US4415364A
Expired / Lapsed
US
⏱️ 0.0 years remaining
One-package inorganic binder composition
Assignee: Mizusawa Industrial Chemicals Ltd
•
Filing: 1982-06-24
•
Granted: 1983-11-15
•
Expires: 2002-06-24
Abstract
Abstract Disclosed is a one-package inorganic binder composition comprising a powdery mixture of a powdery alkali metal silicate having a water solubility or water dispersibility, an alkali metal borate soluble in an alkaline aqueous solution and silicon polyphosphate.
Inventors
- 👤 Hiroyuki Naito
- 👤 Takashi Maruya
- 👤 Masaaki Sugawara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:46
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/24; C04B41/00; C04B41/45; C04B41/50; C04B41/5076; C04B28/26; C04B41/009; C04B41/80; C04B41/81; C04B41/85; C09; C09D; C09D1/00; C09D1/02; C09J; C09J1/00; C09J1/02
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
35 words
A one-package inorganic binder composition comprising a powdery mixture of a powdery alkali metal silicate having a water solubility or water dispersibility, an alkali metal borate soluble in an alkaline aqueous solution and silicon polyphosphate.
Claim 2
Dependent Claim
35 words
A one-package inorganic binder composition comprising a powdery mixture of a powdery alkali metal silicate having a water solubility or water dispersibility, an alkali metal borate soluble in an alkaline aqueous solution and silicon polyphosphate.
Claim 3
Dependent Claim
35 words
A composition as set forth in claim 1, wherein the powdery alkali metal silicate has an M 2 O/SiO 2 molar ratio of from 1/1.3 to 1/2.6 in which M stands for an alkali metal.
Claim 4
Dependent Claim
27 words
A composition as set forth in claim 1, wherein the silicon polyphosphate has a P 2 O 5 /SiO 2 molar ratio of from 1/1.8 to 1/3.6.
Claim 5
Dependent Claim
105 words
A composition as set forth in claim 1, wherein the silicon polyphosphate has an initial dissolution quantity B, defined by the following formula, of up to 250 and an average hydrolysis speed constant A, defined by the following formula, of at least 0.2: Y×AX+B wherein X stands for the elapsed time (minutes), up to 120 minutes, of a sample solution formed by adding 1 g of the curing agent (silicon polyphosphate) in 100 ml of a 4 N aqueous solution of sodium hydroxide, and Y stands for the integrated amount (mg/100 ml) of phosphoric acid (P 2 O 5 ) dissolved in the sample solution.
Claim 6
Dependent Claim
83 words
A composition as set forth in claim 1, wherein the molar ratio of B 2 O 3 in the alkali metal borate to SiO 2 in the powdery alkali metal silicate is in the range of from 1/0.03 to 1/0.3 and the molar ratio of P 2 O 5 in the silicon polyphosphate to the total alkali metal component M 2 O in the total composition, in which M stands for an alkali metal, is in the range of from 1/0.35 to 1/0.85.
Claim 7
Dependent Claim
37 words
A composition as set forth in claim 1, wherein at least one of the silicon polyphosphate and the alkali metal silicate-alkali metal borate mixture is coated with an organic coating material soluble in an alkaline aqueous solution.
Claim 8
Dependent Claim
33 words
A composition as set forth in claim 6, wherein the organic or silicate coating material is present in an amount of 4 to 12% by weight based on said silicon polyphosphate or mixture.
Claim 9
Dependent Claim
18 words
A composition as set forth in claim 6, wherein the organic coating material is a higher fatty acid.
References Cited (Backward Citations)
US4018616A
Cited
US4171986A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-14 | 1987-05-16 | 1987-11-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-14 | 1991-05-16 | 1991-11-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-14 | 1995-05-16 | 1995-11-15 | $7700.00 | Window Closed / Lapsed |