Hydrophilic surfaces and process for making the same
Assignee: Research Corp Technologies Inc
•
Filing: 1982-01-25
•
Granted: 1983-11-01
•
Expires: 2002-01-25
Abstract
Abstract A hydrophilic surface can be provided on a hydrophobic polymer surface by contacting the hydrophobic surface with a solution of a hydroxyalkyl cellulose and a perfluorocarbon surfactant in water or a mixture of water and one or more aliphatic alcohols so as to form a layer of the solution on the hydrophobic surface and then heating the surface coated with the layer so as to remove the solvent, so as to form a bond between the cellulose and the hydrophobic surface. This results in the formation of a hydrophilic surface coating a layer on the hydrophobic surface. Hydrophilic surfaces as are created in this manner are primarily intended to be utilized on polysulfone surfaces in semipermeable membranes such as are utilized in micro- and ultra-filtration.
Inventors
- 👤 Wolfgang J. Wrasidlo
- 👤 Karol J. Mysels
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 19:29
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0081; B01D67/0088; B01D67/0093; C; C08; C08J; C08J7/00; C08J7/04; C08J7/0427; C08J7/056; B01D2323/00; B01D2323/30; C08J2401/00
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
158 words
A process for treating a hydrophobic polymer surface so as to render said surface hydrophilic in character which comprises: contacting said surface with a solution of a hydroxyalkyl cellulose and a perfluorocarbon surfactant in a solvent selected from the group consisting of water, and mixtures of water and water miscible aliphatic alcohols so as to provide a layer of said solution on said surface, said surfactant being present in said solution in an amount sufficient to cause said solution to wet substantially all of said surface, said cellulose being present in said solution in an amount effective to form a layer of said cellulose coating said surface upon the removal of solvent from said solution, and heating said surface and said layer to a temperature sufficient to remove said solvent from said layer and to a temperature sufficient to cause sufficient insolubilization of said cellulose to hold said cellulose on said polymer surface in the presence of water.
Claim 2
Dependent Claim
158 words
A process for treating a hydrophobic polymer surface so as to render said surface hydrophilic in character which comprises: contacting said surface with a solution of a hydroxyalkyl cellulose and a perfluorocarbon surfactant in a solvent selected from the group consisting of water, and mixtures of water and water miscible aliphatic alcohols so as to provide a layer of said solution on said surface, said surfactant being present in said solution in an amount sufficient to cause said solution to wet substantially all of said surface, said cellulose being present in said solution in an amount effective to form a layer of said cellulose coating said surface upon the removal of solvent from said solution, and heating said surface and said layer to a temperature sufficient to remove said solvent from said layer and to a temperature sufficient to cause sufficient insolubilization of said cellulose to hold said cellulose on said polymer surface in the presence of water.
Claim 3
Dependent Claim
55 words
A process as claimed in claim 1 wherein: said polymer present at said polymer surface is selected from the group consisting of polysulfone and polyimide polymers, and the alkyl radical in said hydroxyalkyl cellulose contains from 1 to 6 carbon atoms, said hydroxyalkyl cellulose has an average molecular weight from about 10,000 to about 1,000,000.
Claim 4
Dependent Claim
48 words
A process as claimed in claims 1 or 2 wherein: said solution contains from about 0.02 to about 2.00 percent by weight of said hydroxyalkyl cellulose, from about 0.001 to about 0.5 percent by weight of said surfactant and the remainder of said solution consists of said solvent.
Claim 5
Dependent Claim
68 words
A process as claimed in claim 1 wherein: said hydrophobic polymer surface forms a part of a filter membrane, said polymer surface is a polysulfone polymer surface, the alkyl radical contains from about 1 to 6 carbon atoms, said surface and said layer are heated to a temperature of from about 120° to about 190° C. for a period of from about 10 minutes to about 30 seconds.
Claim 6
Dependent Claim
56 words
A process as claimed in claim 1 wherein: said hydrophobic surface is a porous filter surface; said polymer and said hydrophobic polymer surface is a polysulfone polymer; said alkyl radical in said hydroxy cellulose contains from one to six carbon atoms; said hydroxy cellulose has an average molecular weight of from about 20,000 to about 60,000.
Claim 7
Dependent Claim
51 words
A process as claimed in claim 5 wherein: said membrane is useful for micro- and ultra-filtration purposes; said solution contains about 0.04 percent by weight of said cellulose and said solution contains about 0.023 percent by weight of said surfactant, and said cellulose has an average molecular weight of about 30,000.
Claim 8
Dependent Claim
47 words
In the combination of a hydrophobic polymer surface and a hydrophilic coating on said hydrophobic surface, the improvement which comprises: said hydrophilic coating consisting of a layer of cross-linked hydroxyalkyl cellulose which is not removable from said hydrophobic surface as a result of being sterilized by autoclaving.
Claim 9
Dependent Claim
47 words
In the combination of a hydrophobic polymer surface and a hydrophilic coating on said hydrophobic surface, the improvement which comprises: said hydrophilic coating consisting of a layer of cross-linked hydroxyalkyl cellulose which is not removable from said hydrophobic surface as a result of being sterilized by autoclaving.
Claim 10
Dependent Claim
56 words
A combination as claimed in claim 7 wherein: said polymer present at said hydrophobic polymer surface is selected from the group consisting of polysulfone and polyimide polymers, and said radical in said hydroxyalkyl cellulose contains from 1 to 6 carbon atoms, said hydroxyalkyl cellulose has an average molecular weight of from about 10,000 to about 1,000,000.
Claim 11
Dependent Claim
42 words
The combination claimed in claim 7 wherein: said hydrophobic polymer surface is a part of a filter membrane, said hydrophobic polymer is a polysulfone polymer, said cellulose is hydroxypropyl cellulose has an average molecular weight of from about 20,000 to about 60,000.
Claim 12
Dependent Claim
41 words
The combination claimed in claim 7, 8 or 9 wherein: said hydrophilic surface is a porous surface and said combination has at least 90 percent of the flow capacity of said uncoated hydrophobic surface in the absence of said hydrophilic coating.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-31 | 1987-05-02 | 1987-11-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-31 | 1991-05-02 | 1991-11-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-31 | 1995-05-02 | 1995-11-01 | $7700.00 | Window Closed / Lapsed |