Preparation of polyamides
Assignee: Aerojet Rocketdyne Holdings Inc
•
Filing: 1982-03-04
•
Granted: 1983-11-08
•
Expires: 2002-03-04
Abstract
Abstract Polyamides from lactams are prepared by the reaction of an initiator compound, a liquid hydroxy containing nitrile copolymer and a lactam using as a catalyst a minor amount of a lactam anionic polymerization catalyst. The resulting polyamides exhibit high impact strength and improved dimensional stability or reduced sensitivity to dimensional change upon exposure to a high humidity environment.
Inventors
- 👤 Gerd M. Lenke
- 👤 Hubert J. Fabris
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 15:55
CPC Classifications
C; C08; C08G; C08G69/00; C08G69/02; C08G69/08; C08G69/14; C08G69/16; C08G69/18
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
397 words
The method which comprises reacting together copolymerizable components consisting essentially of I. At least one initiator compound having the formula ##STR11## where A is B(NHCO) X , B(CO) X , --CO--, --SO 2 --, --CS--, ##STR12## B(CS) X , B(SO 2 ) X and B(PO) X/2 , where B is a C 4 to C 30 , or a C 6 to C 15 , hydrocarbon radical selected from the group consisting of alkylene, cycloalkylene, alkcycloalkylene, arylene, alkarylene and aralkylene radicals and mixtures thereof, where X is 2 to 4 and where R is an alkylene radical of from 4 to 11 carbon atoms and R' is hydrogen or an alkyl radical of from 1 to 4 carbon atoms, II. at least one liquid nitrile copolymer having an average of from about 2 to 3 hydroxyl groups per molecule and an average molecular weight of from about 1,500 to 10,000, said copolymer being a copolymer of from about 95 to 60 parts by weight of at least one conjugated diene of from 4 to 6 carbon atoms and from 5 to 40 parts by weight of at least one nitrile selected from the group consisting of acrylonitrile and methacrylonitrile and III. at least one lactam monomer in admixture with IV. at least one anionic lactam polymerization catayst in an amount of from about 1 to 20 meq., or from about 5 to 15 meq., of lactamate anion per 100 grams of I, II and III, the molar amount of III being substantially greater than the molar amounts of I and II, at a time, temperature and pressure sufficient to form a solid polyamide V, the lactam of III and IV having the formula ##STR13## where R is an alkylene radical of from 4 to 11 carbon atoms and R' is hydrogen or an alkyl radical of from 1 to 4 carbon atoms, the equivalent ratio of the lactamate anion of the catalyst IV to the initiator compound I being from about 0.1:1 to 1:1 or from about 0.3:1 to 1:1, the equivalent ratio of the initiator compound I to the OH groups of the nitrile copolymer II being from about 0.8:1 to 4:1 or from about 1:1 to 3:1 and the nitrile copolymer II being used in an amount sufficient to provide from about 5 to 40% by weight of II copolymerized in the resulting polyamide V.
Claim 2
Independent Claim
397 words
The method which comprises reacting together copolymerizable components consisting essentially of I. At least one initiator compound having the formula ##STR11## where A is B(NHCO) X , B(CO) X , --CO--, --SO 2 --, --CS--, ##STR12## B(CS) X , B(SO 2 ) X and B(PO) X/2 , where B is a C 4 to C 30 , or a C 6 to C 15 , hydrocarbon radical selected from the group consisting of alkylene, cycloalkylene, alkcycloalkylene, arylene, alkarylene and aralkylene radicals and mixtures thereof, where X is 2 to 4 and where R is an alkylene radical of from 4 to 11 carbon atoms and R' is hydrogen or an alkyl radical of from 1 to 4 carbon atoms, II. at least one liquid nitrile copolymer having an average of from about 2 to 3 hydroxyl groups per molecule and an average molecular weight of from about 1,500 to 10,000, said copolymer being a copolymer of from about 95 to 60 parts by weight of at least one conjugated diene of from 4 to 6 carbon atoms and from 5 to 40 parts by weight of at least one nitrile selected from the group consisting of acrylonitrile and methacrylonitrile and III. at least one lactam monomer in admixture with IV. at least one anionic lactam polymerization catayst in an amount of from about 1 to 20 meq., or from about 5 to 15 meq., of lactamate anion per 100 grams of I, II and III, the molar amount of III being substantially greater than the molar amounts of I and II, at a time, temperature and pressure sufficient to form a solid polyamide V, the lactam of III and IV having the formula ##STR13## where R is an alkylene radical of from 4 to 11 carbon atoms and R' is hydrogen or an alkyl radical of from 1 to 4 carbon atoms, the equivalent ratio of the lactamate anion of the catalyst IV to the initiator compound I being from about 0.1:1 to 1:1 or from about 0.3:1 to 1:1, the equivalent ratio of the initiator compound I to the OH groups of the nitrile copolymer II being from about 0.8:1 to 4:1 or from about 1:1 to 3:1 and the nitrile copolymer II being used in an amount sufficient to provide from about 5 to 40% by weight of II copolymerized in the resulting polyamide V.
Claim 3
Dependent Claim
57 words
The method according to claim 1 where I is the reaction product of epsilon caprolactam and 4,4'-diphenylmethane diisocyanate or hydrogenated 4,4'diphenylmethane diisocyanate or mixture thereof in an excess of epsilon caprolactam, II is a copolymer of butadiene-1,3 and acrylonitrile, III is epsilon caprolactam and IV is prepared from ethyl magnesium bromide or butyl lithium and epsilon caprolactam.
Claim 4
Dependent Claim
9 words
The product produced by the method of claim 1.
Claim 5
Dependent Claim
9 words
The product produced by the method of claim 2.
Claim 6
Dependent Claim
114 words
A solid polyamide consisting essentially of (1) a lactam having an alkylene chain of from 4 to 15 carbon atoms between amide groups and (2) copolymerized with said lactam, from about 5 to 40% by weight of said solid polyamide, a liquid nitrile copolymer having (a) an average of from about 2 to 3 hydroxyl groups per molecule, (b) an average molecular weight of from about 1,500 to 10,000 and (c) from about 95 to 60 parts by weight of at least one conjugated diene of from 4 to 6 carbon atoms and from 5 to 40 parts by weight of at least one nitrile selected from the group consisting of acrylonitrile and methacrylonitrile.
Claim 7
Dependent Claim
114 words
A solid polyamide consisting essentially of (1) a lactam having an alkylene chain of from 4 to 15 carbon atoms between amide groups and (2) copolymerized with said lactam, from about 5 to 40% by weight of said solid polyamide, a liquid nitrile copolymer having (a) an average of from about 2 to 3 hydroxyl groups per molecule, (b) an average molecular weight of from about 1,500 to 10,000 and (c) from about 95 to 60 parts by weight of at least one conjugated diene of from 4 to 6 carbon atoms and from 5 to 40 parts by weight of at least one nitrile selected from the group consisting of acrylonitrile and methacrylonitrile.
Claim 8
Dependent Claim
26 words
A solid polyamide according to claim 5 where said chain is a chain of 5 carbon atoms, said diene is butadiene-1,3 and said nitrile is acrylonitrile.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-07 | 1987-05-09 | 1987-11-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-07 | 1991-05-09 | 1991-11-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-07 | 1995-05-09 | 1995-11-08 | $7700.00 | Window Closed / Lapsed |