Carbon precursor by hydroheat-soaking of steam cracker tar

Claim 2

A process for preparing a pitch suitable for carbon artifact manufacture comprising: heat soaking a steam cracker tar or a component of a steam cracker tar in a hydrogen atmosphere for a time sufficient to provide a pitch suitable for carbon artifact manufacture.

Claim 3

The process of claim 1 wherein said heat soaking is at temperatures ranging from about 350° C. to about 450° C.

Claim 4

The process of claim 2 wherein said heat soaking is at temperatures ranging from about 370° C. to about 400° C.

Claim 5

The process of claim 2 or 3 wherein said hydrogen is sufficient to provide a pressure of from about 1 kg/cm 2 to about 500 kg/cm 2 .

Claim 6

The process of claim 4 wherein a steam cracker tar is heat soaked and wherein said heat soaked steam cracker tar is vacuum stripped to remove from about 10% to about 50% of the low boiling components present.

Claim 7

The process of claim 4 wherein said component of a steam cracker tar is a vacuum stripped steam cracker tar.

Claim 8

The process of claim 4 wherein said component of the steam cracker tar is a heavy distillate thereof.

Claim 9

A process for providing a pitch capable of being converted into greater than 75% of an optically anisotropic phase and suitable in carbon artifact manufacture comprising: heat soaking a vacuum stripped steam cracker tar at temperatures ranging from about 350° C. to about 450° C. in a hydrogen atmosphere of from about 1 kg/cm 2 to about 500 kg/cm 2 pressure for a time sufficient to provide a pitch suitable for carbon artifact manufacture.

Claim 10

A process for providing a pitch capable of being converted into greater than 75% of an optically anisotropic phase and suitable in carbon artifact manufacture comprising: heat soaking a vacuum stripped steam cracker tar at temperatures ranging from about 350° C. to about 450° C. in a hydrogen atmosphere of from about 1 kg/cm 2 to about 500 kg/cm 2 pressure for a time sufficient to provide a pitch suitable for carbon artifact manufacture.

Claim 11

A process for providing a pitch capable of being converted into greater than 75% of an optically anisotropic phase and suitable in carbon artifact manufacture comprising: heat soaking a steam cracker tar at temperatures ranging from about 350° C. to about 450° C. in a hydrogen atmosphere of from about 1 kg/cm 2 to about 500 kg/cm 2 pressure for a time sufficient to provide a heat soaked steam cracker tar; vacuum stripping said heat soaked steam cracker tar at temperature below about 420° C. to remove from about 10% to about 50% of the low boiling fractions present in said heat soaked tar whereby a pitch suitable for carbon artifact manufacture is obtained.

Claim 12

A process for providing a pitch capable of being converted into greater than 75% of an optically anisotropic phase and suitable in carbon artifact manufacture comprising: heat soaking a steam cracker tar at temperatures ranging from about 350° C. to about 450° C. in a hydrogen atmosphere of from about 1 kg/cm 2 to about 500 kg/cm 2 pressure for a time sufficient to provide a heat soaked steam cracker tar; vacuum stripping said heat soaked steam cracker tar at temperature below about 420° C. to remove from about 10% to about 50% of the low boiling fractions present in said heat soaked tar whereby a pitch suitable for carbon artifact manufacture is obtained.

Claim 13

A process for providing a pitch capable of being converted into greater than 75% of an optically anisotropic phase and suitable in carbon artifact manufacture comprising: heat soaking a heavy distillate of a steam cracker tar boiling in the range of about 350° C. to about 480° C. in a hydrogen atmosphere of from about 1 kg/cm 2 to about 500 kg/cm 2 pressure for a time sufficient to provide a pitch suitable for carbon artifact manufacture.

Claim 14

A process for providing a pitch capable of being converted into greater than 75% of an optically anisotropic phase and suitable in carbon artifact manufacture comprising: heat soaking a heavy distillate of a steam cracker tar boiling in the range of about 350° C. to about 480° C. in a hydrogen atmosphere of from about 1 kg/cm 2 to about 500 kg/cm 2 pressure for a time sufficient to provide a pitch suitable for carbon artifact manufacture.