Method and bath for the electrodeposition of palladium/nickel alloys

Claim 2

In a method of electrodepositing a palladium/nickel alloy coating upon a substrate wherein said coating is plated onto said substrate by electrodeposition from a bath containing 5 to 30 g per liter of palladium and 5 to 30 g per liter of nickel and having a palladium-nickel ratio such that the coating contains 30 to 90% by weight of palladium, the improvement which comprises providing in said bath during the electrodeposition of said coating at least one acetylene alcohol or acetylene alcohol ether capable of improving the brightness and mechanical properties of said coating by promoting mixed crystal deposition, said acetylene alcohol or acetylene alcohol ether being selected from the group which consists of: propargylalcohol propargylalcoholmonoethoxylate (Hydroxyethylpropargylether) butynediol butynediol with 2 EO (Bis-(Hydroxyethoxy)-butyne) butynediol with 1 PO (2-Hydroxypropylpropbutynylether) hexynediol 2-methylbutyne-3-ol-2 3-methylpentyne-1-ol-3 3,4-dimethylpentyne-1-ol-3 3-ethylpentyne-1-ol-3 3-isopropyl-4-methylpentyne-1-ol-3 3-methylhexyne-1-ol-3 and 3-propylhexyne-1-ol-3.

Claim 3

A bath for the electrodeposition of palladium/nickel alloy coatings upon a substrate, said bath comprising an aqueous solution: a palladium amine in an amount sufficient to provide a palladium content in said bath of 5 to 30 g per liter, nickel amine in an amount sufficient to provide a nickel content in said bath of 5 to 30 g per liter, the palladium-nickel ratio being sufficient to deposit a coating of 30 to 90% by weight palladium, and at least one acetylene alcohol or acetylene alcohol ester compound in an amount of 0.01 g per liter to 10 g per liter and sufficient to improve the brightness of said coating by promoting mixed crystal deposition, said acetylene alcohol or acetylene alcohol ether being selected from the group which consists of: propargylalcohol propargylalcoholmonoethoxylate (Hydroxyethylpropargylether) butynediol butynediol with 2 EO (Bis[Hydroxyethoxy]-butyne) butynediol with 1 PO (2-Hydroxypropylprobutynylether) hexynediol 2-methylbutyne-3-ol-2 3-methylpentyne-1-ol-3 3,4-dimethylpentyne-1-ol-3 3-ethylpentyne-1-ol-3 3-isopropyl-4-methylpentyne-1-ol-3 3-methylhexyne-1-ol-3 and 3-propylhexyne-1-ol-3.

Claim 4

A bath for the electrodeposition of palladium/nickel alloy coatings upon a substrate, said bath comprising an aqueous solution: a palladium amine in an amount sufficient to provide a palladium content in said bath of 5 to 30 g per liter, nickel amine in an amount sufficient to provide a nickel content in said bath of 5 to 30 g per liter, the palladium-nickel ratio being sufficient to deposit a coating of 30 to 90% by weight palladium, and at least one acetylene alcohol or acetylene alcohol ester compound in an amount of 0.01 g per liter to 10 g per liter and sufficient to improve the brightness of said coating by promoting mixed crystal deposition, said acetylene alcohol or acetylene alcohol ether being selected from the group which consists of: propargylalcohol propargylalcoholmonoethoxylate (Hydroxyethylpropargylether) butynediol butynediol with 2 EO (Bis[Hydroxyethoxy]-butyne) butynediol with 1 PO (2-Hydroxypropylprobutynylether) hexynediol 2-methylbutyne-3-ol-2 3-methylpentyne-1-ol-3 3,4-dimethylpentyne-1-ol-3 3-ethylpentyne-1-ol-3 3-isopropyl-4-methylpentyne-1-ol-3 3-methylhexyne-1-ol-3 and 3-propylhexyne-1-ol-3.