Chromium plating
Assignee: Boeing Co
•
Filing: 1982-02-22
•
Granted: 1983-11-22
•
Expires: 2002-02-22
Abstract
Abstract A method of electroplating chromium onto a metal article includes an electrolytic surface treatment step and a plating step. In the electrolytic surface treatment step the article is immersed in an alkaline solution of a cyanide salt and an electrical potential is applied to the article and reversed in polarity at predetermined intervals. The potential is preferably applied in alternating 15 second and 5 second intervals, the polarity of the potential applied to the article being positive during the 15 second intervals and negative during the 5 second intervals. A potential of between about 4 to 6 volts is preferred. The potential is applied to the article for a period of 3 to 15 minutes, preferably beginning and ending with a 15 second interval during which the polarity of the potential is positive. The article is then immersed while still wet in a chromic acid electroplating bath. After several minutes a negative plating potential is gradually applied to the article until a desired current density is obtained. Chromium is continuously plated onto the article until a sufficient thickness of chromium is obtained. The method is particularly useful for plating chromium onto a previously chromium-plated article to form a durable chromium plating.
Inventors
- 👤 Richard Herrmann, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 05:41
CPC Classifications
C; C25; C25D; C25D5/00; C25D5/34; C25D5/38; C25D5/40; C25D5/10; C25D5/12; C25D5/14
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
99 words
A method of restarting the electroplating of chromium onto an article having an electroplated chromium coating, said method comprising the steps of: immersing said article in an aqueous alkaline solution of a cyanide salt; applying an electrical potential to said article immersed in said solution and reversing the polarity of said potential at predetermined intervals for a first predetermined period of time while said article is immersed in said aqueous alkaline solution; and, thereafter immersing said article in a chromic acid chromium electroplating bath and applying a cathodic plating potential to said article to electroplate chromium onto said article.
Claim 2
Independent Claim
99 words
A method of restarting the electroplating of chromium onto an article having an electroplated chromium coating, said method comprising the steps of: immersing said article in an aqueous alkaline solution of a cyanide salt; applying an electrical potential to said article immersed in said solution and reversing the polarity of said potential at predetermined intervals for a first predetermined period of time while said article is immersed in said aqueous alkaline solution; and, thereafter immersing said article in a chromic acid chromium electroplating bath and applying a cathodic plating potential to said article to electroplate chromium onto said article.
Claim 3
Dependent Claim
29 words
The method defined in claim 1 wherein said electrical potential applied to said article while said article is immersed in said alkaline solution is between 4 to 6 volts.
Claim 4
Dependent Claim
54 words
The method defined in claim 2 wherein the polarity of said electrical potential aplied to said article is reversed at the ends of alternating 15 second and 5 second intervals, the polarity of said electrical potential applied to said article being positive during said 15 second intervals and negative during said 5 second intervals.
Claim 5
Dependent Claim
37 words
The method defined in claim 3 wherein the application of said electrical potential is terminated at the end of a 15 second interval during which the polarity of said electrical potential applied to said article is positive.
Claim 6
Dependent Claim
37 words
The method defined in claim 4 wherein the application of said electrical potential to said article is commenced with a 15 second interval during which the polarity of said electrical potential applied to said article is positive.
Claim 7
Dependent Claim
19 words
The method defined in claim 5 wherein said first predetermined period of time is about 3 to 15 minutes.
Claim 8
Dependent Claim
39 words
The method defined in claim 6 wherein said article is immersed in said chromic acid chromium electroplating bath for a second predetermined period of up to about 5 minutes before said cathodic plating potential is applied to said article.
Claim 9
Dependent Claim
68 words
The method defined in claim 7 wherein said cathodic plating potential is gradually applied to said article over a third predetermined period of time of about 1 to 2 minutes immediately following said second predetermined period of time, said cathodic plating potential being gradually applied during said third predetermined period of time until a current density of between about 1 and 3 amperes per square inch is obtained.
Claim 10
Dependent Claim
38 words
The method defined in claim 8 wherein said article is rinsed with water at the end of said first predetermined period of time and thereafter immersed in said chromic acid chromium plating bath without being allowed to dry.
Claim 11
Independent Claim
31 words
The method defined in claims 1, 2, 3, 4, 5 or 9 wherein said aqueous alkaline solution of a cyanide salt comprises an aqueous solution of sodium cyanide and sodium hydroxide.
Claim 12
Dependent Claim
38 words
The method defined in claim 10 wherein said aqueous solution comprises between about 5 to 20 ounces of sodium hydroxide per gallon of solution and between about 14 and 40 ounces of sodium cyanide per gallon of solution.
Claim 13
Dependent Claim
38 words
The method defined in claim 11 wherein said aqueous solution comprises between about 7.2 and 14.4 ounces of sodium hydroxide per gallon of solution and between about 16.8 and 33.6 ounces of sodium cyanide per gallon of solution.
References Cited (Backward Citations)
US1942356A
Cited
US1774901A
Cited
US2078868A
Cited
US2678908A
Cited
US2856334A
Cited
US2915444A
Cited
US3388049A
Cited
US3551302A
Cited
US3770286A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-21 | 1987-05-23 | 1987-11-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-21 | 1991-05-23 | 1991-11-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-21 | 1995-05-23 | 1995-11-22 | $7700.00 | Window Closed / Lapsed |