Reversible phase change compositions of calcium chloride hexahydrate with a potassium salt
Assignee: Dow Chemical Co
•
Filing: 1982-09-13
•
Granted: 1983-11-01
•
Expires: 2002-09-13
Abstract
Abstract A reversible liquid/solid phase change composition comprising a mixture of hydrated CaCl 2 and a potassium salt whose anion forms a substantially less soluble salt with calcium and in which the potassium salt modifies the semi-congruently melting behavior of CaCl 2 .6H 2 O to the extent that the mixture approaches congruent melting behavior. Preferred examples of such compositions are CaCl 2 admixed with potassium sulfate, potassium carbonate or potassium phosphate. The composition preferably includes nucleating additives to modify and suppress the supercooling properties of the liquid phase of the composition. The composition is adapted to be incorporated into an encapsulating means for use as a heat storage device.
Inventors
- 👤 George A. Lane
- 👤 Harold E. Rossow
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 08:19
CPC Classifications
C; C09; C09K; C09K5/00; C09K5/02; C09K5/06; C09K5/063
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
94 words
A reversible liquid/solid phase change composition comprising an admixture of hydrated CaCl 2 and a potassium salt whose anion forms a substantially less soluble salt with calcium, wherein the potassium salt is added in an amount sufficient to modify the semi-congruent melting behavior of CaCl 2 .6H 2 O to the extent that the mixture approaches the congruent melting behavior of a congruently melting mixture and to reduce, during retrieval of the stored heat by crystallization of the mixture, the formation of crystalline CaCl 2 hydrate phases other than CaCl 2 .6H 2 O.
Claim 2
Dependent Claim
94 words
A reversible liquid/solid phase change composition comprising an admixture of hydrated CaCl 2 and a potassium salt whose anion forms a substantially less soluble salt with calcium, wherein the potassium salt is added in an amount sufficient to modify the semi-congruent melting behavior of CaCl 2 .6H 2 O to the extent that the mixture approaches the congruent melting behavior of a congruently melting mixture and to reduce, during retrieval of the stored heat by crystallization of the mixture, the formation of crystalline CaCl 2 hydrate phases other than CaCl 2 .6H 2 O.
Claim 3
Dependent Claim
39 words
The composition of claim 1, wherein the potassium salt is added to the hydrated CaCl 2 such that the potassium ion is present in an amount of from about 0.2 to about 4.2 percent by weight of the composition.
Claim 4
Dependent Claim
44 words
The composition of claim 1, comprising an admixture of from about 37 to about 51 weight percent CaCl 2 and from about 0.5 to about 26 weight percent of the potassium salt, with the balance being H 2 O (up to 100 weight percent).
Claim 5
Dependent Claim
47 words
The composition of claim 1, wherein the potassium salt is selected from the group consisting of potassium sulfate; potassium carbonate; potassium phosphate; potassium arsenate; potassium metaborate; potassium citrate; potassium fluoride; potassium hydroxide; potassium molybdate; potassium oxalate; potassium metaphosphate; potassium pyrophosphate; potassium silicate; potassium sulfite, and potassium tartrate.
Claim 6
Dependent Claim
20 words
The composition of claim 4, wherein the potassium salt is potassium sulfate, potassium carbonate or potassium phosphate, or mixtures thereof.
Claim 7
Dependent Claim
54 words
The composition of claim 4, wherein the potassium salt is K 2 SO 4 , and the composition comprises from about 37 to 51 weight percent CaCl 2 , from about 0.5 to about 19 weight percent K 2 SO 4 , with the balance being H 2 O (up to 100 weight percent).
Claim 8
Dependent Claim
43 words
The composition of claim 6, preferably comprising from about 47 to about 50 weight percent CaCl 2 , from about 8.4 to about 10.8 weight percent K 2 SO 4 , with the balance being H 2 O (up to 100 weight percent).
Claim 9
Dependent Claim
55 words
The composition of claim 4, wherein the potassium salt is K 2 CO 3 , and the composition comprises from about 37 to about 51 weight percent CaCl 2 , from about 0.5 to about 15 weight percent K 2 CO 3 , with the balance being H 2 O (up to 100 weight percent).
Claim 10
Dependent Claim
43 words
The composition of claim 8, preferably comprising from about 47 to about 50 weight percent CaCl 2 , from about 8.7 to about 10.6 weight percent K 2 CO 3 , with the balance being H 2 O (up to 100 weight percent).
Claim 11
Dependent Claim
55 words
The composition of claim 4, wherein the potassium salt is K 3 PO 4 , and the composition comprises from about 37 to about 51 weight percent CaCl 2 , from about 0.5 to about 23 weight percent K 3 PO 4 , and the balance being H 2 O (up to 100 weight percent).
Claim 12
Dependent Claim
43 words
The composition of claim 10, preferably comprising from about 48 to about 50 weight percent CaCl 2 , from about 7.6 to about 9.1 weight percent K 3 PO 4 , with the balance being H 2 O (up to 100 weight percent).
Claim 13
Dependent Claim
65 words
The composition of claim 1, including a salt selected from the group consisting of sodium and strontium salts, wherein the anion of said sodium and/or strontium salt forms a substantially less soluble salt with calcium, said sodium and/or strontium salt being present in an amount sufficient to modify the CaCl 2 .6H 2 O and potassium salt mixture to form an effectively congruently melting mixture.
Claim 14
Dependent Claim
47 words
The composition of claim 12, wherein said sodium and strontium salts are selected from the groups consisting of sodium arsenate; sodium metaborate; sodium citrate; sodium fluoride; sodium hydroxide; strontium hydroxide; sodium molybdate; sodium oxalate; sodium metaphosphate; sodium pyrophosphate; sodium silicate; sodium sulfite; sodium tartrate, and strontium tartrate.
Claim 15
Dependent Claim
41 words
The composition of claim 12 or 13, wherein the sodium salt is added to the hydrated CaCl 2 such that the sodim ion is present in an amount of from about 0.04 to about 2.0 percent by weight of the composition.
Claim 16
Dependent Claim
40 words
The composition of claim 12 or 13, wherein the strontium salt is added to the hydrated CaCl 2 such that the strontium ion is present in an amount of from about 0.05 to 2.0 percent by weight of the composition.
Claim 17
Dependent Claim
47 words
The composition of claim 1, including the addition of one or more nucleating agent or agents to said composition in an amount of from about 0.005 to about 2.0 weight percent to reduce supercooling to 5° C. or less during retrieval of the stored heat by crystallization.
Claim 18
Dependent Claim
23 words
The composition of claim 16, wherein the nucleating agent is present in an amount of from about 0.10 to about 1.0 weight percent.
Claim 19
Dependent Claim
58 words
The composition of claim 16 or 17, wherein the nucleating agent is selected from the group consisting of Ba(OH) 2 , BaO, BaI 2 , BaSO 4 , BaS 2 O 3 , BaCO 3 , BaCl 2 , BaF 2 , BaF 2 .HF, Sr(OH) 2 , SrO, SrCO 3 , SrF 2 and SrI 2 .
Claim 20
Dependent Claim
31 words
The composition of claim 18, wherein the nucleating agent is selected from Ba(OH) 2 ; BaO; BaI 2 ; BaSO 4 ; BaCO 3 ; BaCl 2 and Sr(OH) 2 .
Claim 21
Dependent Claim
157 words
A reversible liquid/solid phase change composition comprising a mixture of CaCl 2 .6H 2 O and a potassium salt whose anion forms a substantially less soluble salt with calcium, wherein the potassium ion is present in an amount sufficient to modify the semi-congruent melting behavior of CaCl 2 .6H 2 O to the extent that the mixture approaches the congruent melting behavior of a congruently melting mixture and to reduce, during retrieval of the stored heat by crystallization of the mixture, the formation of crystalline CaCl 2 hydrate phases other than CaCl 2 .6H 2 O, and including a salt selected from the group consisting of sodium and strontium salts, wherein the anion of said sodium and/or strontium salt forms a substantially less soluble salt with calcium, said sodium and/or strontium salt being present in an amount sufficient to modify the CaCl 2 .6H 2 O and potassium salt mixture to form an effectively congruently melting mixture.
Claim 22
Dependent Claim
157 words
A reversible liquid/solid phase change composition comprising a mixture of CaCl 2 .6H 2 O and a potassium salt whose anion forms a substantially less soluble salt with calcium, wherein the potassium ion is present in an amount sufficient to modify the semi-congruent melting behavior of CaCl 2 .6H 2 O to the extent that the mixture approaches the congruent melting behavior of a congruently melting mixture and to reduce, during retrieval of the stored heat by crystallization of the mixture, the formation of crystalline CaCl 2 hydrate phases other than CaCl 2 .6H 2 O, and including a salt selected from the group consisting of sodium and strontium salts, wherein the anion of said sodium and/or strontium salt forms a substantially less soluble salt with calcium, said sodium and/or strontium salt being present in an amount sufficient to modify the CaCl 2 .6H 2 O and potassium salt mixture to form an effectively congruently melting mixture.
Claim 23
Dependent Claim
45 words
The composition of claim 20, comprising CaCl 2 in an amount of from about 37 to about 51 weight percent and from about 0.5 to about 26 weight percent of the potassium salt, with the balance being H 2 O (up to 100 weight percent).
Claim 24
Dependent Claim
47 words
The composition of claim 20, wherein said sodium and strontium salts are selected from the group consisting of sodium arsenate; sodium metaborate; sodium citrate; sodium fluoride; sodium hydroxide; strontium hydroxide; sodium molybdate; sodium oxalate; sodium metaphosphate; sodium pyrophosphate; sodium silicate; sodium sulfite; sodium tartrate, and strontium tartrate.
Claim 25
Dependent Claim
23 words
The composition of claim 20, wherein the potassium ion is present in an amount of from about 0.2 to about 4.2 weight percent.
Claim 26
Dependent Claim
93 words
The composition of claim 20, comprising one or more nucleating agent in said composition in an amount of from about 0.005 to about 2.0 weight percent to reduce supercooling to 5° C. or less during retrieval of the stored heat by crystallization, wherein the nucleating agent is selected from the group consisting of Ba(OH) 2 , BaO, BaI 2 , BaSO 4 , BaS 2 O 3 , BaCO 3 , BaCl 2 , BaF 2 , BaF 2 .HF, Sr(OH) 2 , SrO, SrCO 3 , SrF 2 and SrI 2 .
Claim 27
Dependent Claim
129 words
A heat storage device comprising an encapsulating means having a reversible liquid/solid phase change composition hermetically sealed in said encapsulating means to prevent evaporation of water from the composition, said composition comprising an admixture of hydrated CaCl 2 and a potassium salt whose anion forms a substantially less soluble salt with calcium, wherein the potassium salt is added in an amount such that the potassium ion is present in an amount sufficient to modify the semi-congruent melting behavior or CaCl 2 .6H 2 O to the extent that the mixture approaches the congruent melting behavior of a congruently melting mixture and to reduce, during retrieval of the stored heat by crystallization of the mixture, the formation of crystalline CaCl 2 hydrate phases other than CaCl 2 .6H 2 O.
Claim 28
Dependent Claim
129 words
A heat storage device comprising an encapsulating means having a reversible liquid/solid phase change composition hermetically sealed in said encapsulating means to prevent evaporation of water from the composition, said composition comprising an admixture of hydrated CaCl 2 and a potassium salt whose anion forms a substantially less soluble salt with calcium, wherein the potassium salt is added in an amount such that the potassium ion is present in an amount sufficient to modify the semi-congruent melting behavior or CaCl 2 .6H 2 O to the extent that the mixture approaches the congruent melting behavior of a congruently melting mixture and to reduce, during retrieval of the stored heat by crystallization of the mixture, the formation of crystalline CaCl 2 hydrate phases other than CaCl 2 .6H 2 O.
Claim 29
Dependent Claim
70 words
The heat storage device of claim 25, wherein said composition includes a salt selected from the group consisting of sodium and strontium salts, wherein the anion of said sodium and/or strontium salt forms a substantially less soluble salt with calcium, said sodium and/or strontium salt being present in an amount sufficient to modify the CaCl 2 .6H 2 O and potassium salt mixture to form an effectively congruently melting mixture.
Claim 30
Dependent Claim
47 words
The composition of claim 26, wherein said sodium and strontium salts are selected from the group consisting of sodium arsenate; sodium metaborate; sodium citrate, sodium fluoride; sodium hydroxide; strontium hydroxde; sodium molybdate; sodium oxalate; sodium metaphosphate; sodium pyrophosphate; sodium silicate; sodium sulfate; sodium tartrate, and strontium tartrate.
Claim 31
Dependent Claim
92 words
The heat storage device of claim 25 or 26, wherein said composition includes one or more nucleating agents in an amount of from about 0.005 to about 2.0 weight percent to reduce supercooling to 5° C. or less during retrieval of the stored heat by crystallization, said nucleating agents being selected from Ba(OH) 2 , BaO, BaI 2 , BaSO 4 , BaS 2 O 3 , BaCO 3 , BaCl 2 , BaF 2 , BaF 2 .HF, Sr(OH) 2 , SrO, SrCO 3 , SrF 2 and SrI 2 .
Claim 32
Independent Claim
128 words
A method of storing heat, comprising the steps of preparing a reversible liquid-solid phase change composition by admixing hydrated CaCl 2 and a potassium salt whose anion forms a substantially less soluble salt with calcium, adding said potassium salt in an amount sufficient to modify the semi-congruent melting behavior of CaCl 2 .6H 2 O to the extent that the mixture approaches the congruent melting behavior of a congruently melting mixture and to reduce, during retrieval of the stored heat by crystallization of the mixture, the formation of crystalline CaCl 2 hydrate phases other than CaCl 2 .6H 2 O, introducing the composition into an encapsulating means for use as a heat storage device, and hermetically sealing the encapsulating means to prevent evaporation of water from the composition.
Claim 33
Independent Claim
128 words
A method of storing heat, comprising the steps of preparing a reversible liquid-solid phase change composition by admixing hydrated CaCl 2 and a potassium salt whose anion forms a substantially less soluble salt with calcium, adding said potassium salt in an amount sufficient to modify the semi-congruent melting behavior of CaCl 2 .6H 2 O to the extent that the mixture approaches the congruent melting behavior of a congruently melting mixture and to reduce, during retrieval of the stored heat by crystallization of the mixture, the formation of crystalline CaCl 2 hydrate phases other than CaCl 2 .6H 2 O, introducing the composition into an encapsulating means for use as a heat storage device, and hermetically sealing the encapsulating means to prevent evaporation of water from the composition.
Claim 34
Dependent Claim
72 words
The method of claim 29, including the step of adding an amount of a salt selected from the group consisting of sodium and strontium salts, wherein the anion of said sodium and/or strontium salt forms a substantially less soluble salt with calcium, said sodium and/or strontium salt being present in an amount sufficient to modify the CaCl 2 .6H 2 O and potassium salt mixture to form an effectively congruently melting mixture.
Claim 35
Dependent Claim
94 words
The method of claim 29 or 30, including the step of adding one or more nucleating agents in said composition in an amount of from about 0.005 to about 2.0 weight percent to reduce supercooling to 5° C. or less during retrieval of the stored heat by crystallization, said nucleating agents being selected from Ba(OH) 2 , BaO, BaI 2 , BaSO 4 , BaS 2 O 3 , BaCO 3 , BaCl 2 , BaF 2 , BaF 2 .HF, Sr(OH) 2 , SrO, SrCO 3 , SrF 2 and SrI 2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-31 | 1987-05-02 | 1987-11-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-31 | 1991-05-02 | 1991-11-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-31 | 1995-05-02 | 1995-11-01 | $7700.00 | Window Closed / Lapsed |