Assignee: BTG International Ltd
•
Filing: 1981-08-14
•
Granted: 1983-11-01
•
Expires: 2001-08-14
Abstract
Abstract A shaped element of germanium or silicon is coated with a layer of hard infra red transparent carbon. The carbon is deposited on the element, used as a cathode, in a glow discharge charge chamber by applying a D.C. voltage to a hydrocarbon gas at a pressure of e.g. 10 -1 to 10 -2 Torr. Prior to depositing the carbon the element may be heated and cleaned using argon ion bombardment. Layers of germanium and silicon may also be deposited using the gases germane and silane respectively.
Inventors
- 👤 Geoffrey W. Green
- 👤 Alan H. Lettington
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:15
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/44; C23C16/50; C23C16/503; C23C16/22; C23C16/26; G02B1/105; G; G02; G02B; G02B1/00; G02B1/10; G02B1/11; G02B1/111; G02B1/14; H; H10; H10F; H10F77/00; H10F77/30; H10F77/306; Y; Y10; Y10T; Y10T428/00; Y10T428/30
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
117 words
A method of coating an infra red transparent germanium or silicon element with a layer of hard carbon comprising the steps of: (i) placing the element on a cathode structure in a vacuum chamber, (ii) substantially evacuating the chamber, (iii) heating the substrate to a temperature not exceeding 300° C., (iv) admitting a hydrocarbon gas into the chamber while maintaining a substantial vacuum, (v) applying a D.C. voltage between the cathode and an anode in the chamber, and (vi) maintaining the substrate temperature below 300° C., whereby a glow discharge is initiated and maintained in the chamber so that carbon ions strike the element and build up a hard carbon layer substantially transparent to infra red radiation.
Claim 2
Independent Claim
117 words
A method of coating an infra red transparent germanium or silicon element with a layer of hard carbon comprising the steps of: (i) placing the element on a cathode structure in a vacuum chamber, (ii) substantially evacuating the chamber, (iii) heating the substrate to a temperature not exceeding 300° C., (iv) admitting a hydrocarbon gas into the chamber while maintaining a substantial vacuum, (v) applying a D.C. voltage between the cathode and an anode in the chamber, and (vi) maintaining the substrate temperature below 300° C., whereby a glow discharge is initiated and maintained in the chamber so that carbon ions strike the element and build up a hard carbon layer substantially transparent to infra red radiation.
Claim 3
Dependent Claim
25 words
A method according to claim 1, wherein prior to deposition of the carbon the element is subjected to argon ion bombardment in a glow discharge.
Claim 4
Dependent Claim
23 words
A method according to claim 1, further comprising the step of depositing a layer of silicon by glow discharge from a gas silane.
Claim 5
Dependent Claim
23 words
A method according to claim 1 further comprising the step of depositing a layer of germanium by glow discharge from a gas germane.
Claim 6
Dependent Claim
23 words
A method according to claim 1 wherein said step (ii) comprises the step of evacuating the chamber to at least 10 -4 Torr.
Claim 7
Dependent Claim
94 words
A method according to claim 5 further comprising before step (iv) the steps of: (a) introducing Argon gas into the chamber and bringing the pressure of the chamber to substantially 10 -1 to 10 -2 Torr. (b) applying a D.C. voltage in the range of -2 to -5 KV between the cathode structure and the anode to produce a glow discharge, thereby creating an Argon plasma and causing Argon ions to strike the germanium or silicon element thereby cleaning its surface and raising its temperature, and (c) exhausting the Argon gas from the chamber.
Claim 8
Dependent Claim
46 words
A method according to claim 1 further comprising the step of: (vii) as the hard carbon layer builds up during step (vi), increasing the negative potential applied to the cathode structure to overcome an insulating effect caused by the increasing thickness of the hard carbon layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-31 | 1987-05-02 | 1987-11-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-31 | 1991-05-02 | 1991-11-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-31 | 1995-05-02 | 1995-11-01 | $7700.00 | Window Closed / Lapsed |