim 7, wherein leads of said electrical resistance filament are bent into a kink and annealed before said slurry is deposited thereon.
Claim 10
Dependent Claim
36 words
The method of claim 1, wherein said sensor element is subjected to a conditioning step, said conditioning step comprising: heating said bead in an atmosphere formed by a stoichiometric mixture of a hydrocarbon gas and air.
Claim 11
Dependent Claim
22 words
The method of claim 1, wherein said gas sensor element is subjected to a constant current "soak" for a plurality of days.
Claim 12
Independent Claim
169 words
A method of making a gas sensor element comprising the steps of: providing an electrical resistance filament; preparing a slurry by mixing alumina having a nominal particle size of 50 nm with a substantially non-aqueous organic liquid; subjecting said slurry to ultrasonic vibrations; allowing said slurry to sediment; separating the upper fraction of said slurry; mixing alumina from said upper fraction with at least one catalyst precursor and a substantially non-aqueous organic liquid; subjecting said slurry to a wet grinding stage to reduce the mean particle size in the slurry to less than 20 nm; depositing said slurry on said electrical resistance filament; removing said non-aqueous organic liquid; and, decomposing said at least one catalyst precursor whereby said filament is surrounded by a bead which includes an array of said alumina particles interspersed between and bound together only by particles of a catalyst for inducing catalytic oxidation of flammable gases to form an open porous gas diffusive skeletal matrix having a mean particle size of less than 20 nm.
Claim 13
Independent Claim
169 words
A method of making a gas sensor element comprising the steps of: providing an electrical resistance filament; preparing a slurry by mixing alumina having a nominal particle size of 50 nm with a substantially non-aqueous organic liquid; subjecting said slurry to ultrasonic vibrations; allowing said slurry to sediment; separating the upper fraction of said slurry; mixing alumina from said upper fraction with at least one catalyst precursor and a substantially non-aqueous organic liquid; subjecting said slurry to a wet grinding stage to reduce the mean particle size in the slurry to less than 20 nm; depositing said slurry on said electrical resistance filament; removing said non-aqueous organic liquid; and, decomposing said at least one catalyst precursor whereby said filament is surrounded by a bead which includes an array of said alumina particles interspersed between and bound together only by particles of a catalyst for inducing catalytic oxidation of flammable gases to form an open porous gas diffusive skeletal matrix having a mean particle size of less than 20 nm.
References Cited (Backward Citations)
GB892530A
Cited
GB1387412A
Cited
US4068021A
Cited
US4132673A
Cited
GB1556339A
Cited
US4303612A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-21 | 1987-05-23 | 1987-11-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-21 | 1991-05-23 | 1991-11-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-21 | 1995-05-23 | 1995-11-22 | $7700.00 | Window Closed / Lapsed |